• KIEE International Transactions on Electrophysics and Applications
• /
• v.5C no.6
• /
• pp.251-256
• /
• 2005

Directionally melt-textured high $T_c\;(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_{2}Cu_{3}O_y$ [(YNS)-123] superconductor was systematically investigated by the zone melt growth process in air. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.5}Nd_{0.25}Sm_{0.25})_{2}BaCuO_5$[(YNS)211] inclusions were uniformly dispersed in large $(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_{2}Cu_{3}O_y$ [(YNS)123] matrix. High irreversibility field and magnetization hysteresis loop of the zone melt-textured (YNS)-123 sample exhibited the enhanced flux pinning, compared with $YBa_{2}Cu_{3}O_y$ (Y-123) sample without RE(rare earth). Critical current density of (YNS)-123 sample was $2.5{\times}10^4\;A/cm^2$ at 2 T and 77 K.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.5
• /
• pp.188-192
• /
• 2005

High $T_c(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_2Cu_3O_y[(YNS)-123]$ superconductors with/without $CeO_2$ additive were systematically investigated by the zone melt growth process in air. Cylindrical green rods of (YNS)-123 oxides were fabricated by cold isostatic pressing (CIP) method using rubber mould. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.5}Nd_{0.25}Sm_{0.25})_2BaCuO_5[(YNS)211]$ nonsuperconducting inclusions were uniformly dispersed in large $(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_2Cu_3O_y$[(YNS)123] superconducting matrix. In this study, optimum melting temperature and growth rate were $1100^{\circ}C$ and 3 mm/hr, respectively. The directionally melt-textured (YNS)-123 sample with $CeO_2$ additive showed an onset critical temperature $(T_c)\;T_c{\geq}93K$ and sharp superconducting transition.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.243-243
• /
• 2007

We have studied the electrical properties and microstructure of $(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_2Cu_3O_y[(YNS)-123]$ Oxides by rod-type seeded melt growth process(RSMG) in air atmosphere. Rod-type $NdBa_2Cu_3O_y${Nd-123) seed crystals made a extrusion process method, were used for achieving the ab-plane alignment having large grains perpendicular to the center of (YNS)-123 samples. The observations using SEM and TEM micrographs of the melt-textured (YNS)-123 samples revealed that the nonsuperconducting $(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_2Cu_3O_y[(YNS)-211]$ inclusions are uniformly distributed in the superconducting matrix. The microstructure and electrical properties were investigated by XRD, SEM, TEM and DC SQUID magnetometer. The sample showed a sharp superconducting transition at 90 K. The magnetization values of the (YNS)-123 sample exhibited the enhanced electrical properties, compared with $YBa_2Cu_3O_y$(Y-123) sample.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.280-281
• /
• 2005

We have studied the superconducting properties and flux pinning enhancement of $(Y_{0.5}Nd_{0.25}Sm_{0.25})_{1.8}Ba_{2.4}Cu_{3.4}O_y$ [(YNS)-1.8] composite oxides by melt growth process in air. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.5}Nd_{0.25}Sm_{0.25})_2BaCuO_5$ [(YNS)211] nonsuperconducting particles were uniformly dispersed in large (YNS)123 superconducting matrix. The sample showed a sharp superconducting transition at 91 K. The magnetization measurements of the (YSN)-1.8 sample exhibited the enhanced flux pinning, compared with $YBa_2Cu_3O_y$ (Y-123) sample without Sm and Nd.