• Journal of information and communication convergence engineering
• /
• v.4 no.4
• /
• pp.158-161
• /
• 2006

[ $Bi_2Sr_2Ca_nCu_{n+1}O_y(n{\geq}0)$ ] thin film is fabricatedvia two different processes using an ion beam sputtering method i.e. co-deposition and layer-by-layer deposition. A single phase of Bi2212 can be fabricated via the co-deposition process. While it cannot be obtained by the layer-by-layer process. Ultra-low growth rate in our ion beam sputtering system brings out the difference in Bi element adsorption between the two processes and results in only 30% adsorption against total incident Bi amount by layer-by-layer deposition, in contrast to enough Bi adsorption by co-deposition.

• Korean Journal of Materials Research
• /
• v.4 no.8
• /
• pp.952-957
• /
• 1994

Fe/Co and FeN/CoN multilayer films were prepared by using RF and DC magnetron sputter^ ing technique with Ar or a mixture of Ar and $N_{2}$ gas. Annealing treatment was carried out in a vacuum at temperatures between $100^{\circ}C$ and $500^{\circ}C$ for lhour. Saturation magnetization (MS) and coercivity (Hc) of Fe/Co mutilayer films were investigated as a function of Fe layer thickness and annealing temperature. Permeability ($\mu$) was also examined. Saturation magnetization of 1.8T and coercivity of 1.80e were obtained for the as-deposited Fe/Co($70 \AA /15 \AA$) multilayer film. The Coercivity(Hc) did not change from 1.8 Oe till the annealing temperature $250^{\circ}C$ and then increased rapidly at higher annealing temperatures above $300^{\circ}C$. Coercivity(Hc) measured for the as-deposited FeN/CoN multilayer film was 5 Oe. It decreased gradually with annealing up to $250^{\circ}C$, and then increased rapidly at higher tempera tures.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.216-217
• /
• 2012

QM/MM 혼성 이론 방법인 ONIOM 계산을 통해, $CO_2$가 $B_N$-BNNT 벽면에서의 흡착 반응과 $H_2CO_3$로의 전환 반응 메커니즘을 규명함으로써 $B_N$-BNNT가 효과적인 $CO_2$ 흡착제와 $H_2CO_3$ 생성 반응 촉매로 개발 가능함을 확인하였다.

• Membrane Journal
• /
• v.10 no.3
• /
• pp.130-138
• /
• 2000

Polyethersulfone (PES) asymmetric membranes for gas separation were prepared by dry/wet phase inversion method and their separation properties for CO$_2$ and N$_2$ gases were investigated. The effects of important variables such as composition of casting solution and evaporation time in preparation of asymmetric gas membrane on membrane morphology and the separation properties were analyzed and the optimum condition of membrane preparation was established. To compensate the defects like pinholes existed on skin layer of the membrane prepared, the membranes were coated with silicone resin. By comparing separation properties after coating with those before coating, we found that the coating of silicone resin was effective to enhance the separation properties. The casting solution mainly used in this study consisted of PES, N-methyl-2-pyrrolidone, acetone, ethanol and distilled water was used as coagulation agent. It was shown that the selectivity for CO$_2$/N$_2$ was getting higher but the permeability decreases, as the contents of PES and volatile organic solvent and evaporation time increased. The selectivity for CO$_2$/N$_2$ and permeability of CO$_2$ of the membrane prepared under the optimum condition were found to be 61 and 21 GPU, respectively.

• Bulletin of the Korean Chemical Society
• /
• v.15 no.5
• /
• pp.379-386
• /
• 1994

Reactions of 1',2-bis(diphenylphosphino)-l-(N,N-dimethylaminomethyl)ferrocene (FcNPP) with $M(CO)_6$ (M=Cr, Mo, W) in the presence of TMNO (Trimethylamine oxide) in a stoichiometric ratio of 1 : 1.5 : 3.5 produced a series of Gp 6 metal carbonyl derivatives with a variety of coordination modes: M(CO)$_4({\eta}^2$-FcNPP-P,P) (M=Cr, Mo, W), $M(CO)_5({\eta}^1-FcNPP-P) (M=Mo, W)\;,\; M_2(CO)_9({\eta}^1\;,\;{\eta}^2-FcNPP-P,P,N) (M=Cr, Mo)\;,\;M_2(CO)_{10}({\eta}^1\;,\;{\eta}^1-FcNPP-P,P) (M=Cr, Mo, W)\;, and\;W(CO)_4({\eta}^2-FcNPP(O)-P,N)$. All these complexes were characterized by microanalytical and spectroscopic techniques. In one case, the structure of W(CO)$_4({\eta}^2$-FcNPP(O)-P,N) was determined by X-ray crystallography. Crystals are monocinic, space group P$2_{1/C}$, with a=10.147(2), b=19.902(3), c=19.821(4) ${\AA},\;{\beta}=96.88(2)^{\circ},\;V=3974(l){\AA}^3$, Z=4, and $D_{calc}=1.64 g cm^{-3}$. The geometry around the central tungsten metal is a distorted octahedron, with the nitrogen and phosphorus atoms being cis to each other. Some of these complexes exhibited catalytic activities in the allylic oxidation and epoxidation of cholesterly acetate. Other oxidation products were also formed with the different chemical yields and product distribution depending upon the ligand and the central metal.

• Journal of the Korean Ceramic Society
• /
• v.38 no.6
• /
• pp.515-521
• /
• 2001

출발 물질로서 L $i_2$C $O_3$, NiC $O_3$, CoC $O_3$를 사용하고 조성과 합성 온도를 변화시켜, 고온 고상법에 의하여 LiN $i_{1-y}$ $Co_{y}$ $O_2$(y=0.1, 0.3, 0.5)를 합성하였다. 합성과 시료들의 결정구조, 미세구조 그리고 전기화학적 특성을 조사하였다. 80$0^{\circ}C$와 8$50^{\circ}C$에서 제조한 L $i_{x}$N $i_{1-y}$ $Co_{y}$ $O_2$는, 삼방정계(space group: R3m)의 $\alpha$-NaFe $O_2$구조로 결정화되어 있는 층상 구조를 형성하였다. LiN $i_{1-y}$ $Co_{y}$ $O_2$(y=0.1, 0.3, 0.5)는 Co의 양이 증가함에 따라 a축과 c축의 크기가 감소하였는데, 이는 코발트 이온의 크기가 니켈 이온의 크기보다 작은데 기인하는 것이다. 그러나 c축과 a축의 크기의 비(c/a)가 증가하였음은 이차원적 구조가 잘 발달됨을 보여준다. 니켈에 대한 코발트의 치환량에 따른 리튬 이온의 삽입/추출 가역성은 코발트의 치환량이 증가하면서 증가하여 y=0.3인 LiN $i_{0.9}$ $Co_{0.1}$ $O_2$에서 대체로 우수하였고 그 이상으로 y값이 증가하면 가역성이 나빠졌다. 80$0^{\circ}C$에서 합성한 LiN $i_{0.9}$ $Co_{0.1}$ $O_2$가 가장 큰 초기 방전 용량 146 mAh/g을 나타내었으며, 싸이클링 성능도 비교적 우수하였다. 8$50^{\circ}C$에서 합성한 LiN $i_{0.9}$ $Co_{0.1}$ $O_2$와 LiN $i_{0.7}$ $Co_{0.3}$ $O_2$가 우수한 싸이클링 성능을 보였다.다. 싸이클링 성능을 보였다.다.보였다.다.

• Journal of the Korean Magnetics Society
• /
• v.10 no.5
• /
• pp.210-219
• /
• 2000

The magnetoresistance characteristics of FeN/Co/Cu/Co and FeN/Co/Cu/Co/Cu/Co/FeN multilayers using ferromagnetic iron-nitrides (FeN) has been studied. The microstructure of FeN film is the mixed ${\alpha}$-Fe and $\varepsilon$-Fe$_3$N phase on the condition that the flow rate of N$_2$ gas is over 0.4 sccm. The magnetoresistance effect is observed because of shape magnetic anisotropy induced by needle-shaped $\varepsilon$-Fe$_3$N phase. This magnetoresistance effect changes, because the degree that the shape magnetic anisotropy adheres to the adjacent Co pinned layer is varied according to the flow rate of N$_2$ gas and the thickness of FeN film. The best magnetoresistance effect is obtained on the condition that the thickness of Co free layer is 70 ${\AA}$ and the maximum MR ratio(%) value of 3.2% shows in the FeN(250 ${\AA}$)/Co(70 ${\AA}$)/Cu(25 ${\AA}$)/Co(70 ${\AA}$)/Cu(25 ${\AA}$)/Co(70 ${\AA}$)/FeN(250 ${\AA}$) mutilayer film which is fabricated at the N, gas flow rate of 0.5 sccm and the FeN film thickness of 250 ${\AA}$. Four steps are observed in the magnetoresistance curve owing to this difference of coercive force, because respective magnetic layers in the multilayer possess different coercive forces. These effects observed in these mutilayer films can be expected to application to the memory device the same MRAM as can carry out simultaneously four signals.

• The Korean Journal of Pesticide Science
• /
• v.12 no.2
• /
• pp.111-117
• /
• 2008

The comparative molecular field analysis (CoMFA) for the fungicidal activity with N-phenylbenzenesulfonamide analogues (1-45) against gray mold (Botriyts cinerea) were studied quantitatively. The statistical values of CoMFA models had much better predictability and fitness than those of comparative molecular similarity indices analysis (CoMSIA) models. The statistical values of the optimized CoMFA I model were predictablity, $r^2_{cv.}(or\;q^2)=0.457$ and correlation coefficient, $r^2_{ncv.}=0.959$, and their fungicidal activity was dependent on the steric field (52%) and electrostatic field (35.6%) of the substrate molecules. And also, it was found that the optimized CoMFA I model with the sensitivity to perturbation ($d_q^{2'}/dr^2_{yy'}=0.898$) and prediction ($q^2=0.346$ & SDEP=0.614) produced by a progressive scrambling analysis was not dependent on chance correlation. From the results of graphical analyses on the contour maps with the optimized CoMFA I model, it is expected that the $R_3$ and $R_4$-substituents on the N-phenyl ring as steric favor group and para-substituents ($R_1$) on the S-phenyl ring as steric disfavor group will contribute to the fungicidal activity. Therefore, the optimized CoMFA I model should be applicable to the prediction of the fungicidal activities against gray mold.

• Membrane Journal
• /
• v.24 no.3
• /
• pp.185-193
• /
• 2014

PDMS (polydimethylsiloxane)-HNT (halloysite nanotube) composite membranes were prepared with different amounts tendency of HNT 5, 10, 20 and 30 wt% and rubbery polymer PDMS. The characteristics of these membranes were studied by FT-IR, XRD, TGA, and SEM. Gas permeation experiment were performed under condition of $25^{\circ}C$ and $3kg/cm^2$. Gas permeability of $N_2$, $H_2$, $CH_4$, and $CO_2$ and selectivity were investigated by increasing the amount of HNT contents in the PDMS. In $H_2$, $N_2$, $CH_4$, and $CO_2$ gases, as increasing HNT contents from 0 to 30 wt%, decreasing value of the permeability were observed. The selectivity of ($CO_2/N_2$) was shown in the range of 14 to 44 and the range of selectivity of ($CO_2/CH_4$) was 3.0 to 7.0.

• Clean Technology
• /
• v.16 no.4
• /
• pp.284-291
• /
• 2010

Nitrous oxide ($N_2O$) is a greenhouse material which is hard to remove. Even with a catalytic process it requires a reaction temperature, at least, higher than 670 K. This study has been performed to see the effects of Ce addition to the mixed oxide catalyst which shows the highest activity in decomposing $N_2O$ completely at temperature as low as 473 K when CO is used as a reducing agent. Mixed metal oxide(MMO) catalyst was made through co-precipitation process with small amount of Ce added to the base components of Co, Al and Rh or Pd. Consequently, the surface area of the catalyst decreased with the contents of Ce, and the catalytic activity of direct decomposition of $N_2O$ also decreased. However, in the presence of CO, the activity was found high enough to compensate the portion of activity decrease by Ce addition, so that it can be ascertained that the catalytic activity and stability can be maintained in the CO involved $N_2O$ reduction system when Ce is added for the physical stability of the catalyst.