• Korean Journal of Materials Research
• /
• v.12 no.1
• /
• pp.48-53
• /
• 2002

$Al_2O_3-SiC$ and $Al_2O_3-SiC$-TiC composite powders were prepared by SHS process using $SiO_2,\;TiO_2$, Al and C as raw materials. Aluminum powder was used as reducing agent of $SiO_2,\;TiO_2$ and activated charcoal was used as carbon source. In the preparations of $Al_2O_3-SiC$, the effect of the molar ratio in raw materials, compaction pressure, preheating temperature and atmosphere were investigated. The most important variable affecting the synthesis of $Al_2O_3-SiC$ was the molar ratio of carbon. Unreactants remained in the product among all conditions without compaction. The optimum condition in this reaction was $SiO_2$: Al: C=3: 5: 5.5, 80MPa compaction pressure under Preheating of $400^{\circ}C$ with Ar atmosphere. However there remains cabon in the optimum condition. The effect of $TiO_2$ as additive was investigated in the preparations of $Al_2O_3-SiC$. As a result of $TiO_2$ addition, $Al_2O_3-SiC$-TiC composite powder was prepared. The $Al_2O_3$ powder showed an angular type with 8 to $15{\mu}m$, and the particle size of SiC powder were 5~$10{\mu}m$ and TiC powder were 2 to $5{\mu}m$.

• Journal of the Korean Ceramic Society
• /
• v.38 no.9
• /
• pp.794-798
• /
• 2001

$Y_{2-x}SiO_5:Ce_x^{3+}$(x=0.002∼0.04) phosphors were prepared by sol-gel process, amorphous crystal phase was observed in calcining dry gel at 800$^{\circ}$C, but pure $X_2$ type of type $Y_2SiO_5$ phase appeared from heat treatment above 1000$^{\circ}$C. Light absorption of tye $Y_2SiO_5$ host lattice occurred at 230∼360nm, and light absorption of the $Y_{2-x}SiO_5:Ce_x^{3+}$ phosphors was observed at 300∼400nm in adding $Ce^{3+}$. $Y_{2-x}SiO_5:Ce_x^{3+}$ phosphors showed maximum emission shoulder at 436nm. Maximum CL intensities of $Y_{2-x}SiO_5:Ce_x^{3+}$ were observed in adding 0.025 $Ce^{3+}$ and the phosphor showed x=0.161, y=0.124 in color coordinate of CIE1931.

• Journal of the Korean Ceramic Society
• /
• v.33 no.11
• /
• pp.1209-1216
• /
• 1996

MoSi2-Al2O3 composites were prepared by thermal explosion mode of self-propagating high temperature syn-thesis (SHS) using element powders of MoO3 Mo Si and Al. The combustion products of MoSi2 which have 10, 20, 30 and 40 wt% Al2O3 showed the molten state in the range of Mo to MoO3 6:1-9.5:1, 2:1-8:1, 1:1-5:1, and 1:1-3:1 (molar ratio) respectively. The combustion products which made least seperation the molten phase from the slag phase were in Mo/MoO3=9, 5:1, 8:1, 5:1 and 3:1 (molar ratio) respectively. Particles size of MoSi2 and Al2O3 in the combustion product were decreased as the molar ratio of Mo to MoO3 increase. By XRD analysis only MoSi2 and $\alpha$-Al2O3 peaks were identified in the combusion products, In case of MoSi2 containing 20wt% Al2O3 5.1wt% Al existed into MoSi2 grains and 30.7wt% Si and 7.7wt% Mo existed into Al2O3 grains. The relative density of MoSi2 containing 10, 20, 30 and 40 wt% Al2O3 were 82.7, 85.2, and 81.9% respectively. The fracture strength of MoSi2-Al2O3 composites increased with increasing Al2O3 and that of MoSi2-20wt% Al2O3 composite was 195 MPa.

• Journal of the Korean Ceramic Society
• /
• v.27 no.5
• /
• pp.583-588
• /
• 1990

Glass films in the binary system B2O3-SiO2 and Al2O3-SiO2 were prepared on soda-lime-silica slide glass by the dip-coating technique from TEOS and boric acid or aluminum nitrate. Thickness of the films varying with viscosity and withdrawal speed were measured and effect of composition and firing temperature on the properties such as transmittance and refractive index were investigated. nM2O3.(100-n)SiO2(M=B or Al) films containing up to 20mol% B2O3 and 40mol% Al2O3 were transparent. Maximum transmittance at visible range were obtained for the sample containing 15mol% Ba2O3 and 32.5mol% Al2O3 and heat-treated at 50$0^{\circ}C$, respectively. Refractive index of the film containing 15mol% B2O3 was mininum in the B2O3-SiO2 binary system and minimal refractive index was appeared at the film containing 32.5mol% Al2O3. In IP spectra, addition of B2O3 were increased absorption peak intensity of B-O and Si-O-B bond and addition of Al2O3 were decreased absorption peak intensity of Si-O bond, respectively.

• Applied Chemistry for Engineering
• /
• v.2 no.4
• /
• pp.330-339
• /
• 1991

The acid properties of $V_2O_5-TiO_2/SiO_2$ catalysts and the partial oxidation of o-xylene into phthalic anhydride had been investigated in order to relate the acid property of catalyst to the catalytic activity. $V_2O_5$ had both weak (V=O) and strong (V-O-V) acid sites which gave pyridine desorption peaks at $230^{\circ}C$ and $300^{\circ}C$, respectively, and the amount of weak acid sites at $230^{\circ}C$ decreased with the increase of calcination temperature. On the other hand, the amount of weak acid sites increased considerably by increasing the amount of $TiO_2$ to the $V_2O_5-TiO_2/SiO_5$, and the maximum value was shown at 20 and higher mole % of $TiO_2$ with respect to $SiO_2$. In the oxidation of o-xylene, $V_2O_5-TiO_2/SiO_2$ enhandced more the total conversion and the selectivity to phthalic anhydride than $V_2O_5/SiO_2$, and the higher $TiO_2$ ratio to $V_2O_5$ increased the total conversion but could not change the selectivity to phthalic anhydride. Weak acid sites (V=O) led o-xylene to partial oxidation producing phthalic anhydride by adsorbing o-xylene weakly, while acid sites (V-O-V) led it to total oxidation producing CO and $CO_2$ by adsorbing it strongly.

• Journal of the Korean Ceramic Society
• /
• v.30 no.8
• /
• pp.615-622
• /
• 1993

In order to increase chemical durability of thin films in binary system B2O3-SiO2 and Al2O3-SiO2 on the slide glass by the dip-coating technique from TEOS(Tetraethyl Orthosilicate) and boric acid or aluminum nitrate, phosphoric acid(5~20mol%) was added, respectively. Corrosion of acid and alkali of samples treated with 1N, HCl, NaOH and distilled water at 10$0^{\circ}C$ for 15 minute, were measured IR transmittance and variance of transmittance at visible range. Surface structure of thin film was investigated with SEM and formation of crystal phase according to additiion of phosphoric acid was measrued with XRD. In Al2O3-SiO2 system, change of remarkable characteristic was not obtained at the addition of P2O5 but transmittance of thin film was decreased with addition of P2O5 in B2O3-SiO2 system.

• Journal of the Korean Ceramic Society
• /
• v.34 no.5
• /
• pp.535-543
• /
• 1997

The surface of SiC particles were partially oxidized to produce SiO2 layers on the SiC particles to prepare Al2O3/SiC composite by formation of mullite bonds between the grains of Al2O3 and SiC during sintering at 1$600^{\circ}C$. This process is considered to enable the sintering of Al2O3/SiC composite at lower temperature and also to relieve the stress, produced by thermal expansion mismatch between Al2O3 and SiC. In fact, Al2O3/SiC composite prepared by oxidation of SiC was observed to be more effectively sintered and densified at lower temperature. Maximum density, flexural strength and microhardness were obtained with 5.65 vol% of mullite content in Al2O3/SiC composite.

• Journal of the Korean Ceramic Society
• /
• v.32 no.7
• /
• pp.853-857
• /
• 1995

ZrSiO4 powders were prepared from partially hydrolyzed solution of Si(OC2H5)4 and ZrOCl2.8H2O solution by the sol-gel method and formation rate of ZrSiO4 on the reaction parameter was investigated. In order to prepare homogeneous ZrSiO4 precursor gels, the H2O/Si(OC2H5)4 molar ratio of about 2, the pH of the ZrOCl2.8H2O solution fo about 4 and stirring time of the mixed solutions of about 2 hrs were appropriate. Formation of temperature of ZrSiO4 reduced about 15$0^{\circ}C$ by milling and formation of ZrSiO4 at 1300~135$0^{\circ}C$ showed an accelerative increase through the hedvall effect by silica.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.6
• /
• pp.886-894
• /
• 1990

Sinterbility, microstructure, mechenical and electrical properties of yttriastabilized zirkconiz (92 mole % ZrO2 + 8 mole % Y2O3) doped with 0.5 mole % SiO2 and 0-2.O mole% Al2O3 were studied as a functin of Al2O3 addition. Sintered density increased with increasing Al2O3 addition up to o.5 mole%but decreased up to 1.0mole% Al2O3. Vickers hardness is proportional to sintered density. The specimen added 0.5mole% Al2O3 and 0.5mole% SiO2 exhibited a maximum conductivity. And the specimen added 0.5 mole % Al2O3 and 0.5 mole% SiO2 was measured a maximum electromotive force for a characteristics of oxyzen partial pressure.

• Journal of the Korean Ceramic Society
• /
• v.29 no.6
• /
• pp.431-440
• /
• 1992