• Journal of the Korean Ceramic Society
• /
• v.34 no.4
• /
• pp.368-372
• /
• 1997

The microwave dielectric properties of (1-x)La2/3TiO3-xLaAlO3 system in which LaAlO3 having $\varepsilon$r$\geq$90 and positive $\tau$f was investigated. The crystal system of (1-x)La2/3TiO3-xLaAlO3 was pseudo-cubic in the range of 0.1$\leq$x$\leq$0.07. Its lattice constant increased with increasing x in spite that the amount of LaAlO3 containing of smaller Al(0.57 $\AA$) ion than Ti(0.64 $\AA$) increased. As the amount of LaAlO3 increased from x=0.1 to 0.9, the relative dielectric constant ($\varepsilon$r) decreased from 50 to 23 and the temperature coefficient of resonant frequency($\tau$f) decreased from +84 to -50. On the other hand, the value of Q.f0 reached a maximum (148,000 at 7 GHz) at x=0.7, where a rapid increase in the peak intensity of XRD occured, and further increased after prolonged sintering. The microwave dielectric properties of $\varepsilon$r=37, Q.f0=47,000 (at 7 GHz), and $\tau$f=-2 ppm/$^{\circ}C$ were obtained near 0.6La2/3TiO3-0.4LaAlO3 (x=0.4) composition.

• Applied Chemistry for Engineering
• /
• v.23 no.6
• /
• pp.572-576
• /
• 2012

This study presents the $CO_2$ methanation reaction on Pt catalysts for reducing the amount of $CO_2$, one of greenhouse gases. The AlO(OH) of $Al_2O_3$precusor was used as a support via a thermal treatment and the Pt was used as an active metal. In XRD results, it was confirmed that the Pt was well dispersed and the support existed as the gamma $Al_2O_3$phase. The $Pt/Al_2O_3$ catalyst calcined at $600^{\circ}C$ showed the highest conversion efficiency and selectivity.

• Journal of the Korean Ceramic Society
• /
• v.43 no.9 s.292
• /
• pp.575-581
• /
• 2006

To precipitate the complex gel of flux and aluminum hydroxides gel, aqueous solution of the mixture of $Na_2CO_3\;and\;Na_2PO_4{\cdot}12H_2O$ was added with stirring in aqueous solution of the mixture of $Al_2(SO_4)_3{\cdot}14{\sim}18H_2O,\;Na_2SO_4$, and then the complex gel was aged in $0{\sim}30h\;at\;90^{\circ}C$. As aging time passed, the aluminum hydroxides was grown into the acicular AlO(OH) gel. Also, aging time had an effect on physical properties of the AlO(OH) gel and on crystal growth of the flaky ${\alpha}-Al_2O_3$ prepared by molten-salt precipitation. In this study, the complex gel was crystallized in temperature range of $400{\sim}1,200^{\circ}C$ after drying at $110^{\circ}C$, and then it was investigated to effect of aging time on precipitation temperature, size, thickness, morphology and particle size distribution of the flaky ${\alpha}-Al_2O_3$ crystal. As aging time passed, the flaky a${\alpha}-Al_2O_3$ crystal showed a tendency toward an increase in size and thickness as result from an increase in BET surface area and pore volume of the acicular AlO(OH) gel.

• Journal of the Korean Ceramic Society
• /
• v.34 no.6
• /
• pp.668-676
• /
• 1997

Al2O3/SiC nanocomposites are fabricated through intensive ball milling to mix fine SiC particles uniformly with the Al2O3 powder. Another role of milling is to reduce particle sizes by crushing particles as well as agglomerates. However, balls are worn during ball milling and the sample powder mixtures pick up to weight loss of the balls. In this study, pressureless sintering was performed to obtain Al2O3/SiC nanocomposites. It was found that the wear rate of zirconia balls during milling was considerable, and the zirconia addition after even a few hours of ball milling could increase the sintering rates of the nanocomposites significantly. Thus, addition of ZrO2 changed the sintering behaviors as well as mechanical properties of Al2O3/SiC nanocomposites.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.4
• /
• pp.626-631
• /
• 1997

AlSiCa powders were prepared from the domestic Hadong Kaolin ($Al_2O_3{\cdot}2SiO_2{\cdot}2H_2O$). As a result of the reaction of Hadong Kaolin and carbon powder at reducing atmosphere, $Al_2O_3{\cdot}SiC$ composite started to form at $1300^{\circ}C$ and completed at $1400^{\circ}C$. The optimum amount of carbon was 1:4 in mole ratio. It was found that only bright-green $\beta-SiC$ phase forms when the mixture was packed without carbon powder in alumina crucible.

• Korean Journal of Soil Science and Fertilizer
• /
• v.32 no.1
• /
• pp.39-46
• /
• 1999

This study was performed to examine the effect of initial composition ratio and various reaction conditions on CEC and crystallinity of the product in hydrothermal synthesis of zeolitic materials from fly ash. Na-P1 zeolite was formed from the mixture with $SiO_2/Al_2O_3$ ratio above 2.55, however from the mixture with $SiO_2/Al_2O_3$ ratio below 2.25 hydroxy sodalite was formed. The CEC of reaction product(Na-P1 zeolite) treated with 3N-NaOH, $Na_2O/Al_2O_3$ ratio 2.55 and $SiO_2/Al_2O_3$ ratio 2.0 for 12 hours at $103^{\circ}C$ was about $285cmol^+kg^{-1}$, which was higher than those of the products of other reaction condition. The crystallinity of Na-P1 zeolite as high as 45.1% was attained at the optimum reaction condition of 2N-NaOH, $SiO_2/Al_2O_3$ ratio 2.55, $Na_2O/Al_2O_3$ ratio 1.5 for 12 hours at $103^{\circ}C$. The XRD peak of the reaction product could be measured at 7.16, 5.04, 4.12, 3.18, $2.69{\AA}$ and tetragonal pillar shape observed by SEM image be characteristic for Na-P1 zeolite. Judging from the result, it should be considered the optimum synthesis condition for Na-P1 zeolite from fly ash was 2~3N NaOH, $SiO_2/Al_2O_3$ ratio 2.55 and $Na_2O/Al_2O_3$ ratio 1.5~2.0 for 12 hours at $80{\sim}103^{\circ}C$.

• Journal of the Korean Chemical Society
• /
• v.32 no.3
• /
• pp.267-275
• /
• 1988

Fine powders of amorphous $Al_2O_3,\;SiO_2,\;Al_2O_3-SiO_2$ system were prepared by hydrolysis of solutions containing alkoxides, aluminium tri-isopropoxide and silicon tetra-ethoxide. High purity ultrafine ${\beta}-sialon$ powders were prepared by the carbothermal reduction-nitridation of amorphous $Al_2O_3-SiO_2$ powders mixed with carbon black as a reducing agent. In the hydrolysis step the effect of the factors such as pH, reaction temperature and amount of water on the conversion rate of alkoxides to oxides was investigated. In the carbothermal reduction-nitridation the reaction path was assumed by the analysis of intermediates formed in the process of ${\beta}-sialon$ synthesis and the reaction kinetics of ${\beta}-sialon$ formation was considered.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.107-107
• /
• 2016

TiCrAlSiN films were developed in order to improve the high-temperature oxidation resistance, corrosion resistance, and mechanical properties of conventional TiN films that are widely used as hard films to protect and increase the lifetime and performance of cutting tools or die molds. In this study, a nano-multilayered TiAlCrSiN film was deposited by cathodic arc plasma deposition. It displayed relatively good oxidation resistance at $700-900^{\circ}C$, owing to the formation protective oxides of $Al_2O_3$, $Cr_2O_3$, and $SiO_2$, and semiprotective $TiO_2$. At $1000^{\circ}C$, the increased temperature led to the formation of the imperfect oxide scale that consisted primarily of the outer ($TiO_2$,$Al_2O_3$)-mixed scale and inner ($TiO_2$, $Al_2O_3$, $Cr_2O_3$)-mixed scale.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.37-37
• /
• 2008

에어로졸데포지션법을 이용하여 집적화 기판을 위한 $Al_2O_3$-PMMA 복합체 후막을 상온에서 구리 기판 위 에 제조하였다. XRD, FT-IR 분석을 통해 코팅된 막은 $Al_2O_3$와 PMMA의 혼합물로 존재함을 확인하였으며 성막 중 $Al_2O_3$. PMMA의 상호작용과 PMMA 파우더의 거동에 대한 분석을 통해 $Al_2O_3$-PMMA 복할체 후막의 성막 양상을 확인할 수 있었다. 또한 기판 거칠기에 따라 초기 계면의 양상이 달라질 수 있음을 확인하였고 이러한 초기 계면의 상태가 $Al_2O_3$-PMMA 복합체 후막의 제조에 있어 매우 중요함을 알 수 있었다. 본 연구에서는 에어로졸데포지션법을 이용한 $Al_2O_3$-PMMA 복합체 후막의 성막 양상을 통해 세라믹-폴리머 복합체의 제조에 있어서의 주요 변수들을 알아보고 $Al_2O_3$-PMMA 복합체 후막의 전기적인 특성을 확인하였다.

• 한국연소학회:학술대회논문집
• /
• 2007.05a
• /
• pp.37-44
• /
• 2007

A nickel foam, one of metal foams was seleced as a catalyst support instead of conventional ceramic materials. $Al_2O_3$ was coated on the surface of nickel foam to increase the surface area. $Al_2O_3$ coating process was based on sol-gel process. SEM image was obtained and $Al_2O_3$ coverage was confirmed. Combustion experiments were carried out using SUS combustor and $H_2$/air mixture. Temperatures were measured with different equivalence ratios and $H_2$ flow rates. $H_2$ conversion rates were calculated by the analysis of product gas using gas chromatography. Catalytic combustion of $H_2$ was complete and stable with Pt/$Al_2O_3$ coated nickel foam and influences of water vapor were confirmed during the beginning of combustion.