• Journal of Korea Foundry Society
• /
• v.15 no.6
• /
• pp.596-603
• /
• 1995

${\gamma}-TiAl$ 금속간화합물에 크롬과 질소첨가의 영향을 관찰하기 위하여 첨가량에 따른 열처리 전후의 미세조직과 기계적 성질을 비교 분석하였다. 그 결과 질소첨가량이 증가할수록 결정립이 미세화되고 항복강도가 증가되었으며 크롬과 질소의 동시첨가의 경우가 이들의 효과가 현저하였다. 또한 이들 원소의 첨가로 $Ti_2AlN$이 제3상으로 생성되어 열처리시 ${\alpha}_2/{\gamma}$층상조직의 안정화를 보였으며 첨가량을 다량으로 하였을 때 결정립의 크기가 급격히 감소함에도 상온연성이 감소되는 것은 $Ti_2AlN$의 크기에 기인한 것으로 판단된다. 적정량의 크롬과 질소를 동시첨가하여 열처리시 상온연성 및 항복강도가 향상되었다.

• Journal of Korean Society for Atmospheric Environment
• /
• v.23 no.1
• /
• pp.64-73
• /
• 2007

The catalytic activity of transition metals (Cu, Co, Mn, Fe and Ni) supported on ${\gamma}-Al_2O_3$ for the oxidation of toluene was investigated in the microreactor of fixed-bed type. The catalytic activity of transition metals for the oxidation of toluene turned out to be increasing in the order of Ni$Cu/{\gamma}-Al_2O_3$ catalysts for the oxidation of toluene increased with the increasing loadings of copper, reached the maximum activity at 5% loadings of copper, and decreased with higher loadings of copper in the catalysts. The activity of $Cu/{\gamma}-Al_2O_3$ catalysts for the oxidation of toluene decreased with the increasing calcination temperatures. This might result from the decreasing surface area of catalysts due to the sintering of copper oxide as well as ${\gamma}-Al_2O_3$ supports. The 5wt% $Cu/{\gamma}-Al_2O_3$ catalysts calcined at $400^{\circ}C$ for 4 hrs in the air showed the highest activity for the oxidation of toluene. Mutual inhibition was observed for the binary mixture of toluene and xylene. The activity of the easy-to-oxidize toluene was greatly decreased while the difficult-to-oxidize xylene was slightly decreased in the binary mixture of toluene and xylene. It might suggest that the inhibition of toluene and xylene in the binary mixture resulted from the competitive adsorption for the adsorbed oxygen on the catalytic surface.

• Journal of Korean Society for Atmospheric Environment
• /
• v.22 no.6
• /
• pp.799-807
• /
• 2006

The catalytic activity of $Pt/{\gamma}-Al_2O_3$ catalysts for the oxidation of toluene and toluene+xylene mixture was investigated in the microreactor of fixed-bed type. The calcination temperatures and loadings of $Pt/{\gamma}-Al_2O_3$ catalysts played the important role in the activity of catalysts for the oxidation of toluene. The increasing calcination temperatures and loadings of $Pt/{\gamma}-Al_2O_3$ catalysts increased the crystallite size of the platinum to result in the higher oxidation activity of catalysts. The catalytic activity for the toluene oxidation over $Pt/{\gamma}-Al_2O_3$ catalysts turned out to be increasing in the order of $500^{\circ}C\;<\;800^{\circ}C<600^{\circ}C\;<\;700^{\circ}C$ for calcination temperatures and 0.1 wt% < 0.3 wt% < 1.0 wt% for platinum loadings, respectively. The 1.0 wt% $Pt/{\gamma}-Al_2O_3$ catalysts calcined at $700^{\circ}C$ for 3 hrs in the air showed the highest activity for the oxidation of the toluene. The decrease of oxidation activity of $Pt/{\gamma}-Al_2O_3$ catalysts calcined at $800^{\circ}C$ might result from the decrease of active sites by sintering of platinum metals as well as ${\gamma}-Al_2O_3$ supports. The 1.0wt% $Pt/{\gamma}-Al_2O_3$ catalyst showed the activity from the lower temperature at $120^{\circ}C$, reached the light-off temperature ($T_{50%}$) at $180^{\circ}C$, and leveled off its activity at $340^{\circ}C$ with the conversion of 100% 'Mutual promotion' effects were observed for the binary mixture of toluene and xylene. The activity of the easy-to-oxidize toluene was slightly increased with the existence of the xylene. It might suggest the different mechanism for the oxidation of toluene and xylene on the $Pt/{\gamma}-Al_2O_3$ catalysts on different sites, and its reaction of gaseous oxygen.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.2
• /
• pp.59-64
• /
• 2014

Crystallographic phases of Plasma electrolytic oxidized Al alloy, A1050, were investigated. The electrolyte of PEO was $Na_2Si_2O_3$ and KOH. Unipolar pulse, $ 2000{\mu}sec$ with $400{\mu}sec+420V$ impulse, were applied for 2 min, 5 min, 15 min, and 30 min. ${\gamma}-Alumina$, as well as ${\alpha}-alumina$, was main crystal phase. ${\gamma}-Alumina$ was appeared in the beginning, then the amount of ${\alpha}-alumina$ was increased with time, but the amount of ${\gamma}-Alumina$ remained constant without any increasing. So, it is concluded that plasma gas produce ${\gamma}-Alumina$ at the first, and then ${\gamma}-Alumina$ transform ${\alpha}-alumina$ finally. During the transformation, high temperature of micro plasma gives transformation energy.

• Journal of Conservation Science
• /
• v.30 no.4
• /
• pp.417-425
• /
• 2014

Color characteristics of the Cu-Sn alloys (bronze) in as-cast conditions were determined by reference to the $L^*$, $a^*$, $b^*$ color space. Results show that the values of $a^*$ and $b^*$ decrease with the increase in Sn levels, indicating that the colors of bronze alloys are increasingly away from red and yellow with the increase in the fraction of the ${\delta}$ phase while the opposite is true with the ${\alpha}$ phase. It has also been found in similar experiments with the Cu-22% Sn alloys that heat treatments in varying conditions produce subtle differences in their color characteristics as observed in the $L^*$, $a^*$, $b^*$ color space, due likely to the formation of various phases in different fractions.

• The Transactions of the Korean Institute of Power Electronics
• /
• v.5 no.2
• /
• pp.176-183
• /
• 2000

In this paper, sixth order hannonic injected PWM for improving‘ input CWTent distortion of single switch t three phase boost converter is presented. Peliodic sixth order hmmonic ${\gamma}$oltage is inj<:ded in the control circuit t to var${\gamma}$ the duty ratio of the converter switch within one switching cycle. In the result, the input phase c currents are forced to track the input voltage and an 해most unity power factor is obtained. Expelimental r results are verified by converter operating at 400V /6kW with three phase 140V ~220V input and by C02 arc w welding machine which was nonlinear load with 3 $\phi$ 220V input.

• Korean Chemical Engineering Research
• /
• v.46 no.3
• /
• pp.545-549
• /
• 2008

The surface characteristics of calcined ${\gamma}-Al_2O_3$ particles as well as ${\gamma}-AlO$(OH) sol particles were controlled by aging in the boehmite sol preparation. As a result of the study, the IEPs of ${\gamma}-AlO$(OH) particles were decreased from pH 9.25 to pH 8.70 and those of the calcined ${\gamma}-Al_2O_3$ particles were decreased from pH 9.90 to pH 8.86 by the increase of the aging times. As a result of the acidic and basic characterization of the calcined ${\gamma}-Al_2O_3$ particles by the aging, the amount of acid sites was decreased from 0.1367 mmol/g to 0.0783 mmol/g by the increase of the aging times and Hammett acidity, $H_o$ was showed the acidic strength of 4.8 or above. On the other hand, the amount of basic sites was decreased from 0.4399 mmol/g to 0.3074 mmol/g by the increase of the aging times. Based on these results, we proposed the fact that the aging step in the sol-gel process was an important step to control the surface characterization of ${\gamma}-Al_2O_3$ particles including acidity and basicity.

• Journal of Conservation Science
• /
• v.27 no.4
• /
• pp.421-430
• /
• 2011

Thermal conditions in practice at the traditional bronze workshop of the Korean Folk Village in Yongin were examined along with the microstructures of some high tin bronze objects made there. Laboratory experiments approximating the conditions of the workshop were also carried out and the results were compared. The operating temperature of the workshop furnace was measured to range from $750^{\circ}C$ to $850^{\circ}C$ while the surface temperature of an object, upon its removal from the furnace for additional thermo-mechanical treatments, was generally in the range of $600^{\circ}C$ to $685^{\circ}C$. This variation in working temperatures was reflected in varying microstructures developed upon quenching. The products of the Folk Village were found to consist of microstructures where the ${\alpha}$ grains of the Cu-Sn system were distributed in the background of different phases including the ${\beta}$-martensite phase, retained ${\gamma}$ phase, ${\alpha}+{\delta}$ eutectoid or their mixtures. This variability, which is also identified in objects made in ancient times as well as in our laboratory experiments, suggests that the actual thermal conditions given during the quenching treatments are much more complicated than is inferred from the temperature measurements. This paper will present detailed accounts of the thermo-mechanical treatments as observed in the high tin bronze workshop of the Korean Folk Village and discuss the evolution of varying microstructures in terms of the substantial variability involved in the implementation of the traditional forged high tin bronze technology of Korea.

• Journal of the Korean Magnetics Society
• /
• v.4 no.4
• /
• pp.347-354
• /
• 1994

The structural change and magnetic properties of mechanically milled Fe-N and Mn-Al alloy powders have been investigated by XRD, TEM, VSM, $M\"{o}ssbauer$ spectroscopy and inelastic neutron scattering measurements. During milling of ${\gamma}'-Fe_{4}N$ powders, and fcc ${\gamma}'-Fe_{4}N$ phase is transformed to a bct ${\alpha}'-Fe(N)$ phase by stress-induced martensitic transformation, being accompanied by an initial increase in saturation magnetization. During annealing the bct ${\alpha}'-Fe(N)$ nanocrystalline phase which is obtained by mechanical grinding for a long time, an ${\alpha}'-Fe_{16}N_{2}$ phase partially appears as an intermediate phase at 673~773 K, causing an increase in saturation magnetization. During milling of Mn-45, 70 and 85 at.% Al mixed powders, Al atoms are partially solubilized into an ${\alpha}-Mn$ phase. The Al supersaturated ${\alpha}-Mn-type$ phases change from paramagnetic to ferromagnetic : the saturation magnetization is 11 emu/g for the as-milled Mn-70 at.% Al powders. Moreover, by removing almost all Al atoms from the as-milled Mn-85 at.% Al powders using chemical leaching, the saturation magnetization increases up to 36 emu/g. The above bct ${\alpha}'-Fe(N)$ and ferromagnetic ${\alpha}-Mn$ type alloys are the magnetic materials found for the first time, by using the present mechanochemical process.

• Clean Technology
• /
• v.15 no.4
• /
• pp.273-279
• /
• 2009

$SF_6$, which has a high global warming potential, can be decomposed to sulfur and fluorine compounds through hydrolysis by $H_2O$ or oxidation by $O_2$ over solid acid catalysts. In this study ${\gamma}-Al_2O_3$ was employed as the solid acid catalyst for the abatement of $SF_6$ and its catalytic activity was investigated with respect to the reaction temperature and the space velocity. The catalytic activity for $SF_6$ decomposition by the hydrolysis reached the maximum at and above 973 K with the space velocity of $20,000\;ml/g_{-cat}{\cdot}h$, exhibiting a conversion very close to 100%. When the space velocity was lower than $45,000\;ml/g_{-cat}{\cdot}h$, the conversion was maintained at the maximum value. On the other hand, the conversion of $SF_6$ by the oxidation was about 20% under the same conditions. The SEM and XRD analyses revealed that the ${\gamma}-Al_2O_3$ was transformed to ${\alpha}-Al_2O_3$ during the hydrolysis and to $AlF_3$ during the oxidation, respectively. The size of $AlF_3$ after the oxidation was over $20\;{\mu}m$, and its catalytic activity was low due to the low surface area. Therefore, it was concluded that the hydrolysis over ${\gamma}-Al_2O_3$ was much more favorable than the oxidation for the catalytic decomposition of $SF_6$.