• Journal of the Korean Ceramic Society
• /
• v.33 no.9
• /
• pp.1038-1044
• /
• 1996

The variations of sintering and electrical characteristics of semiconducting BaTiO3 ceramics with sintering agents added were investigated comparing the case of BaB2O4 addition to BN and TiO2 addition. When BaB2O4 added in BaTiO3 ceramics the densitifcation of specimen could be acheived more easily and recvealed the better PTCR characteristics than BN and TiO2 addition. As increase of addition of BaB2O4 in BaTiO3 spec imens the slope of resistivity jump also increased but the temperature of maximum resistivity decreased, It was supposed that addition of BaB2O4 led to increase of Ns (acceptor state density) value at grain boundaries.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.99.1-99
• /
• 2003

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1996.06b
• /
• pp.239-257
• /
• 1996

$\beta$-BaB2O4는 고출력 가시광선 및 적외선을 발진시키는데 유용한, 비선형 특성을 가진 물질이다. $\alpha$-$\beta$ 상전이 온도가 녹는점보다 18$0^{\circ}C$ 낮기 때문에 보통 flux법으로 단결정을 성장시킨다. 수년전 Itoh등은 $\beta$-BaB2O4단결정을 congruent조성의 용액으로부터 Czochralski법으로 metastable한 상태에서 직접 성장시켰다. 그렇지만 그 공정은 잘 이해되지 않고 있으며 재현하기가 매우 어렵다. 저자들은 $\beta$-BaB2O4단결정을 용액표면온도도 1034$^{\circ}$-1085$^{\circ}C$, pulling rate 3mm/h, 10-30 rpm의 범위에서 성장시켰으며 융액표면의 온도구배는 $\beta$-상으로 성장시키는데 매우 중요한 인자로 여겨진다. Seed로는 직경 1-2mm의 c축방향 $\beta$-BaB2O4단결정 봉이 상용되어 성장방향을 조절하고 열응력을 최소화시켰다. 성장된 $\beta$-상의 단결정들은 6-fold모양을 하며 표면에 작은 비늘같은 것들이 붙어있고 중심부에 core가 있는 것을 알았다. Flux법으로 성장시킨 $\beta$-BaB2O4단결정을 사용한 seeds는 단결정 성장 및 냉각 중에 cracks이 자주 발생하였으며, boule의 cracks은 afterheater를 사용할 경우 다소 줄일 수 있었다. 성장된 단결정의 광학특성이 측정되었다.

• Journal of the Korean Ceramic Society
• /
• v.23 no.6
• /
• pp.25-32
• /
• 1986

Phase spearated glass is heterogeneous in microscopic point of view and the heterogeneities affect the structures of glasses. In the present work the phase separation of $BaO-B_2O_3$ glass system was investigated and the effect of $P_2O_5$ on the phase separation and crystallization was also studied in the above system. Experiments such as scanning electron microscopy X-ray diffraction and infrared spectroscopy were performed. Phase separation with $B_2O_3$ rich phase matrix and BaO rich phase droplet was observed for the glasses containing less than 6 mole% of BaO while the opposite morphology of phase separation was found for the glasses containing more than 7 mole% of BaO. Phase separation region was extended up to the glass with 22mole% of BaO when the amount of $P_2O_5$ was increased. The heat-treated glasses crystallized to BaO.$4B_2O_3$$P_2O_5$ hindered the glass from the crystalli-zation.

• Elastomers and Composites
• /
• v.50 no.1
• /
• pp.7-12
• /
• 2015

The $BaCrO_4$ nanoparticles were synthesized from a 0.1 M $K_2CrO_4$ and 0.1 M $BaCO_3$ solution with stirring for 10 h. The product was washed several times with acetone and heated to $700^{\circ}C$ for 6 h. At that time, the color of mixture was a greenish yellow. The graphene/$BaCrO_4$ nanocomposites were prepared with graphene and $BaCrO_4$ nanoparticles by stirring in tetrahydrofuran and heated in an electric furnace at $700^{\circ}C$ for 2 h. The $BaCrO_4$ nanoparticles, graphene/$BaCrO_4$ and heated graphene/$BaCrO_4$ nanocomposites were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The graphene/$BaCrO_4$ nanocomposites and heated graphene/$BaCrO_4$ nanocomposites were evaluated as a photocatalyst and discussed about kinetics study for the degradation of organic dyes, such as methylene blue and rhodamine B under ultraviolet light irradiation at 254 nm.

• The Korean Journal of Ceramics
• /
• v.5 no.2
• /
• pp.189-194
• /
• 1999

Crystallization of glasses in the system (Ca, Sr, Ba)$O-Al_2O_3-B_2O_3-SiO_2-TiO_2$ and dielectric properties of crystallized glasses were investigated. As increasing B2O3 content and decreasing SiO2 content in the glass, the major crystalline phase changed from $(Sr, Ba)_2TiSi_2O_8$ to (Ca, Sr, Ba)TiO3, the dielectric constant of crystallized glasses increased and the Temperature Coefficient of Capacitance (TCC) changed to negative. The dielectric constant and TCC was estimated for (Sr, Ba)2TiSi2O8 phase as 18 and -440 $ppm/^{\circ}C$, respectively and for (Ca, Sr, Ba)TiO3 phase as 307 and -1900 $ppm/^{\circ}C$, respectively. The dielectric properties of (Ca, Sr, Ba)TiO3 phase (in this study) were similar to those of (Ca, Ba) TiO_3 solid-solution^12)$, but $(Sr, Ba)_2TiSi_2O_8$ phase (in this study) and $Sr_2TiSi_2O_\;8^4$ showed the different properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.611-614
• /
• 2004

[ $Ba(Zn_{1/3}Nb_{2/3})O_3$ ] (BZN) 세라믹스의 소결 온도는 약 $1350^{\circ}C$ 이다. 그러나 $B_2O_3$가 첨가된 경우, BZN 세라믹스는 $900^{\circ}C$에서 소결되었다. $BaB_4O_7$, $BaB_2O_4$ 그리고 $BaNb_2O_6$ 이차상이 $B_2O_3$가 첨가된 BZN 세라믹스에서 관찰되었다. $BaB_4O_7$과 $BaB_2O_4$ 이차상은 약 $900^{\circ}C$에서 공정 온도를 가지기 때문에 $B_2O_3$를 첨가한 BZN 세라믹스론 $900^{\circ}C$에서 소결하는 동안 액상으로 존재할 것으로 여겨지며, 그것이 BZN 세라믹스의 소결온도를 낮출 것으로 생각된다. 소결 온도의 증가에 따라 유전 상수 ($\varepsilon_r$)와 품질 계수 ($Q{\times}f$)의 값은 증가하였는데, 이는 밀도의 증가에 기인한다. 그러나 $B_2O_3$의 첨가량이 많은 경우 Q 값은 감소하는데, 이는 이차상의 존재가 품질계수의 저하를 초래한다고 생각된다. 2.0 mol% $B_2O_3$가 첨가된 BZN 세라믹스를 $950^{\circ}C$에서 2시간 동안 소결하는 경우, $Q{\times}f$=13.600 GHz, $\varepsilon_r$=37.6 그리고 공진 주파수 온도계수 ($\tau_f$) = 19 ppm/$^{\circ}C$의 유전특성을 얻을 수 있었다.

• Journal of the Korean Ceramic Society
• /
• v.36 no.2
• /
• pp.136-144
• /
• 1999

Crystal structures of tungsten-bronze type microwave dielectric ceramics, $BaOLa_2O_34TiO_2$ (BLT) and $BaO(Nd_{0.77}Y_{0.23})_4TiO_2$ (B(NY)T), were analysed using the Rietveld method. The most relibale refinement was obtained by refining the cation and anion positions from the x-ray and neutron diffraction data, respectively. The ambiguites inherent in the refined crystal structure by Mateeva et al. were resolved. The $BaORe_2O_34TiO_2$ structure consiste of $3\times2$ perovskite blocks and 4 pentagon-channels. The Ti-O6 octahedrons are distroted and tilted, which, consequently, induces the displacements of Ba and Re ions producing the superlattics (c$\approx$ 7.6 $\AA$). The B(NY)T showed more severely tilted Ti-O6 octahedrons. The relative dielectric constant $\varepsilon_{\gamma}$ and temperature coefficient $\tau_\varepsilon$ are 109.5 and-$180 ppm/^{\circ}C$ in BLT, 76 and $+40 ppm/^{\circ}C$ in B(NY)T, respectively. The small Re ions produced a positive $\tau_\varepsilon$. The relation between $\tau_\varepsilon$ and the octahedron tilting in complex perovskite is discussed for the tungsten bronze type structure.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.272-273
• /
• 2006

LTCC(low temperature co-fired ceramics)용 glass/ceramic 복합체를 제조하기 위해 4 종류의 borosilicate계 glass를 선정하고 filler로 $Al_2O_3$ ceramics를 filler 사용하여 30~50 vol% glass frit에 따른 소결 및 유전 특성에 대하여 조사하였다. Glass frit은 $SiO_2$와 $B_2O_3$ 함량비를 고정한 후 R(CaO, BaO, ZnO, $Bi_2O_3$)에 따라 유리 연화온도(Ts)와 함량이 소결에 미치는 영향 및 유전 특성 변화를 고찰한 결과, CaO-$B_2O_3-SiO_2$ glass의 경우 다량의 2 차상이 형성되었고, 이에 $900^{\circ}C$ 이하에서 완전 소결이 이루어지지 않았으며, BaO-$B_2O_3-SiO_2$ glass는 celsian($BaAl_2Si_2O_8$) 결정이 형성되면서 소결성의 저하를 갖고 왔으며, ZnO-$B_2O_3-SiO_2$ glass는 소결이 진행됨에 따라 주상이 $Al_2O_3$에서 gahnite($ZnAl_2O_4$) 결정이 형성되면서 품질계수가 크게 증가하였으며, $Bi_2O_3-B_2O_3-SiO_2$ glass는 45 vol%일 때 $900^{\circ}C$에서부터 일정한 선수축율 특성을 나타내었지만, 다량의 액상으로 인하여 유전 특성의 저하를 나타내었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.679-683
• /
• 2004

[ $BaO-Sm_2O_3-4TiO_2$ ] 세라믹을 LTCC용 재료로 사용하기 위해 $B_2O_3$와 CuO를 소결조제로 첨가하여 소결온도를 낮추었다. 10.0 mol%의 $B_2O_3$만을 첨가하였을 경우 $1000^{\circ}C$에서 2시간 소결시 er=72.23, Qf=4,050GHz, ${\tau}f=-0.574ppm/^{\circ}C$의 우수한 유전 특성값을 얻을 수 있었지만, $960^{\circ}C$이하에서는 소결이 잘 이루어지지 않았다. $B_2O_3$와 CuO를 동시에 소결조제로 첨가하였을 경우에는 $900^{\circ}C$에서 2시간 소결시 10.0 mol% $B_2O_3$, 15.0 mol% CuO의 첨가조성에서 ${\varepsilon}r$=70.09, Qf=4,728GHz의 우수한 유전특성을 보여 고유전율을 가진 저온 동시 소결용 재료로서의 가능성을 보여주었다. 이처럼 BaO-$Sm_2O_3-4TiO_2$ 세라믹의 소결온도를 낮출 수 있었던 요인은 소결온도보다 용융점이 낮은 2차상들이 액상을 형성하여 액상소결이 진행되었기 때문이며 이때 소결에 기여한 이차상들은 결정화되지 못하고 비정질 상태로 남아있는 것으로 추정된다.