• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2002년도 춘계학술발표대회 논문집
• /
• pp.139-142
• /
• 2002

Recently, GFRP is well known as a structural material for the radome of aircraft. In this paper, we have observed the reflectivity of electromagnetic waves on GFRP reinforced with $\textrm{Al}_2\textrm{O}_3$ woven fabric. The result of the experiment has revealed that the reflectivity of $\textrm{Al}_2\textrm{O}_3$/GFRP composites is remarkably reduced compared with that of GFRP. And it also shows that the electromagnetic wave reflections are greatly influenced by the number of $\textrm{Al}_2\textrm{O}_3$ plies in a specific frequency band. These results are expected to be utilized for the technique of manufacturing a low-reflectivity composite structure.

• 한국재료학회지
• /
• 제9권1호
• /
• pp.3-7
• /
• 1999

The change of phosphorescent property with chemical modification and co-doping of Nd as an auxiliary activator in CaAl$_2$$O_4$: Eu\ulcorner, Nd\ulcorner phosphor, employing Nd\ulcornerion(0.6%) and an co-activator maintained its afterglow for 4.5 hours. And also the initial persistent brightness and phosphorescent property were further improved both by substituting Al by B atoms and incorporation of Nd\ulcorner ion. It was found that the persistent time was 30 hours for&Ca(Al_{0.97}\;B_{0.03}) $_2$$O_4$:EU\ulcorner(0.3%), Nd\ulcorner(0.6%) phosphor.

• 한국재료학회지
• /
• 제9권1호
• /
• pp.73-80
• /
• 1999

The effect of alloy compositions of the bond coating on the plasma sprayed-thermal barrier coatings was investigated. The performance of the coating composed of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ and Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$was evaluated by isothermal and thermal cyclic test in an ambient atmosphere at 115$0^{\circ}C$. The failure of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ coatings was occurred at the bond coating/ceramic coating interface while Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ coating was failed at the substrate/bond coating interface after thermal cyclic test. The lifetime of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$coatings was longer than Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$coating. The oxidation rate of the NiCrAl bond coating examined by TGA was lower than CoNiCrAlY bond coatings. In summary, these results suggest that Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$system as thermal barrier coating be not suitable considering the durability of the coating layer for high temperature oxidation and thermal stress.

• 한국재료학회지
• /
• 제9권4호
• /
• pp.345-348
• /
• 1999

The properties of Fe ions in the $ CdFe_2$$O_4$ and $CdFeAlO_4$ were investigated using the Mossbauer spectroscopy, in the temperature range from 300K to 900K. The calculated Debye temperature, recoil free fraction, mean square displacement and velocity are, 476.5K, 0.835, 3.39$\times$10\ulcorner$\textrm{cm}^2$, and 1.11$\times$10\ulcorner$\textrm{cm}^2$sec$^2$for Fe ions in the $CdFe_2$$O_4$ and 369.0K, 0.741, 5.65$\times$10\ulcorner$\textrm{cm}^2$ and 1.33$\times$10\ulcorner$\textrm{cm}^2$/$sec^2$in the $CeFeAlO_4$. The difference of the properties in the two samples were explained by the variation of the Fe\ulcorner-O\ulcorner bonding length with the substituted Al ions.

• The Korean Journal of Ceramics
• /
• 제1권3호
• /
• pp.147-151
• /
• 1995

Porous composite of $Al_2O_3$ and AIN based mullite and SiC can be prepared by alumium reaction synthesis and atmosphere controllied sintering in order to improve the durability of a gas filter body. The porous $Al_2O_3$-AIN-mullite, which has a strength of 168 kg/$\textrm{cm}^2$ and porosity of 51.59%, could be obtained by stmospheric firing at $1600^{\circ}C$ and the porous $Al_2O_3$-AIN-SiC with a porosity of 33% and strength of 977 kg/$\textrm{cm}^2$, could also be prepared. The average pore size has been changed from 0.2$\mu\textrm{m}$ in a reduction atmosphere and to 2$\mu\textrm{m}$ in an air atmosphere, respectively.

• 한국재료학회지
• /
• 제9권4호
• /
• pp.428-433
• /
• 1999

본 연구는 $0.1~1.2\mu\textrm{m}$ 압도분포를 갖는 미세 $Al_2O_3$를 이용하여 플라츠마 용사한 후 상업용 용사분말(Metco 105)과 용사층의 특성을 비교하였다. 미세조직은 미세 $Al_2O_3$층이 상업용분말보다 더 치밀하였고 용샤층의 평균 표면조도 $(R_a)$는 미세 $Al_2O_3$의 경우에 $5.3\mu\textrm{m}$로 상업용 분말 $(R_a=8.2\mu\textrm{m})$ 보다 작은 값을 보였으며, 용사층 평균 splat 두께는 $1.4\mu\textrm{m}$ 였다. 또한 용샤층에는 많은 양의 부분 용융입자가 관찰되었다. XRD분석결과 두 분말 모두 용사층을 이루는 주된 상은 $\gamma-Al_2O_3$이였으며 $\alpha-Al_2O_3$도 관찰되었다. 용사층에 존재하는 $\alpha-Al_2O_3$의 분율은 미세 $Al_2O_3$층의 경우 8.39%. 상업용 $Al_2O_3$의 경우 13.79%이였다. 미세 경도 값은 두 분말에서 큰 차이를 보이지는 않았으나, 미세 $Al_2O_3$의 경우 큰 경도값 편차를 보였으며 따라서 미세 $Al_2O_3$층의 splat의 접합강도는 상업용 $Al_2O_3$보다 상대적으로 낮을 것으로 생각된다.

• 한국재료학회지
• /
• 제5권6호
• /
• pp.644-649
• /
• 1995

$UO_2$-6wt%Gd$_2$O$_3$가연성 독물질 소결체에 미량첨가한 Al 화합물(Al(OH)$_3$, ADS(aluminium disterate), Al(OH)$_3$+ADS)이 소결성 및 미세조직에 미치는 영향을 고찰하고자 하였다. 이를 위하여 Al이 첨가된 $UO_2$-6wt%Gd$_2$O$_3$압분체를 1$700^{\circ}C$, 수소 분위기에서 4시간동안 소결한 후 특성시험을 수행하였다 Al을 첨가한 $UO_2$-6wt%Gd$_2$O$_3$의 소결밀도는 94% T.D.이상이였고, ADS를 이용한 Al 첨가가 개기공도 감소에 상대적으로 크게 기여하였다. 또한 Al을 첨가하면 10$\mu\textrm{m}$ 이상의 큰 기공과 1$\mu\textrm{m}$ 이하의 작은 기공은 많이 줄어들었고 첨가된 Al 화합물의 종류와는 무관하게 평균 기공크기는 2-3$\mu\textrm{m}$였다. 그리고 Al을 첨가하지 않은 소결체의 결정립은 이중 결정립 형태를 갖는 반면에 Al을 첨가하면 결정립은 균일하였다. 특히, ADS를 첨가한 소결체의 평균 결정립 크기는 4.6$\mu\textrm{m}$로 가장크게 증가하였다.

• 한국재료학회지
• /
• 제9권10호
• /
• pp.1025-1031
• /
• 1999

6종류의 조성을 가진 TiAl계 합금, 즉 Ti-(42, 44)Al-2Nb-4V, Ti-(42, 44)Al-4Nb-2V 및 Ti-(42, 44)Al-4Nb-2Cr을 아크용해법으로 제조한 후, 이들의 산화성질을 조사하였다. 700, 800 및 $900^{\circ}C$의 대기 중, 50시간동안의 등온 및 반복 산화실험으로부터, 산화저항은 Ti-(42, 44)Al-2Nb-4V, Ti-(42, 44)Al-4Nb-2V 및 Ti-(42, 44)Al-4Nb-2Cr의 순으로 증가함을 알 수 있었다. 내산화성에서 V은 해로운 원소이고 Cr은 유익한 원소이었다. 산화 중 모든 모재 구성원서는 외부확산하였고 분위기중으로 부터의 산소는 내부확산하는 상호확산이 관찰되었으며, 생성되는 산화물은 최외각 $\textrm{TiO}_2$층, 상부 ($\textrm{TiO}_2+\textrm{Al}_2\textrm{O}_3$) 혼합층 및 하부 $\textrm{TiO}_2$-잉여층으로 이루어진 3층 산화물구조로 구성되어 있었다.

• 한국세라믹학회지
• /
• 제25권3호
• /
• pp.201-206
• /
• 1988

Mo 입자의 첨가가 Al_2O_3$ 세라믹스의 미세구조와 기계적 성질에 미치는 영향을 알아보기 위하여 평균입경이 2-micron인 Mo와 6-micron인 Mo를 Al_2O_3$에 각 분산시켜 1$600^{\circ}C$, $H_2$ 분위기에서 5시간 소결하였다. Mo는 Al_2O_3$의 입자성장을 억제시켰으며 Mo의 입자가 작을 때 그 효과는 크게 나타났다. 2-micron Mo를 분산한 경우 꺽임강도와 파괴인성은 크게 증가하여하였으며, 6-micron Mo를 분산한 경우 강도는 증가하지 않았으나 파괴인성은 다소 증가하였다. Al_2O_3$-Mo계의 인성증진기구는 균열편향에 의한 파단면의 증가와 미세균열에 의한 균열전파에너지의 분산에 의한 것으로 보인다.

• 한국재료학회지
• /
• 제6권10호
• /
• pp.1043.1-1048
• /
• 1996

알루미나 매트릭스 복합재료를 AIZnMg(7075)-합금의 직접적인 용융산화를 통하여 제조하였다. 충전재료는 17$\mu\textrm{m}$ 크기의 모서리가 둥근 연마재용 SiC 입자를 사용하였다. 산화촉진재 SiO2를 사용한 경우와 사용하지 않은 경우를 비교하였다. 매트릭스 형성 매카니즘과 반응거동을 온도와 SiO2사용량을 중심으로 연구하였으며, 얻어진 AI2O3/SiC/금속 복합재료의 미세구조를 관찰하였다.