• Journal of the Korean Ceramic Society
• /
• v.39 no.3
• /
• pp.315-320
• /
• 2002

Treatment effects of dilute hydrofluoric acid (6 wt% HF) on the surface properties of $Al(OH)_3$ were investigated at the molar ratio of F/Al(fluoride/aluminum)=0.15. Temperature and pH variations in the reaction system were recorded to analyze reaction mechanism between $Al(OH)_3$ and aqueous Hf. The reaction of HF to the surface of $Al(OH)_3$ accompanied with a quantity of heat evolution, resulting in increasing temperature of a reactionsystem. And also the reaction was proceeded as transitional state which metastable ${\alpha}-form\;AlF_3{\cdot}3H_2O$ was transferred to insoluble ${\beta}$-form. The resulting ${\beta}-form\;AlF_3{\cdot}3H_2O$ formed by a surface treatment was identified by FT-IR and X-ray diffractormetry. The formation of ${\beta}$-form aluminum fluoride hydrates with diameter less than $1{\mu}m$ on the surface of $Al(OH)_3$ could be visulaized by SEM imgae, making up a coating layer as precipitate-like. The surface whiteness of $Al(OH)_3$ treated with aqueous HF was furthermore increased approximately 6.6% due to the formation of surface hydrates.

• Proceedings of the KIEE Conference
• /
• 2000.11c
• /
• pp.479-481
• /
• 2000

The effect of $Al_{2}O_{3}+Y_{2}O_{3}$ additives on fracture toughness of $\beta-SiC-TiB_2$ composites by hot-pressed sintering were investigated. The f$\beta-SiC-TiB_2$ ceramic composites were hot-presse sintered and annealed by adding 16, 20, 24wt% $Al_{2}O_{3}+Y_{2}O_{3}$(6 : 4wt%) powder as a liquid forming additives at low temperature($1800^{\circ}C$) for 4h. In this microstructures, the relative density is over 95.88% of the theoretical density and the porosity increased with increasing $Al_{2}O_{3}+Y_{2}O_{3}$ contents because of the increasing tendency of pore formation. The fracture toughness showed the highest of $5.88MPa{\cdot}m^{1/2}$ for composites added with 20wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives at room temperature. The electrical resistivity showed the lowest of $5.22{\times}10^{-4}\Omega{\cdot}cm$ for composite added with 20wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives at room temperature and is all positive temperature coefficient resistance (PTCR) against temperature up to $700^{\circ}C$.