• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.1278-1282
• /
• 2004

수열처리법으로 nano-sized $CeO_2$ 입자를 $Al_3O_3$ 입자의 표면에 균일하게 코팅하여 $AL_2O_3/O_2$ composite 연마 입자를 제조하었다. 제조된 $Al_2O_3\CeO_2$ composite 입자의 뭍성을 TEM, XRD, zeta potential analyzer 및 particle size analyzer로 측징하였다. $Al_2O_3/CeO_2$ composite 입자와 구성된 슬러리와 비교 시료로서 $Al_2O_3$와 $CeO_2$ 입자를 혼합한 슬러리를 사용하여 thermal oxide film에 대한 연마특성을 평가하였다. 연마슬러리에 포함된 $A1_2O_3/CeO_2$ composite 입자와 $Al_2O_3$와 $CeO_2$ 혼합입자에서 나노 크기의 세리아 입자가 sub-micron 크기의 알루미나 입자의 표면에 균일하게 코팅되므로서 $Al_2O_3$ 단일 성분의 슬러리에 비해 removal rate(RR)는 106 nm/min, WIWNU는 $8\sim9%$, roughness는 $2.6{\AA}$의 향상된 연마 특성을 나타내었다. 알루미나 입자의 불규칙한 형상 때문에 $Al_2O3/CeO_2$ composite 슬러리와 $Al_2O_3$ 와 $CeO_2$ 혼합슬러리의 연마 특성이 비슷한 수준을 나타내었다.

• Journal of the Korean Ceramic Society
• /
• v.25 no.2
• /
• pp.117-124
• /
• 1988

The properties of the powders of the system Al2O3-ZrO2-Y2O3 prepared by precipitation method were investigated. Al2(SO4)3$.$18H2O3, ZrOCl2$.$8H2O and YCl3$.$6H2O were used as starting materials. Amorphous aluminum hydrate prepared by precipitation method was completely transformed to alpha Al2O3 as a result of calcining at 1100$^{\circ}C$ for 1 hr and gamma, delta and theta phases appeared as transition phases. In ZrO2-Y2O3 system prepared by co-precipitation method, the crystallization temperature of ZrO2 was increase with Y2O3 contents. The coupled crystallization occured in coprecipitated Al2O3-ZrO2-Y2O3 system, therefore the formation temperature of alpha Al2O3 and ZrO2-Y2O3 system. In this ternary system, the powder morphology showed a particular shape which was composed of large Al2O3 grains having small spherical ZrO2 particles within large Al2O3 grain and relatively large ZrO2 particles along the grian boundaries.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.81-81
• /
• 2009

Non-sintered Alumina films were fabricated via inkjet printing processes without a high temperature sintering process. The packing density of these inkjet-printed alumina films measured around 60%. Polymer resin was infiltrated thru these non-sintered films in order to fill out the 40% of voids constituting the rest of the inkjet-printed films. The concept of inkjet-printed Alumina-Resin hybrid materials was designed in order to be applicable to the ceramic package substrates for 3D-system module integration which may possibly substitute LTCC-based 3D module integration. So, the dielectric properties of these inkjet-printed $Al_2O_3$ hybridmaterialsareofourgreatinterest. We have measured dielectric constant and dissipation factor of the inkjet-printed $Al_2O_3$-resinhybridfilmsbyvaryingtheamountofresininfiltratedthruthe$Al_2O_3$films.

• Journal of the Korean Ceramic Society
• /
• v.27 no.6
• /
• pp.799-807
• /
• 1990

In this study, effects of oxide additives on mechanical properties and microstructure of A1N and A1N polytype ceramics were investigated. Fine A1N powder was synthesized by nitriding alumiuim hydroxide prepared from Al-isopropoxide, at 1350$^{\circ}C$ for 10h in N2 atmosphere. By adding 3w/o Y2O3, 0.56w/o CaO, and 10w/o SiO2 to AlN powder, AlN and AlN polytype ceramics were prepared by hot-pressing under the pressure of 30 MPa at 1800$^{\circ}C$ for 1h. AlN ceramics with no additives formed considerable amount of AlON phase, while AlN ceramics doped with Y2O3 or CaO decreased AlON phase and formed Y-Al or Ca-Al oxide compound. AlN＋10w/o SiO2(＋3w/o Y2O3) composition produced AlON and AlN polytype compound having 21R as a major phase. Room temperature flexural strength of AlN ceramics with no additive was 246MPa, and room temperature flexural strength and critical temperature difference by thermal shock(ΔTc) of AlN ceramics dooped with Y2O3 or CaO were 532MPa/340$^{\circ}C$ and 423MPa/300$^{\circ}C$, respectively. Y2O3 and CaO used as sintering agent played roles of densification and oxygen removal of AlN ceramics, and affected grain growth/grain morphologies of AlN ceramics.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.332-332
• /
• 2010

We have successfully demonstrated the inkjet printing method to create $Al_2O_3$ films withouWe have successfully demonstrated the inkjet printing method to create $Al_2O_3$ films without a high temperature sintering process. In order to remove the coffee ring effect in the ink drop, we have introduced a co-solvent system in order to create Marangoni flow in the ink drop, which leads to the dense packing of ceramic powders on the substrate during inkjet process. The packing density of the Inkjet-printed $Al_2O_3$ films is around 60% (max. 70%) which is very high compared to the value obtained from the same material films by other conventional methods such as film casting, dip coating process, etc. The voids inside the films (which are around 40% of the entire film volume) are filled with the polymer resin (Cyanate ester) by the infiltration process. This resin infiltration is also implemented by the inkjet printing process right after the Ah03 film ink-jetting process. The microstructures of the printed $Al_2O_3$ films are investigated by Scanning Electron Microscope (SEM) to understand the degree of packing density in the printed films. The inkjet-printed $Al_2O_3$ films have been characterized to investigate its thickness and roughness. Quality factor of the printed $Al_2O_3$ film is also measured to be over 300 at 1MHz.

• Journal of the Korean Ceramic Society
• /
• v.36 no.9
• /
• pp.997-1005
• /
• 1999

• Journal of the Korean Ceramic Society
• /
• v.20 no.1
• /
• pp.49-54
• /
• 1983

The main object of this study is to investigate the effect of Al powder as an additive on the sintering of calcined alumina comparing with that of calcined alumina alone. The degree of Al oxidation is calculated by measuring the weight increase during the firing Water absorption bulk density and compressive strength of the $Al_2O_3+Al$ system at each temperature are compared with those of $Al_2O_4$ alone. The $Al_2O_3+Al$ system shows better physical propeties than Al2O3 alone and it seems by the SEM observation that the fine oxidized Al particles(fine $Al_2O_3$ particles submicron unit) fill the interstices of the original $Al_2O_3$ par-ticles and thus result in the well-close-packed arrangement of the particles.

• Journal of the Korean Ceramic Society
• /
• v.20 no.1
• /
• pp.25-30
• /
• 1983

This experiment was studied in the system of (1-x) CaO MgO $2SiO-Al_2O_3$ to investigate forming of solid solution. The technique empolyed was the well known water-quenching method. Differential thermal analysis of the each glass water quenched indicated that under 30 mole% $Al_2O_3$ was lowered with increasing of the amount of $Al_2O_3$ It was supposed by X-ray diffraction patterns of each specimen sintered at various temperature that only solid solution was formed under the 30mole % $Al_2O_3$ compositions solid solution and anorthite were formed at the 20mole% $Al_2O_3$ composition anorthite solid solution and spinel$(MgAl_2O_4)$ were formed over the 40mole% $Al_2O_3$ compositions. The maximum density and thermal expanison coefficient was 2.89g/cm 7.74x106./C$^{\circ}$ respectively in the composi-tion of 10 mole% $Al_2O_3$ . All the specimens showed linear thermal expansion behavior. Microhardness was as high as 850kg/nm2 in the composition of 5, 10, 20 mole % $Al_2O_3$ and dielectric constant was 7.3-6.9.

• Journal of the Korean Ceramic Society
• /
• v.29 no.6
• /
• pp.431-440
• /
• 1992

• Journal of the Semiconductor & Display Technology
• /
• v.20 no.2
• /
• pp.61-66
• /
• 2021

In this study, we studied the alternative of plasma resistant ceramic parts that constitute plasma chambers in the semiconductor dry etching process. MgO-Al₂O₃-SiO₂(MAS) glass was made of 13 types of glass using the Design Of Experiments(DOE) and the effect on thermal properties such as glass transition temperature and crystallization temperature depending on the content of each composition and etching resistance to CF₄/O₂/Ar plasma gas. MAS glass showed excellent plasma resistance and surface roughness up to 20 times higher than quartz glass. As the content of Al₂O₃ and MgO increases, the plasma resistance is improved, and it has been confirmed that it has an inverse relationship with SiO₂.