• Korean Chemical Engineering Research
• /
• v.49 no.6
• /
• pp.739-744
• /
• 2011

Activated carbon SCR(CSCR) catalyst that is used to remove $NO_x$ in exhaust gas including boron discharged from the production process of liquid crystal display(LCD) shows deactivation when boron is deposited to block the pores within the catalyst or to cover its active sites. The spent carbon catalyst is regenerated by washing with various surfactants, drying and calcination. For comparison of the physical and chemical properties before and after the regeneration with the variables, type of surfactants and calcination condition, element analysis by ICP, $N_{2}$ adsorption were conducted. $DeNO_{x}$ in SCR with $NH_3$ was carried out in a fixed bed reactor at $120^{\circ}C$. The activated carbon catalyst regenerated through washing with a non-ionic surfactant in $H_{2}O$ at $90^{\circ}C$ and calcination under $N_{2}$ gas at $550^{\circ}C$ shows similar level of surface area and $NO_x$ removal efficiency with those of fresh catalyst.

• Resources Recycling
• /
• v.29 no.5
• /
• pp.38-47
• /
• 2020

In this study, factors affecting the adsorption reaction for the separation/recovery of V and W using Lewatit monoplus MP 600, a strong basic anion exchange resin, from the leachate obtained through the soda roasting-water leaching process from the spent SCR DeNO_X catalyst investigated and the adsorption mechanism was discussed based on the results. In the case of the mixed solution of V and W, both ions showed a high adsorption ratio at pH 2-6, but the adsorption of W was greatly reduced at pH 8. In the adsorption isothermal experiment, both V and W were fitted well at the Langmuir adsorption isotherm, and the reaction kinetics were fitted well at pseudo-second-order. As a result of conducting an adsorption experiment by adjusting the pH with H₂SO₄ to remove Si, which inhibits the adsorption of V and W from the leachate, the lowest W adsorption ratio was shown at pH 8.5. Desorption of W was hardly achieved in strongly acidic solutions, and desorption of V was well performed in both strongly acidic and strongly basic solutions.

• Resources Recycling
• /
• v.30 no.4
• /
• pp.54-63
• /
• 2021

Vanadium and tungsten can be obtained by separating/recovering the leaching solution from a spent SCR DeNO_X catalyst using the soda roasting-water leaching process. Therefore, in this study, the adsorption/desorption mechanism of vanadium and tungsten in an ion-exchange column was investigated using Lewatit MonoPlus MP 600, a strong basic anion exchange resin. The operating conditions for the separation of vanadium and tungsten in the ion-exchange column was intended to present. By conducting a continuous adsorption experiment in a pH 8.5 solution, the adsorption capacity of vanadium and tungsten was found to be 44.75 and 64.92 mg/(g of resin), respectively, which showed that the adsorption capacity of tungsten was larger than that of vanadium because of the difference in ion charge. Vanadium has a higher affinity for MP 600 than tungsten. Consequently, as the vanadium-containing solution is eluted through the ion exchange resin onto which tungsten is adsorbed, the adsorbed tungsten is exchanged with vanadium and desorbed. A continuous experiment was performed with a solution of vanadium and tungsten prepared at the same concentration as the spent SCR DeNO_X catalyst leachate. The adsorption capacity of vanadium was found to be 48.72 mg/(g of resin) and 80% of the supplied vanadium was adsorbed; in contrast, almost no tungsten was adsorbed. Therefore, vanadium and tungsten were separated effectively. The ion exchange resin was treated with 2 M HCl at 15 mL/h, and 97.7% of the vanadium(99% purity) could be desorbed. After desorption, NH₄Cl was added to precipitate ammonium polyvanadate at 90℃ and recover 93% of the vanadium.

• Resources Recycling
• /
• v.27 no.4
• /
• pp.57-64
• /
• 2018

Water leaching of tungsten(W) and vanadium(V) was researched from their oxides through mechanochemical (MC) reaction with alkali compounds. Intensive grinding for the mixture of tungsten/vanadium oxide and alkali compounds (NaOH, $Na2CO_3$) was carried out with change of their mixing ratios and grinding duration. Water soluble compounds, $Na_2WO_4$ and $NaVO_3$, were synthesized through MC reaction and their solubilities increased in proportion to the mixing ratio of sodium compound and grinding times. Whereas vanadium leachability was less affected by the mixting ratio and grinding times. The leachabilities of 99.0% were accomplished by a short period of MC treatment, W (30 min.) and V (5 min.). This process enable us to extract W and V from their oxides via a water leaching, and can be applied to the selective recovery of W and V from $DeNO_x$ spent catalysts.

• Resources Recycling
• /
• v.22 no.1
• /
• pp.55-63
• /
• 2013

Considering considerable contents of vanadium and tungsten in spent SCR DeNOx catalysts, separation and recovery of those metals are required. In this respect, commercial anion exchange resin (MP600) was employed to recover vanadium from the synthetic solution of ammonium metavanadate. Experimental results indicated that vanadium exist as anion under the acidic condition (pH 2 ~ 6) and adsorbed on the resin. Although the adsorption rate was increased with temperature, the maximum amount of adsorption was not affected by temperature. Desorption took place under either strong acidic (less than pH 1) or strong caustic (higher than pH 13) condition. However, desorption seldom took place under moderate conditions (pH 3~11). Furthermore, adsorption equilibrium results agreed well with Freundlich isotherm and pseudo-second-order reactions. And, adsorption energy was evaluated using Dubinin-Radushkevich and Temkin isotherm.