• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.4
• /
• pp.190-199
• /
• 2015

The study is intended to investigate the effect of solution treatment on microstructure and corrosion behavior of AZ91(Mg-9%Al-1%Zn-0.3%Mn)-2%Ca casting alloy. In as-cast state, the AZ91-2%Ca alloy consisted of intermetallic ${\beta}(Mg_{17}Al_{12})$, $Al_8Mn_5$ and $Al_2Ca$ phases in ${\alpha}-(Mg)$ matrix. After the solution treatment, Al within the ${\alpha}-(Mg)$ matrix was distributed more homogeneously, along with the slight decrease in the total amount of intermetallic compounds. The corrosion resistance of the AZ91-2%Ca alloy was improved after the solution treatment. The microstructural examinations for the solution-treated samples revealed that the better corrosion resistance may well be related to the incorporation of more oxides and hydroxides such as $Al_2O_3$, $Al(OH)_3$, CaO and $Ca(OH)_2$ into the surface corrosion product without dissolution of the intermetallic phases along the grain boundaries.

• Journal of the Korean Solar Energy Society
• /
• v.38 no.1
• /
• pp.25-36
• /
• 2018

The stoichiometric mixture of evaporating materials for the $CaAl_2Se_4$: Co single crystal thin film was prepared from horizontal furnace. Using extrapolation method of X-ray diffraction patterns for the polycrystal $CaAl_2Se_4$, it was found orthorhomic structure whose lattice constant $a_0$, $b_0$ and $c_0$ were 6.4818, $11.1310{\AA}$ and $11.2443{\AA}$, respectively. To obtain the $CaAl_2Se_4$: Co single crystal thin film, $CaAl_2Se_4$: Co mixed crystal was deposited on throughly etched Si (100) by the HWE (Hot Wall Epitaxy) system. The source and substrate temperature were $600^{\circ}C$ and $440^{\circ}C$ respectively. The crystalline structure of $CaAl_2Se_4$: Co single crystal thin film was investigated by the double crystal X-ray diffraction (DCXD). Hall effect on this sample was measured by the method of Van der Pauw and studied on carrier density and mobility depending on temperature. From Hall data, the mobility was likely to be decreased by impurity scattering in the temperature range 30 K to 100 K and by lattice scattering in the temperature range 100 K to 293 K. The temperature dependence of the energy band gap of the $CaAl_2Se_4$: Co obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=3.8239eV-(4.9823{\times}10^{-3}eV/K)T_2/(T+559K)$. The open-circuit voltage, short current density, fill factor, and conversion efficiency of $p-Si/p-CaAl_2Se_4$: Co heterojunction solar cells under $80mW/cm^2$ illumination were found to be 0.42 V, $25.3mA/cm^2$, 0.75 and 9.96%, respectively.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2003.07a
• /
• pp.836-839
• /
• 2003

We have synthesized some phosphors in the system $CaO-Y_{2}O_3-Al_{2}O_{3}$ by combinatorial polymerized-complex method. Composition and synthetic temperature of phosphors in the liblary was screened from the emission intensities of individual samples under VUV excitation. In $Tb^{3+}$-activated $CaO-Y_{2}O_3-Al_{2}O_{3}$, green phosphors showing good intensity were found to be $CaYAl_{3}O_{7}$, $CaYalO_{4}$, $YAlO_{3}$, $Y_{3}Al_{5}O_{12}$, $Y_{4}Al_{2}O_{9}$, $Ca_{3}Al_{2}O6$.

• Journal of Korea Foundry Society
• /
• v.34 no.6
• /
• pp.187-193
• /
• 2014

In the present work, the effect of adding Ce on the corrosion behavior of Mg-4Al-2Sn-1Ca alloy was investigated. The studied alloys were fabricated by gravity casting method and a potentiodynamic polarization, A.C. impedance and hydrogen evolution tests were carried out in a 3.5% NaCl solution with pH 7.2 at room temperature to measure the corrosion properties of Mg-4Al-2Sn-1Ca-xCe alloys. The microstructure of the Mg-4Al-2Sn-1Ca alloy was composed of ${\alpha}$-Mg, Mg17Al12, Mg2Sn and CaMgSn phase. Also, a $Al_{11}Ce_3$ phase was newly formed by the addition of Ce. With an increase of the Ce contents, the microstructure became refined and the corrosion resistance improved.

• Korean Journal of Environmental Agriculture
• /
• v.30 no.3
• /
• pp.229-233
• /
• 2011

BACKGROUND: Soil acidification, which is known to be one of the reasons of forest decline, is associated with decreases in exchangeable Ca and increases in Al concentration, leading to low Ca/Al ratio in soil solution. As tree rings are datable archives of environmental changes, Ca/Al ratios of annual growth ring may show decreasing pattern in accordance with the progress of soil acidification. This study was conducted to investigate Ca/Al pattern of Pinus densiflora tree ring in an attempt to test its usefulness as an indicator of historical soil acidification. METHODS AND RESULTS: Three P. densiflora tree disks were collected from P. densiflora forests in Jeonnam province, and soil samples (0-10, 10-20, and 20-30 cm in depth) were also collected from the tree locations. Soils were analyzed for pH and exchangeable Ca and Al concentrations, and Ca/Al was calculated. Annual growth rings formed between 1969 and 2007 were separated and analyzed for Ca/Al. Soil Ca/Al was positively (P<0.01) correlated with soil pH, suggesting that soil acidification decreased Ca while increasing Al availability, lowering Ca/Al in soil solution. The Ca/Al of tree rings also showed a decreasing pattern from 18.2 to 5.5 during the period, and this seemed to reflect historical acidification of the soils. CONCLUSION(s): The relationship between soil pH and Ca/Al and the decreasing pattern of Ca/Al of tree ring suggest that Ca/Al of tree ring needs to be considered as a proxy of the progress of soil acidification in P. densiflora forest in southern Korea.

• Journal of the Korean Ceramic Society
• /
• v.31 no.4
• /
• pp.448-456
• /
• 1994

The reaction-sintered alumina and zirconia-alumina ceramics were fabricated from the Al/Al2O3 or Zl/ZrO2(Ca-PSZ) powder mixtures via the attrition milling. And the effects of the milling characteristics of used raw powders on reaction sintering were investigated. After attrition milling and isopressing at 400 MPa the Al/Al2O3 specimen was oxidated at 1200℃ for 8 hours followed by sintering at 1550℃ for 3 hours. Because mixed powders of flake-type Al with coarse alumina was much more effectively comminuted than the globular-type Al with coarse alumina powders, it's sintered body of more than 97% theoretical density was achived, but low contents of Al leads to relatively higher shrinkage of about 8%. And because coarse alumina particles was much more beneficial in cutting and reducing the ductile Al particles, using the coarse alumina powder was much more effective in reaction sintering. Fused Ca-PSZ powder was reaction sintered with Al at 1550℃ for 3 hours and low shrinkage ZrO2-Al2O3 composites were fabricated. But because Al/Ca-PSZ powder mixtures were not effectively milled the reaction sintering and densification was difficult. And the Ca ion in Ca-PSZ grains diffused into alumina grains during sintering so that the unstabilization of Ca-PSZ body was occured which gave the microcracks in the specimens.

• Korean Journal of Materials Research
• /
• v.16 no.2
• /
• pp.92-98
• /
• 2006

Molecular dynamics simulations were performed to study interface structures between an $Al_2O_3$ crystalline phase and a interface phase of $CaAl_2Si_2O_8$. We calculated atomic structures and excess interface energies in systems with different thicknesses of the interface film. It was found that excess interface energies at first readily decreased with increasing film thickness, but increased for larger thicknesses of more than 2 nm. The excess energies of $Al_2O_3/CaAl_2Si_2O_8$ interfaces exhibit a minimum at a thickness around 1 nm. In this range of film thicknesses, the atoms in the interface film show a short-range ordered structure and slow diffusion rather than the random structure and rapid diffusion expected to an observation of an equilibrium thickness for interface films in ceramics.

• Transactions of Materials Processing
• /
• v.26 no.5
• /
• pp.306-313
• /
• 2017

This study investigated the microstructure, tensile strength, and high cycle fatigue properties of ADC12 aluminum alloys with different $Mg+Al_2Ca$ contents manufactured using die casting process. Microstructural observation identified the presence of ${\alpha}-Al$, eutectic Si, $Al_2Cu$, and Fe-intermetallic phases. The increase of $Mg+Al_2Ca$ content resulted in finer pore size and decreased pore distribution. Room temperature tensile strength tests were conducted at strain rate of $1{\times}10^{-3}/sec$. For 0.6%Mg ADC12, measured UTS, YS, and El were 305.2MPa, 157.0MPa, and 2.7%, respectively. For 0.8%Mg ADC12, measured UTS, YS, and El were 311.2 MPa, 159.4 MPa, and 2.4%, respectively. Therefore, 0.8% ADC12 alloy had higher strength and slightly decreased elongation compared to 0.6% Mg ADC12. High cycle fatigue tests revealed that 0.6% Mg ADC12 alloy had a fatigue limit of 150 MPa while 0.8% Mg ADC12 had a fatigue limit of 160MPa. It was confirmed that $Mg+Al_2Ca$ added ADC12 alloy achieved finer, spherical eutectic Si particles, and $Al_2Cu$ phases with greater mechanical and fatigue properties since size and distribution of pores and shrinkage cavities decreased as $Mg+Al_2Ca$ content increased.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.4
• /
• pp.1-9
• /
• 2020

This study conducted to understand effects of CA (CaAl₂O₄) and CA₂ (CaAl₄O₇) ratio on chloride binding ability and compressive strength and pore structure of cement mortar incorporating mixture of CA and CA₂. The Portland cement based specimens were mixed with the clinkers CA and CA₂, and these calcium aluminate clinker mixture were replaced 0, 5, 10% by weight of cement. After all the test specimens were cured for 28 days under water curing, they were immersed in the distilled water and NaCl solution. As a result, 28 days compressive strength of all specimens was similar, and As the replacement ratio of calcium aluminate clinker in the specimen increased, Friedel's salt production tended to increase. However, it was dependent on the amount of Al₂O₃ in the level of 5% replacement and CA ratio in the level of 10% replacement. Through equilibrium isotherm result, it was also indicated that as replacement ratio of calcium aluminate clinker in cement matrix increased, chloride binding capacity was improved, and chloride penetration was suppressed. In this study, the specimen replaced with 10% of the calcium aluminate clinker mixture (CA 39%, CA₂ 60%) was remarkable to control chloride attack. We figured out necessity to understand optimal CA/CA₂ ratio to effectively apply CA₂ as a sustainable building material by improving the chloride binding ability in Portland cement based system.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.1
• /
• pp.42-45
• /
• 2017

The magnesium-base AZ61 alloy was cast while adding 1% CaO powder into the melt. It was hot extruded, and oxidized at $550-650^{\circ}C$ in air in order to study its microstructure and oxidation behavior. Initially added CaO powder reacted with Al in the melt to $Al_2Ca$ particles that aligned along the extrusion direction. The formed $Al_2Ca$ particles increased the oxidation resistance through forming the superficial CaO scale at the upper part of the thin MgO oxide scale.