• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2006년도 6th International Meeting on Information Display
• /
• pp.1096-1099
• /
• 2006

$II-III_2-(S,Se)_4$ structured of phosphor have been used at various field because those have high luminescent efficiency and broad emission band. Among these phosphors, europium doped $BaGa_2S_4$ was prepared by solid-state method and we try to look into an application possibility due to an emissive property of UV region. Also, general sulfide phosphors were synthesized by using injurious $H_2S\;CS_2$ gas. However, this study prepared $BaGa_2S_4:Eu^{2+}$ phosphor is addition to excess sulfur under 5% $H_2/95%\;N_2$ reduction atmosphere. So, this process could large scale synthesis because of non-harmfulness and simple process. The photo-luminescence efficiency of the prepared $BaGa_2S_4:Eu^{2+}$ phosphor increased 20% than commercial $SrGa_2S_4:Eu^{2+}$ phosphor. The prepared $BaGa_2S_4:Eu^{2+}$ could apply to green phosphor for white LED of three wavelengths.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2006년도 6th International Meeting on Information Display
• /
• pp.1360-1363
• /
• 2006

A borate compound was adopted as new host material for $EU^{3+}$ activator. The $Eu^{3+}-doped\;YCa_3(GaO)_3(BO_3)_4$ (YCGB) phosphors were successfully synthesized. Also, their photoluminescence properties under the excitation of UV ray were measured. In the XRD patterns of the synthesized powders, most peaks were well-matched to a gaudefroyite phase. The emission of $Eu^{3+}$ in YCGB consists of a strong peak centered at 622 nm, which is attributed to $^5D_O-^7F_2$ transition of $Eu^{3+}$ and several weak peaks at near the wavelength. Optimum $Eu^{3+}$ concentration of the red phosphor under the excitation with the wavelength of 395 nm was about 75 mol%. This indicates that the red phosphor has a relatively higher critical concentration than that of the other $Eu^{3+}-doped$ phosphors. The dominant interaction character of $Eu^{3+}$ might be dipole-dipole interaction.

• 한국전기전자재료학회논문지
• /
• 제27권7호
• /
• pp.477-482
• /
• 2014

$CaNb_2O_6:RE^{3+}$ (RE=Sm or Eu) phosphor powders were prepared with different contents of activator ions by using solid-state reaction method. The X-ray diffraction patterns exhibited that the phosphors synthesized with different activator ions showed an orthorhombic system with a main (131) diffraction peak. The maximum size of the grain particles, determined from the measurement of scanning electron microscopy, was observed at 0.05 mol of $Eu^{3+}$ ions and at 0.01 mol of $Sm^{3+}$. As for the $Eu^{3+}$-doped phosphor powders, the excitation spectra were composed of a broad band peaked at 278 nm and several weak bands in the range of 350~500 nm, and the highest red emission spectrum was observed at 0.15 mol of $Eu^{3+}$ ions. As for the $Sm^{3+}$-activated phosphor powders, three strong emission bands under excitation at 273 nm were observed at 570, 612, and 659 nm, respectively. The intensities of all the emission bands approached maxima for 0.05 mol of $Sm^{3+}$ ions. The optical properties show that the $Eu^{3+}$- or $Sm^{3+}$-doped $CaNb_2O_6$ powders are promising red-orange emitting phosphor powders applicable to full-color photonic devices.

• 한국방사선학회논문지
• /
• 제13권4호
• /
• pp.645-652
• /
• 2019

폴리 인산염 모체에 이온 반경이 유사한 Sr과 Eu 치환에 적합한 형광체를 찾아 단일 희토류 이온이 첨가된 형광체를 합성하고 후처리를 통해 형광 영역이 변화를 연구하였다. 고상법을 이용하여 Eu 이온이 첨가된 $NaSr(PO_3)_3$형광체를 합성하고 탄소열환원법을 통하여 $NaSr(PO_3)_3:Eu^{2+}$ 형광체를 완성하였다. 두 형광체 모두 X선 회절 측정을 통하여 결정상을 확인하였다. $NaSr(PO_3)_3:Eu^{3+}$의 여기 및 방출 스펙트럼 모두 $Eu^{3+}$ 농도가 증가할수록 형광 강도가 증가하였고 농도소광을 확인하였다. 방출스펙트럼에서 $Eu^{3+}$ 농도가 높아질수록 $Eu^{3+}$ 주변 환경의 국부적 대칭성이 높아지는 것 알 수 있었다. $NaSr(PO_3)_3:Eu^{2+}$ 농도별 방출스펙트럼에서 $Eu^{2+}$ 이온 농도 증가에 따른 $Eu^{2+}$ 이온 사이의 임계 거리가 가장 가까운 $Eu^{2+}$ 사이의 에너지 전달에 의해 형광이 감소하는 농도소광의 메커니즘을 확인하였다. 단일 희토류 이온이 첨가된 형광체의 후처리를 통해 형광 영역 변화가 가능하며 형광체 내 $Eu^{3+}$ 주변 환경의 국부적 대칭성과 $Eu^{2+}$ 이온간 거리에 따른 에너지 전달 및 농도소광 메커니즘 연구를 통하여 형광 특성 응용에 적합하고 효율성이 높은 형광체 개발에 좋은 모체 결정으로 사용 될 것으로 기대된다.

• 한국세라믹학회지
• /
• 제51권1호
• /
• pp.25-31
• /
• 2014

New green phosphor is synthesized by reducing $LiAlO_2:xEu^{3+}$ phosphors in a low pressure $H_2$ atmosphere. The $LiAlO_2:xEu^{3+}$ prepared by a solid state reaction method is reported as red phosphor. The effect of the reduction treatment on the $LiAlO_2:xEu^{3+}$ on the crystalline phase change and photoluminescence (PL) property are characterized. The reduced phosphor had a broad green light spectrum centered at 524 nm. The PL intensity of the reduced phosphor increased to a maximum at the reduction temperature of $1100^{\circ}C$. The PL intensity decreased with a further increase in the reduction temperature. The crystalline phase constituting the reduced phosphor varied with the temperature. A new crystalline phase $Li_2Al_4O_7$ was observed at $1100^{\circ}C$. The origin of the green-light emission is discussed in relation to the crystalline phase change.

• 한국응용과학기술학회지
• /
• 제19권3호
• /
• pp.174-180
• /
• 2002

In recent days, the study of a new phosphorescent phosphor has been performed in order to overcome the defect of sulfide phosphor and increase the brightness and long after-glow characteristic of phosphorescent phosphor. Particularly, sulfide phosphor usually used is so chemically unstable that the study of oxide phosphors are processing. $Eu^{2+}$, $Nd^{3+}$ doped Ba-Al-O phosphors sintered at $600{\sim}1500^{\circ}C$ for 2hours had the PL emission spectrum and after-glow over $1200^{\circ}C$. In this system, as the mole concentration of alumina increases, emission bands of phosphors moved from 500nm to 380nm. The optimum concentration of flux was 5wt% and after-glow characteristics of phosphors were found at the host material molar ratio ($BaCO_{3}:Al_{2}O_{3}$), 1:1 and 1:3.

• 한국세라믹학회지
• /
• 제40권7호
• /
• pp.709-714
• /
• 2003

에틸렌글리콜을 용매로 하여 용매열 합성으로 20$0^{\circ}C$에서 3-5시간 반응시킨 후 1000-140$0^{\circ}C$에서 2-4시간동안 대기 중에서 열처리 과정으로 Eu가 도핑된 $Y_2$ $O_3$ 나노 입자는 제조되었다. 100$0^{\circ}C$에서 열처리한 결정의 X-선 회절패턴은 보고되어진 데이터(JCPDS 카드파일 41-1105, a=10.6041 $\AA$)와 거의 일치하는 격자상수 a=10.5856 $\AA$으로 순수한 큐빅 $Y_2$ $O_3$ 상을 나타내었다. 제조된 적색 형광체의 평균입자의 크기는 대략 100 nm로 구형의 형태를 가진다 열처리 온도가 증가함에 따라 형광체 입자의 크기가 감소하였고, 열처리 온도가 증가함에 따라 형광체의 발광 세기가 증가하였다. PL 스펙트럼 분석을 통해 Eu의 농도가 3 ㏖% 도핑된 $Y_2$ $O_3$은 250 nm 파장에서 여기 스펙트럼을 나타내었고 611 nm 파장에서 주발광 스펙트럼을 나타내었다.

• 자원리싸이클링
• /
• 제16권5호
• /
• pp.46-50
• /
• 2007

[ $Eu^{2+},\;Nd^{3+}$ ]로 도핑된 $CaAl_2O_4$ 청색 형광체를 고상반응법으로 제조하였다. 1 mol% $Eu^{2+}$로 doping된 형광체에 다양한 조성의 $Nd^{3+}$를 co-doping함에 따라 고휘도, 장잔광 특성을 보였다. 제조한 형광체에 대하여 XRD, SEM, TEM, 빛발광 특성을 조사하였다. $CaAl_2O_4:Eu^{2+}:Nd^{3+}$의 넓은 밴드의 UV로 여기된 빛발광 특성이 $Eu^{2+}$의 $4f^65d^1$에서 $4f^7$ 상태로 천이에 의해 기인된 청색영역(${\lambda}_{max}=440\;nm$)에서 관찰되었다. $Nd^{3+}$로 co-doping한 형광체는 여기광을 차단하였을 때 장잔광 발광 특성을 나타내었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.430-431
• /
• 2009

In this study, europium doped strontium silicate ($Sr_2SiO_4:Eu^{2+}$) phosphor has been synthesized by conventional solid-state method and investigated luminescent characteristic. $SrCO_3$ and $SiO_2$ were mixed together by 2:1 mole ratio. Also $NH_4Cl$ was added as a flux. The mixture were sintered at $800^{\circ}C$, $1000^{\circ}C$ for 3h under the atmosphere (5% $H_2$/95% $N_2$). This phosphor can be applicated to the yellow phosphor for white LED because it has yellow emission band (540nm), which emits efficiently under the 370nm excitaion energy.

• 한국세라믹학회지
• /
• 제49권4호
• /
• pp.325-327
• /
• 2012

Europium-doped $LaSi_3N_5$ phosphor was synthesized from LaSi/Si/$Si_3N_4/Eu_2O_3$ mixture by nitridation at $1390^{\circ}C$ and additional annealing at $1650^{\circ}C$ for 4 h. The phosphor shows emissions in the green light region with a maximum at 560 nm. With increasing europium content in the general formula $La_{1-z}Eu_zSi_3N_{5-z}O_{1.5z}$ from z = 0.01 to 0.06 there was a maximum emission for z = 0.04 followed by concentration quenching for the highest europium content (z = 0.06).