• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 추계학술대회 논문집 Vol.16
• /
• pp.267-270
• /
• 2003

We have studied the interfacial diffusion phenomena and the role of ${\alpha}-Al_2O_3$ buffer layer as a diffusion barrier in the $Ba-ferrite/SiO_2$ magnetic thin films for high-density recording media. In the interface of amorphous Ba-ferrite ($1900-{\AA}-thick)/SiO_2$ thin film during annealing, the interfacial diffusion started to occur at ${\sim}700^{\circ}C$. As the annealing temperature increased up to $800^{\circ}C$, the interfacial diffusion abruptly proceeded resulting in the high interface roughness and the deterioration of the magnetic properties. In order to control the interfacial diffusion at the high temperature, we introduced ${\alpha}-Al_2O_3$ buffer layer ($110-{\AA}-thick$) in the interface of $Ba-ferrite/SiO_2$ thin film. During the annealing of $Ba-ferrite/{\alpha}-Al_2O_3/SiO_2$ thin film even at ${\sim}800^{\circ}C$, the interface was very smooth. The smooth interface of the film was also clearly shown by the cross-sectional FESEM. The magnetic properties, such as saturation magnetization 3nd intrinsic coercivity, were also enhanced, due to the inhibition of interfacial diffusion by the ${\alpha}-Al_2O_3$ buffer layer. Our study suggests that the ${\alpha}-Al_2O_3$ buffer layer act as a useful interfacial diffusion barrier in the $Ba-ferrite/SiO_2$ thin films.

• 한국자기학회지
• /
• 제16권6호
• /
• pp.283-286
• /
• 2006

고밀도 자기기록용 Ba-페라이트/$SiO_{2}$ 자성박막에서 계면확산 장벽으로써 ${\alpha}-Al_{2}O_{3}$ 버퍼층의 역할을 연구하였다. 열처리동안 $1900{\AA}$의 두께를 가진 비정질 Ba-페라이트/$SiO_{2}$ 박막에서 계면확산은 약 $700^{\circ}C$에서 일어나기 시작하였다. 열처리온도를 $800^{\circ}C$까지 증가시켰을 때, 계면확산은 자기특성을 저하시킬 정도로 급격히 진행되었다. 고온에서의 계면확산을 억제하기 위하여, $110{\AA}$ 두께의 ${\alpha}-Al_{2}O_{3}$ 버퍼층을 Ba-페라이트/$SiO_{2}$ 박막의 계면에 증착하여 사용하였다. Ba-페라이트/${\alpha}-Al_{2}O_{3}/SiO_{2}$ 박막에서는 $800^{\circ}C$의 고온까지 열처리하여도 계면확산이 심각하게 일어나지는 않았다. ${\alpha}-Al_{2}O_{3}$ 버퍼층에 의하여 계면확산이 억제되기 때문에 Ba-페라이트 자성박막의 포화자속밀도와 보자력이 향상되었다. 따라서 Ba-페라이트/$SiO_{2}$ 박막의 계면에서 ${\alpha}-Al_{2}O_{3}$ 버퍼층은 $SiO_{2}$ 기판 성분의 계면확산 장벽으로 사용될 수 있다.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 1999년도 High Temperature Superconductivity Vol.IX
• /
• pp.58-62
• /
• 1999

We fabricated a new hairpin type HTS 2-pole microstrip Bandpass filter to operate at 5.8GHz. The fabrication method was pulsed laser deposition and YBCO films were deposited on ${\alpha}$-A1$_2O_3$ substrates with a CeO$_2$ thin layer as a buffer layer. We developed a new style hairpin type filter by using interdigitide innerpole. Compared to the saute size regular hairpin type filters, our filter had a lower center frequency, bandwidth and loss by an amount of 14.5%, 29.6%, 0.5488dB, respectively. The size of the filters were 13.7${\times}$3.3mm. We did simulations on the several types of band pass filters by using HFSS and serenade. We measured growth rate and Tc of YBCO films grown on CeO$_2$/ ${\alpha}$-A1$_2O_3$ substrates which were rotated while growing films.

• 센서학회지
• /
• 제8권2호
• /
• pp.195-201
• /
• 1999

$Al_2O_3$ (알루미나 및 R-면 사파이어)기판 위에 c-축 $YBa_2Cu_3O_{7-{\delta}}$ (YBCO) 박막을 펄스레이저 증착법을 이용하여 성장하였다. 완충층으로 사용하기 위해 $Al_2O_3$ 기판 위에 증착한 $CeO_2$ 박막의 결정성은 기판온도에 많은 영향을 받았다. $CeO_2$ 박막은 $800^{\circ}C$의 기판온도에서 $\alpha$-축방향으로 잘 성장하였으며, $CeO_2$ 완충층의 두께에 따라 YBCO/$CeO_2/Al_2O_3$ 박막의 초전도 특성은 큰 변화를 나타내었다. 알루미나 기판 위에서 $CeO_2$ 완충층의 두께는 약 $1200\;{\AA}$이하, 사파이어 기판의 경우 $100{\sim}1000\;{\AA}$ 범위에서 YBCO 박막은 양호한 초전도 특성을 나타내었으나, 그 보다 두껍게 성장시킬 경우 초전도 특성이 급격하게 나빠졌다. 알루미나 기판 위에 성장된 YBCO 박막의 임계온도는 83 K였으며, R-면 사파이어 기판 위에 성장된 YBCO 박막의 임계온도는 ${\geq}89.5\;K$였고, 임계전류밀도는 77K에서 $3{\times}10^6\;A/cm^2$로 나타났다.