• Electrical & Electronic Materials
• /
• v.10 no.8
• /
• pp.819-829
• /
• 1997

The microwave dielectric materials of the BaO-Nd$_2$O$_3$-TiO$_2$and BaO-(Sm, Nd)$_2$O$_3$-TiO$_2$system were synthesized by conventional ceramic processing and sintered 1220 to 140$0^{\circ}C$ for 2 hours respectively. Their crystallization and dielectric properties were examined. In the BaO-Nd$_2$O$_3$-TiO$_2$ and BaO-(Sm, Nd)$_2$O$_3$-TiO$_2$system. Nd$_2$Ti$_2$O$_{7}$ and (Sm, Nd)$_2$Ti$_2$O$_{7}$ were observed as a second phase respectively. The maximum relative dielectric constant were 79,99 for the BaO-Nd$_2$O$_3$-TiO$_2$system and 105.07 for the BaO-(Sm,Nd)$_2$O$_3$-TiO$_2$system and their Q-value were over 2000 at 3GHz.GHz.

• Journal of the Korean Ceramic Society
• /
• v.31 no.9
• /
• pp.995-1004
• /
• 1994

Phase relation and microwave dielectric properties of the system BaO.(Nd1-xSmx)2O3.TiO2 (n=4, 5) were studied. With n=5 (1 : 1 : 5), Ba2Ti9O20 and TiO2 formed in case of X$\leq$0.7, and Ba2Ti9O20 and Sm2Ti2O7 formed at X=1.0 as the second phases dispersed in fine-grained orthorhombic matrix phase. With n=4 (1 : 1 : 4). on the contrary, only fine grains of an ortho-rhombic phase were observed irrespective of Nd/Sm ratio. The compositions of these two stable orthorombic phases having distinct lattic constants even with the same Nd/Sm ratio were estimated as 4BaO.5(Nd1-xSmx)2O3.18TiO2 and BaO.(Nd1-xSmx)2O3.4TiO2 with n=5 and n=4 in the system BaO.(Nd1-xSmx)2O3.TiO2, respectively. Consequently the composition BaO.(Nd1-xSmx)2O3.5TiO2 lies in the compatible triangle of 4BaO.5(Nd1-xSmx)2O3.18TiO2 and the second phases mentioned above. The microwave dielectric properties (~4 GHz) of BaO.(Nd1-xSmx)2O3.5TiO2 can be controlled effectively by adjusting Sm content : with increasing X from 0 to 0.7, both dielectric constant and the temperature coefficient of resonant frequency decreased monotonically from 82 to 65 and from 91 (ppm/$^{\circ}C$) to -19(ppm/$^{\circ}C$), respectively, while unloaded Q(Qo) remained constant at about 2,600.

• Journal of the Korean Ceramic Society
• /
• v.35 no.8
• /
• pp.775-782
• /
• 1998

This experiment is third study concerning BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} (Ln=Sm, Nd, Pr, La..) system which is known to show a high dielectric constant and Q value in microwave dielectric materials. The process of cry-stallization and the microwave dielectric properties of the specimens sintered at 1220-140$0^{\circ}C$ for 2 hr was investigated in the BaO-(Na,{{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} as well as BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} system. The single phase BaPr2Ti5O14 and Ba(Nd,{{{{ { { Pr})_{2 }O }_{3 } }}Ti5O14 was finally formed from the Pr2Ti2O7 (Nd, Pr)2Ti2O7 as a secondary phase in the BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} and BaO-(Nd, {{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} system respectively The dielectric constant of the specimens sint-ered at 1280~131$0^{\circ}C$ showed the maximum value as 105(BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} system) and 88 (BaO-(Nd,{{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} system) and the Q values of them showed higher value than 1800 which are due to the maximum den-sity. However the dielectric properties of the specimens sintered at higher temperature than 131$0^{\circ}C$ were reduced due to the increases of pore which were resulted from the sudden grain growth.

• Electrical & Electronic Materials
• /
• v.10 no.3
• /
• pp.274-283
• /
• 1997

These days, according to surprising development of communication enterprises, every soft of devices is getting smaller and cheaper. Among these Devices, microwave dielectric ceramics are studied and progressed briskly as the materials of dielectric resonator. Dielectric properties of BaO-S $M_{2}$ $O_{3}$-Ti $O_{2}$, one of the BaO Lnsub 2/ $O_{3}$-Ti $O_{2}$ (Ln=La, Sm, Nd, Pr…) system, synthesized by solid-reaction and coprecipitation method were investigated. Disk-type samples were sintered at 1250-1400.deg. C for 2hrs. As a result, single phase was not synthesized in both method. First created the second phase of S $M_{2}$ $Ti_{2}$ $O_{7}$, and then the last phase of $Ba_{3.75}$S $m_{9.5}$ $Ti_{18}$ $O_{54}$, Ti $O_{2}$, and $Ba_{2}$ $Ti_{9}$ $O_{20}$. When the sample was sintered at 1280.deg. C (in solid reaction method) and at 1310.deg. C (in coprecipitation method), it obtained highest dielectric constant (72.96 and 71.70, respectively) and high Q value. Above that temperature, dielectric constant and Q value decreased because of lattice defect according to oxygen vacancies........