• 한국자기학회지
• /
• 제12권2호
• /
• pp.64-67
• /
• 2002

속박층 (pinning layer) IrMn를 사용한 Ta/NiFe/IrMn/CoFe/Cu/CoFe/NiFe/Ta 구조의 스핀밸브 박막 (SV; spin valve)을 산화층이 코팅된 Si(111) 기판에 dc 마그네트론 스퍼터링 방법으로 상온에서 제작하였다. 이 SV에 대하여 교환결합자기장 (H$_{ex}$; exchange coupling field), 자기저항 (MR; magnetoresistance)비 및 보자력 (H$_{c}$ coercivity)의 열처리 순환수와 온도 의존성을 조사하였다. 증착조건과 후열처리 조건을 최적화 함으로써 MR비 3.6%, 피속박층의 H$_{ex}$ 11800 Oe을 얻었다. H$_{ex}$는 열처리 순환횟수가 2 이후에 일정한 값을 유지하여 열적으로 안정성을 갖는 것을 확인하였다. H$_{ex}$는 24$0^{\circ}C$ 까지는 600 Oe를 유지하다가 점점 감소하여 27$0^{\circ}C$에 0이 되었다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.257.1-257.1
• /
• 2014

We investigated characteristics of ITO/Ag-Pd-Cu (APC)/ITO multilayer electrodes prepared by direct current magnetron sputtering for use as an anode in organic solar cells (OSCs). To optimize electrical properties of ITO/APC/ITO multilayer, we fabricated the ITO/APC/ITO multilayer at a fixed ITO thickness of 30 nm as a function of APC thickness. Compare to the surface of Ag layer on ITO, the APC had a smooth surface morphology. At optimized APC thickness of 12 nm, the ITO/APC/ITO multilayer exhibited a sheet resistance of $6{\Omega}/square$ and optical transmittance of 84.15% at a wavelength of 550 nm which is comparable to conventional ITO/Ag/ITO multilayer. However, the APC-based ITO multilayer showed a higher average transmittance in a visible region than the Ag-based ITO multilayer. The higher average transmittance of ITO/APC/ITO multilayer indicated the multilayer is suitable anode for organic solar cells with P3HT:PCBM active layer. OSCs fabricated on the optimized ITO/ACP/ITO multilayer exhibited a better performance with a fill factor of 64.815%, a short circuit current of $8.107mA/cm^2$, an open circuit voltage of 0.59 V, and power conversion efficiency (3.101%) than OSC with ITO/Ag/ITO multilayer (2.8%).

• Progress in Superconductivity
• /
• 제8권1호
• /
• pp.59-64
• /
• 2006

High $J_c\;YBa_2Cu_3O_x$ superconducting films were fabricated by MOD method using fluorine-free dichloroacetic acid(DCA) as chelating solvent for preparing precursor solution. Coating solutions were prepared by dissolving Y-, Ba- and Cu-acetates in DCA solvent followed by drying in rota vapor to obtain the blue gel that is diluted in methanol and 2-methoxyethanol for adjusting the cation concentration. DCA-MOD precursor solution was coated on a single crystal(001) $LaAlO_3(LAO)$ substrate by a dip coating method with a speed of 25 mm/min. Coated films were calcined at lower temperature up to $500^{\circ}C$ in flowing oxygen atmosphere with a 7.2% humidity. Conversion heat treatment was performed at various temperatures of $780{\sim}810^{\circ}C$ for 2 h in flowing Ar gas containing 1000 ppm oxygen with a humidity of 9.45%. SEM observations showed that films have very dense microstructures for the films prepared at the temperature higher than $800^{\circ}C$ regardless of diluting solvent; methanol or 2-methoxyethanol. X-ray diffraction analysis showed that YBCO grains grew with a (001) preferred orientation. A High critical current density($J_c$) of 1.28 $MA/cm^2$(@77 K and self-field) was obtained id. the YBCO film prepared using 2-methoxyethanol as a solvent.

• 마이크로전자및패키징학회지
• /
• 제4권1호
• /
• pp.19-30
• /
• 1997

고분자 Polyimide (PI) film 표면을 반응성 가스 분위기에서 1KeV의 에너지를 가지 는 여러 종류의 이온빔으로 조사하여 표면을 개질하였다. PI표면의 친수성과 표면에너지를 측정하기 위해 접촉각 측정기를 사용하였으며 개질 된 표면의 화학적 변화를 측정하기 위해 X-ray photoelectron spectroscopy (XPS)를 사용하였다. 표면 개질을 위한 이온조사량은 5 $\times$1014 -1$\times$1017 ions/cm2이며 반응가스는 0-8scm까지 변화시켰다. 아르곤 이온빔으로 표면 개질시에는 67。에서 40。까지 감소하였고 표면에너지는 46 dyne/cm에서 64dyne/cm까지 증가하였다. 산소를 6sccm 주입하면서 산소 이온빔으로 표면 개질시 물과의 접촉각은 67。 에서 최대 12。까지 감소하였으며 표면에너지는 46dyne/cm에서 72dyne/cm까지 증가하였고 이때의 이온조사량은 5$\times$1014 -1$\times$1017 ions/cm2 이였다. 여러 종류의 반응성 가스와 이온을 사용하여 개질하여 본 결과 산소분위기에서 산소 이온을 이용하여 개질 하였을 때 접촉각이 8。인 표면을 얻을수 있었다, 산소분위기에서 아르곤 이온빔으로 1$\times$1017 ions/cm2 의 이온 조사량으로 개질 된 Pi 시료를 대기 중에 보관하였을 때에는 110시간 후 65。로 증가하였고 물속에서 보관하였을 때에는 46。로 증가하였다. 그러나 산소 이온빔에 산소분위기에서 개 질 된 시료의 경우 물속에 보관할 경우 접촉강의 증가없이 일정한 값을 나타내었다. 이온조 사로 개질된 시료의 화학적 변화를 확인하기 위하여 XPS 사용하였다. 표면 개질 전의 PI 시료와 산소 분위기에서 1$\times$1017 ions/cm2의 아르곤 이온빔으로 개질한 XPS peak 결과로 보아 Cls의 spectra를 보면 C-C, C-N 그리고 C=O의 결합들은 intensity가 감소하였고 C-O 의 intensity는 증가하였다. Nls peak로 보아 imide N 성분은 이온빔의 조사로 인하여 감소 하였고 C-O의 intensity는 증가하였다. Nls peakk로 보아 imide N성분은 이온빔의조사로 감소하였고 Ols peak로 보아 C-O는 증가하였고 C=O는 약간의 감소가 나타났다. 또한 이온 보조 반응법을 이용하여 처리한 시료의 경우 접착력이 증가하는데 이는 주로 C-O 결합의 산소와 Cu와의 상호작요에 의한 것임을 알수 있었다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2013년도 제45회 하계 정기학술대회 초록집
• /
• pp.309.2-309.2
• /
• 2013

Cu(In,Ga)Se2 (CIGS) 박막 태양전지는 일반적으로 Na을 함유하고 있는 소다회유리를 기판으로 사용하여 제작되며, 높은 광전 변환 효율로 인해 많은 연구가 이루어지고 있다. 특히 제조 비용 절감과 양산성 향상을 위해 현재 유연 기판 CIGS 박막 태양전지에 대한 연구가 활발히 이루어지고 있으며, 폴리이미드 기판에서 20.4%의 최고 효율이 보고되었다. 유연 기판은 유리 기판 대비 무게가 가볍기 때문에 유리 기판 태양전지보다 활용도가 높으며, 우주용으로 사용할 경우 단위 무게 당 발생되는 전력이 높은 장점이 있다. 본 연구에서는 폴리이미드 기판을 이용하여 유연 CIGS 박막 태양전지를 제작하였다. 후면 전극 Mo은 DC sputtering으로 증착하였으며, Mo의 증착 압력에 따라 폴리이미드 기판의 잔류 응력과 전기적 특성을 분석하여 증착 압력을 결정하였다. 광흡수층인 CIGS는 다단계 동시 증발 법으로 증착하였으며, 2nd stage 공정온도는 유리 기판 대비 저온인 $475^{\circ}C$로 공정을 진행하였다. 저온공정인 $475^{\circ}C$ 공정에서는 Ga의 함량이 높아질수록 성능이 감소하였으며, Na 공급을 통해 Voc와 FF가 향상되어 성능이 향상됨을 알 수 있었다. 버퍼층 CdS는 습식 공정인 CBD법으로 증착하였으며, 공정변수인 thiourea의 농도와 CdS 박막의 두께 변화를 통해 폴리이미드 기판 CIGS 박막 태양전지에서 CdS 버퍼층의 최적의 조건을 도출하였다. 최종적으로 제작된 폴리이미드 기판 유연 CIGS 박막 태양전지는 반사 방지막 없이 개방전압 0.511V, 단락전류밀도 32.31mA/cm2, 충실도 64.50%, 변환효율 10.65%를 나타내었다.

• 소성∙가공
• /
• 제30권1호
• /
• pp.5-15
• /
• 2021

The effects of heat treatments (T6 and T73) on the microstructure, mechanical properties, and high cycle fatigue behavior of modified AA7075 alloys were investigated. A modified 7075 alloy was manufactured using modified-Mg (Mg-Al2Ca) instead of the conventional element Mg. Based on the microstructure, the average grain size was 4.5 ㎛ (T6) and 5.2 ㎛ (T73). Regardless of heat treatment, the modified AA7075 alloys consisted of Al matrix containing homogeneously distributed Al2CuMg and MgZn2 phases with reduced Fe-intermetallic compound. Room temperature tensile tests showed that the properties of modified 7075-T6 (Y.S.: 622MPa, T.S: 675MPa, elongation: 15.4%) were superior to those of T73 alloy (Y.S.: 492MPa, T.S: 548MPa, elongation: 12.8%). Experimental data show that the fatigue life of T6 was 400 MPa, about 64% of its yield strength. However, the fatigue life of T73 alloy was 330 MPa and 67%. Irrespective of the stress level, all crack initiation points were located on the specimen surface, and no inclusions acting as stress concentrators were seen. Superior mechanical properties and high cycle fatigue behavior of modified AA7075-T6 alloy are attributed to the fine grains and homogeneous distribution of small second phases such as MgZn2 and Al2CuMg, in addition to reduced Fe-intermetallic compounds.

• Archives of Metallurgy and Materials
• /
• 제64권2호
• /
• pp.617-622
• /
• 2019

This study investigated the effect of T6 heat treatment on the microstructure and scratch wear behavior of hypoeutectic Al-12wt.%Si alloy manufactured by extrusion. Microstructural observation identified spherical eutectic Si phases before and after the heat treatment of alloys (F, T6). Phase analysis confirmed Al matrix and Si phase as well as Al₂Cu and Al₃Ni, Mg₂Si in both alloys. In particular, Al₂Cu was finer and more evenly distributed in T6 alloy. This resulted in Vickers hardness of T6 alloy that was 2.3 times greater compared to F alloy. The scratch wear test was conducted using constant load scratch test (CLST) mode and multi-pass scratch test (MPST) mode. The scratch coefficient and worn out volume obtained by such were used to evaluate wear properties before and after heat treatment. In the case of T6 alloy, its scratch coefficient was lower than F alloy in all load ranges. After 15 repeated tests to measure worn out volume, F alloy and T6 alloy measured 1.2×10^-1 mm³ and 7.8×10^-2 mm³, respectively. In other words, the wear resistance of T6 alloy were confirmed to be better than those of F alloy. In addition, this study attempted to identify the microstructural factors that contribute to the better scratch wear resistance of T6 alloy and wear mechanism from surface and cross-section observations after the wear tests.

• 한국지구과학회지
• /
• 제27권1호
• /
• pp.49-60
• /
• 2006

본 연구는 나주지역 하상퇴적물에 대한 지구화학적 특성 연구이다. 이를 위해 1차 수계를 대상으로 139개의 하상퇴적물 시료를 채취하였다. 채취된 시료는 실험실에서 자연 건조시켰으며, XRF, ICP-AES, NAA를 이용하여 화학분석을 실시하였다. 기반암에 따른 지구화학적 특성을 알아보기 위하여, 화강암질편마암 지역, 편암류 지역, 화강암류 지역, 사질암 지역, 응회암 지역, 안산암 지역, 유문암 지역으로 분류하였다. 나주지역 하상퇴적물의 지질집단별 주성분원소 평균함량은 $SiO_2\;58.37{\sim}66.06wt.%,\;Al_2O_3\;13.98{\sim}18.41wt.%,\;Fe_2O_3\;4.09{\sim}6.10wt.%,\;CaO\;0.54{\sim}1.33wt.%,\;MgO\;0.86{\sim}1.34wt.%,\;K_2O\;2.38{\sim}4.01wt.%,\;Na_2O\;0.90{\sim}1.32wt.%,\;TiO_2\;0.82{\sim}1.03wt.%,\;MnO\;0.09{\sim}0.15wt.%,\;P_2O_5\;0.11{\sim}0.18wt.%$이다. 주성분원소의 평균함량 비교에서 $Al_2O_3$와 $K_2O$는 화강암질편마암 지역에서, $Fe_2O_3,\;CaO,\;P_2O_5$는 응회암 지역에서, MgO와 $TiO_2$는 안산암 지역에서, $Na_2O$는 유문암 지역에서 높고, $SiO_2$와 MnO 함량은 사질암 지역에서 약간 높다. 미량성분 및 희토류원소의 지질집단별 평균함량은 $Ba\;1278{\sim}1469ppm,\;Be\;1.1{\sim}1.5ppm,\;Cu\;18{\sim}25ppm,\;Nb\;25{\sim}37ppm,\;Ni\;16{\sim}25ppm,\;Pb\;21{\sim}28ppm,\;Sr\;83{\sim}155ppm,\;V\;64{\sim}98ppm,\;Zr\;83{\sim}146ppm,\;Li\;32{\sim}45ppm,\;Co\;7.2{\sim}12.7ppm,\;Cr\;37{\sim}76ppm,\;Cs\;4.8{\sim}9.1ppm,\;Hf\;7.5{\sim}25ppm,\;Rb\;88{\sim}178ppm,\;Sc\;7.7{\sim}12.6ppm,\;Zn\;83{\sim}143ppm,\;Pa\;11.3{\sim}37ppm,\;Ce\;69{\sim}206ppm,\;Eu\;1.1{\sim}1.5ppm,\;Yb\;1.8{\sim}4.4ppm$이다. Pb, Li, Cs, Hf, Rb, Sb, Pa, Ce, Eu, Yb 평균함량은 화강암질편마암 지역에서, Ba, Co, Cr 평균함량은 편암류 지역에서, Nb, Ni, Zr 평균함량은 사질암 지역에서, Sr 평균함량은 응회암 지역에서 높고, Be, Cu, V, Sc, Zn 평균함량은 안산암 지역에서 다른 지질집단에서 보다 높다.

• 한국식품저장유통학회지
• /
• 제21권5호
• /
• pp.702-709
• /
• 2014

시판 건조김의 일반성분, 아미노산, 지방산, 구성당 및 무기질 함량을 분석한 결과는 다음과 같다. 수분 함량은 5.67~7.43%, 조회분 함량은 8.01~8.95%, 조지방 함량은 1.54~2.25%, 조단백질 함량은 37.77~39.98% 및 탄수화물 함량은 43.83~46.24%으로 산지에 따라 유의적인 차이를 나타냈다. 구성아미노산 함량은 건조김 100 g 당 완도가 25,982.15 mg, 부산이 23,847.35 mg, 고흥이 21,499.83 mg, 서천이 20,190.80 mg의 순으로, 필수아미노산은 건조김 100 g 당 완도가 9048.28 mg, 부산이 8003.11 mg, 고흥이 7178.65 mg, 서천이 7156.80 mg의 순으로, 유리아미노산 함량은 건조김 100 g 당 완도가 4,545.44 mg, 부산이 3,526.64 mg, 고흥이 3,103.19 mg, 서천이 2,871.62 mg의 순으로 산지에 따라 유의적 차이를 나타냈다. 주요 지방산 조성은 20:5n3가 64.50~70.06%, 16:0가 8.79~10.29%, 23:0가 3.15~7.36%, 22:1n9가 1.86~3.09%으로 산지에 따라 유의적 차이를 보였고 전체 지방산의 78.30~90.80%를 차지하였다. 구성당은 건조김 100 g 당 galactose가 3,678.84~4,052.52 mg, fructose가 2,112.30~2,473.86 mg, mannose가 1,103.74~1,648.39 mg, glucose가 361.67~590.21 mg의 순으로 산지에 따라 유의적 차이를 나타냈다. 무기질 함량은 완도 및 부산 김이 K, Na, Mg, Ca, Fe, Zn, Mn, Cu 순으로, 고흥 및 서천의 김은 K, Na, Ca, Mg, Fe, Zn, Mn, Cu 순으로 산지에 따라 유의적 차이를 보였다.

• 한국자기학회지
• /
• 제7권1호
• /
• pp.13-18
• /
• 1997

기본 조성 N $i_{0.18}$Z $n_{0.68}$C $u_{0.14}$F $e_{2}$ $O_{4}$와 N $i_{0.14}$Z $n_{0.64}$C $u_{0.22}$F $e_{2}$ $O_{4}$ 및 N $i_{0.24}$Z $n_{0.64}$C $u_{0.12}$F $e_{2}$ $O_{4}$에 입계의 고저항층을 형성하고 소결을 촉진시키기 위해서 0.1 mol %의 Ca $Co_{3}$와 입자의 성장을 촉진시키고 높은 투자율을 얻을 목적으로 $V_{2}$ $O_{5}$를 0.04 mol% 첨가하였다. 이들 원료들을 혼합한 후 950 .deg. C에서 3시간 하소 과정을 거친후 ball mill해서 toroid 시편을 만들고 1030 .deg. C, 1050 .deg. C 및 1070 .deg. C 에서 2시간 동안 공기중에서 소결 시켰다. Raw material의 조성비 변화 및 소결 온도 변화에 따른 여러 가지 물리적 특성들을 조사하였다. X-선 회절 분석 결과 이들 시편들이 spinel 구조를 이루고 있음을 확인하였고 금속현미경으로 측정한 결정 입자의 크기는 6 .mu. m ~ 16 .mu. m 이었다. 초투자율, 자기 유도는 소결 온도가 1030 .deg. C에서 1050 .deg. C로 증가함에 따라 증가하였고 Q factor와 보자력은 감소하였다. 보자력과 큐리온도는 각각 0.17 Oe 및 220 .deg. C 근처로 모든 시편들에서 거의 비슷하였다. 본 시편의 사용 주파수 범위는 0.4 ~ 20 MHz로 확인되었으며, 소결 온도 1050 .deg.C와 기본 조성 N $i_{0.14}$Z $n_{0.64}$C $u_{0.22}$F $e_{2}$ $O_{4}$ 에서 다른 사람들 보다 더욱 더 우수한 자기유도값(B, $B_{m}$ )을 얻을 수 있었다.