• Korean Journal of Materials Research
• /
• v.12 no.8
• /
• pp.624-633
• /
• 2002

In order to improve the hydrogen storage capacity and the activation properties of the hydrogen storage alloys, the rare-earth metal alloy series, MmN $i_{4.5}$M $n_{0.5}$Z $r_{x}$(x=0, 0.025, 0.05, 0.1), are prepared by adding excess Zr in MmN $i_{4.5}$M $n_{0.5}$ alloy. The various parts in hydrogen storage vessel consisted of copper pipes reached the setting temperature within 4~5 minutes after heat addition, which indicated that storage vessel had a good heat conductivity required in application. The performance test on storage vessel filled with rare-earth metal alloys of 1000 gr was also conducted after hydrogen charging for 10 min at $18^{\circ}C$ under 10 atm. It showed that the average capacity of discharged hydrogen volume was found to be for $MmNi_{4.5}$ $Mn_{0.5}$ and $MmNi_{4.5}$ $Mn_{x}$ 0.5/$Zr_{samples}$ indicated that the released amount of hydrogen for this $AB_{5}$ type alloys was more than 92 % of theoretic value, and also it was found that the optimum discharging temperature for obtaining an appropriate pressure of 3 atm was determined to be $V^{\circ}C$ for $MmNi_{4.5}$ $Mn_{0.5}$$Zr_{x}$(x=0, 0.025, 0.05, 0.1) hydrogen storage alloys. The released amount of these hydrogen storage samples was 125 $\ell$ , 122.4 $\ell$ and 108.15 $\ell$/kg for $MmNi_{4.5}$ $Mn_{0.5}$ $Zr_{0.025}$ $MmNi_{4.5}$M $n_{0.5}$Z $r_{0.05}$, and MmN $i_{4.5}$ Mn_0.5$Zr_{0}$, at $70^{\circ}C$ respectively. Amount of the 2nd phases increase with increase on Zr contents in $MmNi_{4.5}$$Mn_{0.5}$ $Zr_{ 0.1}$/ alloy. This phenomenon indicates that$ ZrNi_3$ in $MmNi_{4.5}$ $Mn_{0.5}$ $Zr_{x}$ / phase, which shows the maximum storage capacity and the strong resistance to intrinsic degradation, is considered as a proper alloy for hydrogen storage. As the Zr contents increase, the activation time and the plateau pressure decreases and sloping of the plateau pressure increases.creases.eases.s.

• Korean Journal of Materials Research
• /
• v.12 no.8
• /
• pp.617-623
• /
• 2002

In order to improve the hydrogen storage capacity and the activation properties of the hydrogen storage alloys, the rare-earth metal alloy series, $MmNi_{ 4.5}$$Mn_{0.5}$ $Zr_{x}$ (x=0, 0.025, 0.05, 0.1), are prepared by adding the excess Zr in $MmNi_{4.5}$ $Mn_{0.5}$ / alloy for the strong resistance to intrinsic degradation. The hydrogen storage alloys of rare-earth metal such as $LaNi_{5}$ , and $MmNi_{5}$X and $MmNi_{4.5}$ /$_Mn{0.5}$ alloys which substituted La by misch metal properties were characterized as well. The hydrogen storage alloys were produced by melting each metal mixture in arc melting furnace, and the as-cast alloys were heat-treated at $1100^{\circ}C$ for 10 hr. The major elements of misch metal(Mm) were La, Ce, Pr and Nd with some impurities less than 1wt.% determined by ICP-AES. X-ray diffraction indicated that the structure for these samples was a single phase of hexagonal with $CaCu^{5}$ type. As the Zr contents increases, the activation time and the plateau pressure decrease and sloping of the plateau pressure increase. Amount of the 2nd phases increases with increase in Zr contents in $MmNi_{ 4.5}$$Mn_{0.5}$ $Zr_{0.1}$ alloy, This phenomenon indicated that $ZrNi_3$ in this phase, which shows the maximum storage capacity and the strong resistance to intrinsic degradation, is considered as a proper alloy for hydrogen storage..