• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.11a
• /
• pp.75-76
• /
• 2018

MiDF, Micro Defect Free concrete, is the concrete made for high strength development by minimizing the defects such as micro pore and ITZ. Since MiDF exhibits strength through hydro-thermal synthesis reaction, it is essential to select the optimum C/S mole ratio. In this study, the basic characteristics of MiDF were evaluated by controlling the C/S mole ratio by SF and QP.

• Journal of the Korean Ceramic Society
• /
• v.30 no.12
• /
• pp.1071-1079
• /
• 1993

Interaction of alkali oxides and SO3 and C3S formation and microstructure was studied using K2CO3 and Na2CO3 as alkali sources and (NH4)2SO4 for SO3. When SO3/K2O=1.43 as mole ratio, K2O and SO3 react to form K2SO4, this phase is immiscible with other oxide melt and thus could not affect C3S formation as well as its microstructure. In a condition of SO3/K2O 1, C3S crystals were round and grown in a much larger size. With addition of Na2O and SO3 by only 1wt% each, C3S formation was strongly hindered. Since C2S was stabilized by Na+ and SO4-2, it could not react to give C3S formation. However in the condition of SO3/Na2O=1.43, a little amount of C3S was formed. It is considered that small amount of Na2SO4 was formed, this phase was immiscible with clinker liquid, and the C3S crystals were formed locally in the liquid part of relatively low Na2O and SO3 compositions. These crystals had irregular and rough surfaces and contained more inclusions than those grown from K2O.SO3 system.

• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.216-224
• /
• 1997

Porous silica ceramics were prepared(with HCI catalyst) using H2O/TEOS molar ratios of 2.6~59.0, with the EtOH/TEOS ratio fixed. After preparing 9 kinds of sol, the followings were investigated; measurement of the gelation time, thermal analyses by TG/DTA, property analyses of the intermediates by FT-IR and X-ray diffractometry with dried samples, analyses of SiO2 polymer by FT-IR, the investigation of specific sur-face area and pore size distribution by N2-adsorption isotherm, and structural change of SiO2 polymer and pore morphology by TEM observation, with samples heat-treated to 50$0^{\circ}C$. In the concentrations of in-vestigated compositions and catalyst, gelation time showed a minimum at ca. 11 moles of water per one mole of TEOS, the highest degree of polymerization at ca. 8-18 moles, and the largest specific surface area at ca. 11 moles, which means that the polymerization proceeded fastest at ca. 11 moles of water. In con-clusion, the more water used, the faster the polymerization reaction up to ca. 11 moles, but more than ca. 11 moles of water caused retardation of gelation and resultant reduction of specific surface area.

• Journal of the Korean Ceramic Society
• /
• v.46 no.4
• /
• pp.413-418
• /
• 2009

Glass systems based on Ca, Sr, Ba, and Zn modified alumino-boro silicates were investigated in order to improve the dielectric and mechanical properties of a typical LTCC (low temperature co-fired ceramic) which was developed for high frequency highly-integrated modules. The glass was prepared by a typical melting procedure and then mixed with cordierite fillers to fabricate glass/ceramic composite-type LTCC materials. The amount of cordierite filler was fixed at 50 volumetric%. For an optimal glass composition of 7.5% CaO, 7.5% BaO, 5% ZnO, 10% $Al_2O_3$, 30% $B_2O_3$, and 40% $SiO_2$ in mole ratio, the resultant LTCC composite showed a dielectric constant of 5.8 and a dielectric loss ($tan{\delta}$) of 0.0009 after firing at $900^{\circ}C$. An average bending strength of 160MPa was obtained for the optimal composition.

• Journal of the Korean Magnetics Society
• /
• v.6 no.4
• /
• pp.204-210
• /
• 1996

M type hexa-ferrites were prepared by means of a solid state reaction using mill scale, $Fe_{2}O_{3}$, and the mixture of mill scale and $Fe_{2}O_{3}$. The mixture of powders were calcined at $1150^{\circ}C$ for 2 hrs. and sintered at $1250^{\circ}C$ for 2 hrs, with varing the mole ratio of $Fe_{2}O_{3}$/$BaCO_{3}$, by 5.2~6.0. And the magnetic properties and morphologies of Baferrites with impurities such as $SiO_{2},\;Al_{2}O_{3},\;MgO,\;CaO\;and\;Na_{2}O$ in the mill scale were investigated. The magnetic properties were worsened by the addition of $Na_{2}O because of non-reacted iron oxide and intermediate compound of $BaFe_{2}O_{4}$ but they were improved apparently by the addition of $Si_{2}$ and $Al_{2}O_{3}$ in the composition of $BaO.5.6Fe_{2}O_{3}$. Moreover, $M_{s}$ decreased but $_{B}H_{C}$ increased through the addition of $Al_{2}O_{3}$ in Ba-ferrite. ${(BH)}_{max}$ of sintered BM($BaCO_{3}$, mill scale mixture) and BFM($BaCO_{3}$, $Fe_{2}O_{3}$, and null scale mixture) were 0.86 and 1.04 MGOe, respectively, and the magnetic properties were changed around $440^{\circ}C$.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.1 no.3
• /
• pp.219-224
• /
• 2013

In this study, the inorganic insulating material was fabricated with quartzite, ordinary portland cement(OPC), lime and anhydrous gypsum. After characteristic analysis of slurry, the optimum mixing ratio was derived with different $CaO/SiO_2$ mole ratio. Based on derived mixing ratio, the inorganic insulating material was fabricated at different water content and hydrothermal synthesis conditions. Specific gravity was $0.26g/cm^3$, compressive strength was 0.4 MPa, and thermal conductivity was 0.064 W/mK. This properties were enhanced performance of conventional ALC (Autoclaved Lightweight Concrete). And it can replace organic insulation with harmless inorganic insulation through continues research and development.

• Resources Recycling
• /
• v.2 no.4
• /
• pp.17-22
• /
• 1993

SiC whiskers were synthesized from rice hulls and activated carbon by carbothermal reduction method. The effects of gases and various additives were studied. Carbothermal reduction to produce SiC whiskers was conducted at $1450^{\circ}C$ and the synthesized SiC whiskers were examined using SEM and XRD. The length of whiskers is increased with the increases of $H_2$concentration and total gas flows. The most favorable form of SiC whiskers couble be obtained in the following experimental conditins : Ar : $H_2$=300:45(ml/min), $SiO_2$(inrice hulls): $CaF_2$=1:0.5:0.5(mole ratio) and the addition of Ni flakes ($1{\times}1$mm).

• Applied Chemistry for Engineering
• /
• v.16 no.1
• /
• pp.123-130
• /
• 2005

Zeolite X adsorbents with large surface area were prepared for using oxygen PSA adsorbent. Selective adsorption performance of nitrogen on the synthesized zeolite X adsorbent was improved by the cation exchange of adsorbent. The zeolite X which had over $650m^2/g$ surface area was synthesized at the conditions of $SiO_2\;:\;Na_2O\;:\;H_2O\;:\;Al_2O_3$ = 2.5 : 3.5 : 150 : 1 mole ratio, $98^{\circ}C$ temperature and 18 h synthesized time in 50 L reactor. The metal ions Li, Ag, Ca, Br, Sr, etc. were investigated for ion exchange with zeolite X. Ag ion was showed the highest ion exchange rate among these metal ions and all metal ions were exchanged with Na ion at equivalent rate. Compared with the NaX adsorbent, the ion exchanged zeolite X adsorbent remarkably improved its adsorption performance of nitrogen at the conditions of $10{\sim}40^{\circ}C$ temperature and 0~9 atm pressure. At an equilibrium pressure under 0.5 atm, adsorption performance of nitrogen on the ion exchanged zeolite adsorbent increased in the order of Ag > Li > Ca > Sr> Ba > K, whereas at an equilibrium pressure over 1 atm showed in the order of Li > Ag > Ca > Sr > Ba > K. Nitrogen/oxygen separation factor of Li ion exchanged zeolite X adsorbent was 13.023 at the partial pressure of nitrogen/oxygen gas mixture similar to air and $20^{\circ}C$ adsorption temperature.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.4
• /
• pp.103-111
• /
• 2012

One of the basic physical properties of the hardened cement paste, the rigidity, is deteriorated during concrete matrix forming, depending on the replacement rate of the crushed stone powder, and due to drying shrinkage. Therefore, the concrete containing crushed stone powder has been limitedly used as non-structural construction material. To improve these disadvantages, a hydrothermal reaction employing method can be considered. High-temperature and high-pressure water is involved in the hydrothermal reaction in the mixing with specific materials. The rigidity improving mechanism is related to the synthesis of calcium silicate. The calcium silicate is produced through reaction between calcium compounds and the silicic acid. Various kinds of calcium silicate can be produced depending on the CaO/$SiO_2$ mole ratio, the temperature of the hydrothermal synthesis, the pressure, and the reaction time. The product of the synthesis mechanism, tobermorite crystal, plays a pivotal role for the rigidity reinforcement. The crushed stone powder, analyzed in this study, contains 50 to 60% of $SiO_2$ and 10 to 20% $Al_2O_3$. The composite rate is appropriate to create the tobermorite crystal through formation of hardened cement matrix under the hydrothermal synthetic conditions and with the CaO in the cement. Moreover, further reinforcement was promoted using the property of material under the identical density through promoting the formation of tobermorite crystal.

• Bulletin of the Korean Chemical Society
• /
• v.22 no.1
• /
• pp.30-36
• /
• 2001

The crystal structures of fully dehydrated $Pd^{2+}$ - and $TI^{+}$ -exchanged zeolite X, $Pd_{18}TI_{56}Si_{100}Al_{92}O_{384}(Pd_{18}TI_{50-}X$, a = $24.935(4)\AA$ and $Pd_{21}TI_{50}Si_{100}Al_{92}O_{384}(Pd_{21}TI_{50-}X$ a = $24.914(4)\AA)$, have been determined by single-crystal X-ray diffraction methods in the cubic space group Fd3 at $21(1)^{\circ}C.$ The crystals were prepared using an exchange solution that had a $Pd(NH_3)_4Cl_2\;:TINO_3$ mole ratio of 50 : 1 and 200 : 1, respectively, with a total concentration of 0.05M for 4 days. After dehydration at $360^{\circ}C$ and 2 ${\times}$$10^{-6}$ Torr in flowing oxygen for 2 days, the crystals were evacuated at $21(1)^{\circ}C$ for 2 hours. They were refined to the final error indices $R_1$ = 0.045 and $R_2$ = 0.038 with 344 reflections for $Pd_{18}Tl_{56-}X$, and $R_1$ = 0.043 and $R_2$ = 0.045 with 280 reflections for $Pd_{21}Tl_{50-}X$; I > $3\sigma(I).$ In the structure of dehydrated $Pd_{18}Tl_{56-}X$, eighteen $Pd^{2+}$ ions and fourteen $TI^{+}$ ions are located at site I'. About twenty-seven $TI^{+}$ ions occupy site II recessed $1.74\AA$ into a supercage from the plane of three oxygens. The remaining fifteen $TI^{+}$ ions are distributed over two non-equivalent III' sites, with occupancies of 11 and 4, respectively. In the structure of $Pd_{21}Tl_{50-}X$, twenty $Pd^{2+}$ and ten $TI^{+}$ ions occupy site I', and one $Pd^{2+}$ ion is at site I. About twenty-three $TI^{+}$ ions occupy site II, and the remaining seventeen $TI^{+}$ ions are distributed over two different III' sites. $Pd^{2+}$ ions show a limit of exchange (ca. 39% and 46%), though their concentration of exchange was much higher than that of $TI^{+}$ ions. $Pd^{2+}$ ions tend to occupy site I', where they fit the double six-ring plane as nearly ideal trigonal planar. $TI^{+}$ ions fill the remaining I' sites, then occupy site II and two different III' sites. The two crystal structures show that approximately two and one-half I' sites per sodalite cage may be occupied by $Pd^{2+}$ ions. The remaining I' sites are occupied by $TI^{+}$ ions with Tl-O bond distance that is shorter than the sum of their ionic radii. The electrostatic repulsion between two large $TI^{+}$ ions and between $TI^{+}$ and $Pd^{2+}$ ions in the same $\beta-cage$ pushes each other to the charged six-ring planes. It causes the Tl-O bond to have some covalent character. However, $TI^{+}$ ions at site II form ionic bonds with three oxygens because the super-cage has the available space to obtain the reliable ionic bonds.