• Journal of the Korean Ceramic Society
• /
• v.36 no.4
• /
• pp.410-416
• /
• 1999

The reactivity of three kinds of spinels which CaO-Al2O3-SiO2 slag was investigated in terms of mineral phases and microstructures. New crystal products were not formed by reaction of 12CaO.7Al2O3 in the slag with spinels and free MgO components was preferenctially dissolved into slag for MgO-rich spinel and stoichiometric spinel. Meanwhile mineral phase was changed from 12CaO.7Al2O3 to CaO.Al2O3 to CaO.2Al2O3 finally to CaO.6Al2O3 having high melting point for Al2O3 -rich spinel. The Fe-oxide component of the slag was taken up by only stoichiometric spinel grains within the spinel clinker and the trapped amount of Fe-oxide was independent of MgO content of MgO in spinel clinker the more th resistance to slag corrosion but the less resistance to slag penetration.

• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.593-602
• /
• 1991

Al2O3 and NiO-doped Al2O3 powders were prepared from the ethanol solution of Al (NO3)3$.$9H2O and Ni(NO3)2$.$6H2O by spray pylolysis method using two-fluid nozzle. As a result of spraying test with 0.3 mol/{{{{ iota }} concentration starting solution, mean droplet sizes varied with 8.99∼9.69$\mu\textrm{m}$ and those standard deviation were 4.57∼5.12. As-prepared powders which were synthesized at 1000$^{\circ}C$ have spherical shape, sizes of 0.1∼3.0$\mu\textrm{m}$ and specific surface area of 22.34∼24.20㎡/g. Most powders consisted of {{{{ gamma }}-Al2O3 phase and transforned into ${\alpha}$-A;2O3 phase by calcination at 1100$^{\circ}C$ for 1 hr. NiO-doped Al2O3 sintered bodies had better sinterability than those of pure Al2O3 and 0.3 wt% NiO-doped Al2O3 had near theoretical density and dense microstructure.

• Journal of the Korean Ceramic Society
• /
• v.38 no.10
• /
• pp.936-941
• /
• 2001

The influence of the ${Al_2}{O_3}$ particle size on flaw tolerance of the $ZrO_2/{Al_2}{O_3}$ composites prepared by mixing 5.31 mol% ${Y_2}{O_3}$-4.45 mol% ${Nb_2}{O_5}$-90.31 mol% $ZrO_2$ and ${Al_2}{O_3}$ was investigated. The composites exhibited rising R-curve behavior and plateau fracture toughness of 7.9 and $8.8MPam^{1/2}$ for the additions of 20 vol% of 0.2 and $2.8{\mu}m$ ${Al_2}{O_3}$ particles, respectively. The difference in the fracture toughness resistance was attributed mainly to the grain size of tetragonal $ZrO_2$ phase in the composites, which scaled with the ${Al_2}{O_3}$ particle size.

• Journal of the Korean Ceramic Society
• /
• v.35 no.9
• /
• pp.923-932
• /
• 1998

Al2O3/Al composites were produced by displacement reaction method which was carried out by imm-ersing the sintered silica preform which was prepared form fused silica powder in molten aluminu. an ac-tivation energy of 94kJ/mole was calculated from Al-SiO2 reaction data in 1000-130$0^{\circ}C$ temperature range With increase of reaction temperature the alumina particle in the Al2O3/Al composites produced with pur metal Al showed grain growth and the growth of alumina particle in Al2O3/Al composite produced by using of Mg contained Al alloy was inhibited. The flexural strength of Al2O3/Al composites produced at 100$0^{\circ}C$ showed the highest value as 393 MPa. Flexural strength of the composite fabricated at 85$0^{\circ}C$ showed higher deviation than that of the composite produced at above 100$0^{\circ}C$ Low flexural strength of the composite fa-bricated at 120$0^{\circ}C$ due to the growth of pore and alumina particle size. The hardness of composites de-pended on alumina content in Al2O3/Al composite decreased with increasing of aluminium content in case the same alumina content and increased with increasing of silicon content in composite.

• Journal of the Korean Vacuum Society
• /
• v.19 no.5
• /
• pp.385-390
• /
• 2010

We studied the optical characteristics of ZnO:Al and $Al_2O_3$ coated ZnO nanorods. When ZnO:Al is deposited around the undoped ZnO nanorods, thermal diffusion of Al into ZnO gives rise to decrease the binding energy of neutral donor bound exciton whereas an insulating Al2O3 is coated around ZnO, we found that semiconducor-insulator interface states play an important role in optical quenching.

• Journal of the Korean Ceramic Society
• /
• v.28 no.1
• /
• pp.11-18
• /
• 1991

A precipitation method, one of the most effective liquid phase reaction methods, was adopted in order to prepare high-tech Al2O3/ZrO2 composite ceramics, and the effects of stress-induced phase transformation of ZrO2 on thermal shock behavior of Al2O3-ZrO2 ceramics were investigated. Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Metal hydroxides were obtained by single precipitation(process A) and co-precipitation(process B) method at the condition of pH=7, and the composition of Al2O3-ZrO2 composites was fixed as Al2O3-15v/o ZrO2(+3m/o Y2O3). Critical temperature difference showing rapid strength degradation by thermal shock showed higher value in Al2O3/ZrO2 composites(process A : 20$0^{\circ}C$, process B : 215$^{\circ}C$) than in Al2O3(175$^{\circ}C$). The improvement of thermal shock property for Al2O3/ZrO2 composites was mainly due to the increase of strength at room temperature by adding ZrO2. The strength degradation was more severe for the sample with higher strength at room temperature. Crack initiation energies by thermal shock showed higher values in Al2O3/ZrO2 composites than in Al2O3 ceramics due to increase of fracture toughness by ZrO2.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.6
• /
• pp.886-894
• /
• 1990

Sinterbility, microstructure, mechenical and electrical properties of yttriastabilized zirkconiz (92 mole % ZrO2 + 8 mole % Y2O3) doped with 0.5 mole % SiO2 and 0-2.O mole% Al2O3 were studied as a functin of Al2O3 addition. Sintered density increased with increasing Al2O3 addition up to o.5 mole%but decreased up to 1.0mole% Al2O3. Vickers hardness is proportional to sintered density. The specimen added 0.5mole% Al2O3 and 0.5mole% SiO2 exhibited a maximum conductivity. And the specimen added 0.5 mole % Al2O3 and 0.5 mole% SiO2 was measured a maximum electromotive force for a characteristics of oxyzen partial pressure.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.2
• /
• pp.185-190
• /
• 1999

An $Al_2O_3/Fe$ composite was synthesized through the double stage processes by a reaction sintering which requires simple process and equipments but provides near-net-shape, a reduction/oxidation process for 5 hrs at $650^{\circ}C$ was followed by sintering at $1200^{\circ}C$ to form an $Al_2O_3/Fe$ composite. The composite processed through the double stage sintering are mainly consists of $\alpha$-Fe and ${\alpha}Al_2O_3$ with minor amount of $FeAl_2O_4$, a spinnel structure which is known to prevent Fe from filling up the pores and good contact with $Al_2O_3/Fe$ particles.

• Journal of the Korean Applied Science and Technology
• /
• v.33 no.2
• /
• pp.401-410
• /
• 2016

The $Pt-Sn/Al_2O_3$ catalysts mixed with metal oxides for propane dehydrogenation were studied. $Cu-Mn/{\gamma}-Al_2O_3$, $Ni-Mn/{\gamma}-Al_2O_3$, $Cu/{\alpha}-Al_2O_3$ was prepared and mixed with $Pt-Sn/Al_2O_3$ to measure the activity for propane dehydrogenation. As standard sample, $Pt-Sn/Al_2O_3$ catalyst mixed with glassbead was adopted. In the case of catalytic activity test after non-reductive pretreatment of catalyst and metal oxide, $Pt-Sn/Al_2O_3$ mixed with $Cu-Mn/{\gamma}-Al_2O_3$ showed higher conversion of 15% and similar selectivity at $576.5^{\circ}C$, compared to conversion of 8% in standard sample. In the case of catalytic activity test after reductive pretreatment of catalyst and metal oxde, $Cu/{\alpha}-Al_2O_3$ showed higer yield than standard sample. But, increase of yield of most of samples after reductive pretreatment was not significant, so it was found that lattice oxygen of $Cu-Mn/{\gamma}-Al_2O_3$ is effective to propane dehydrogenation.

• Journal of the Korean Ceramic Society
• /
• v.30 no.9
• /
• pp.731-739
• /
• 1993

R-curve measurements were performed on Al2O3(matrix)-ZrO2-SiC whisker composite and Al2O3-ZrO2, Al2O3-SiC whisker composites in the favor of comparing the effect of ZrO2 and SiC whisker, as a second phase, to Al2O3 matrix. Al2O3-SiC whisker and Al2O3-ZrO2-SiC whisker were fabricated by hot pressing at 1$700^{\circ}C$, 15MPa and Al2O3-ZrO2 by pressureless sintering at 1$600^{\circ}C$. A controlled flaw/strength technique was utilized to determine fracture resistance as a function of crack extension and R-curve behaviour was determined from the relationship which is KR=K0(Δa)m. R-curveresults were KR=6.173$\times$Δa0.031 for Al2O3-ZrO2, KR=18.796$\times$Δa0.172 for Al2O3-SiC whisker and KR=11.96$\times$Δa0.110 for Al2O3-ZrO2-SiC whisker composite. From the analysis of R-curve and expeirmental data above three composites, it is found that R-curve behaviour of Al2O3-ZrO2-SiC whisker composite was dominated initially by the strengthening effect of ZrO2 and after, some extended crack were influenced by the effect of SiC whisker. Analysis of SEM and X-ray data revealed that whisker bridging in the crack wake and whisker pull-out mechanisms were the main mechanism for the R-curve behaviour.