Characterization of Poly(trimethylene terephthalate) Nanofibrous and Microfibrous Web  

Kang, Yun-Ok (Department of Nano Technology, Chungnam National University)
Park, Cho-Hee (Department of Advanced Organic Materials and Textile System Engineering)
Nam, Young-Sik (Institute of Chemical and Biological Engineering, Chungnam National University)
Kim, Jin-Hong (The Huvis R&D Institute)
Park, Won-Ho (Department of Advanced Organic Materials and Textile System Engineering)
Publication Information
Textile Science and Engineering / v.47, no.6, 2010 , pp. 399-405 More about this Journal
Abstract
A nanofibrous web was fabricated by electrospinning poly(trimethylene terephthalate)(PTT). The PTT web with an average diameter of 290 nm was obtained by electrospinning from a 16%(w/v) PTT solution, whereas a PTT film was obtained from solution casting. The water contact angle of the PTT web was much higher than that of the PTT film because the web had a nanofibrous structure with a high surface area and surface roughness. The PTT film crystallized isothermally in the temperature range of $182-231^{\circ}C$ and exhibited a multiple melting phenomenon. The degrees of crystallinity of the PTT film and PTT web were 59.2 and $38.7^{\circ}C$ respectively. The crystallinity of the PTT web was lower than that of the PTT film because the web solidified rapidly by fast solvent evaporation during electrospinning. To increase the thickness of the web, the spinning solvent was changed to 1,1,1,3,3,3-hexafluoro-2-propanol (HFIP). As a result, a nanofibrous web with average diameter of 900 nm and thickness of 0.36 mm was obtained under the same electrospinning conditions. The overall porosity of the nanofibrous web was higher than the microfibrous web. The tensile strength and tear strength of the microfibrous web was higher than those of the nanofibrous web, whereas the breaking elongation of the nanofibrous web is higher than that of the microfibrous web.
Keywords
poly(trimethylene terephthalate); electrospinning; nanofibrous web;
Citations & Related Records
연도 인용수 순위
  • Reference
1 E. M. Woo and T. Y. Ko, "A Differential Scanning Calorimetry Study on Poly(ethylene terephthalate) Isothermally Crystallized at Stepwise Temperatures: Multiple Melting Behavior Re-investigated", Colloid Polym Sci, 1996, 274, 309-315.   DOI
2 B. S. Hsiao, Z. Wang, F. Yeha, Y. Gao, and K. C. Sheth, "Time-resolved X-ray Studies of Structure Development in Poly(butylenes terephthalate) during Isothermal Crystallization", Polymer, 1999, 40, 3515-3523.   DOI   ScienceOn
3 P. Srimoaon, N. Dangseeyun, and P. Supaphol, "Multiple Melting Behavior in Isothermally Crystallized Poly (trimethylene terephthalate)", Eur Polym J, 2004, 40, 599-608.   DOI   ScienceOn
4 B. Wang, C. Y. Li, J. Hanzlicek, S. Z. D. Cheng, P. H. Geil, J. Grebowicz, and R. Ho, "Poly(trimethylene teraphthalate) Crystal Structure and Morphology in Different Length Scales", Polymer, 2001, 42, 7171-7180.   DOI   ScienceOn
5 Y. Il, H. S. Moon, W. S. Lyoo, T. S. Lee, and W. H. Park, "Superhydrophobicity of Cellulose Triacetate Fibrous Mats Produced by Electrospinning and Plasma Treatment", Cabohydrate Polymers, 2009, 75, 246-250.   DOI   ScienceOn
6 A. Singh, L. Steely, and H. R. Allcock, "Poly(bis(2,2,2-trifluoroethoxy)pheosphazene) Superhydrophobic Nanofibers", Langmuir, 2005, 21, 11604-11607.   DOI   ScienceOn
7 D. Li and Y. Xia, "Electrospinning of Nanofibers: Reinventing the Wheel", Adv Mater, 2004, 16, 1151-1170.   DOI   ScienceOn
8 M. Pyda, A. Boller, J. Grebowicz, H. Chuah, B. V. Lebedev, and B. Wunderlich, "Heat Capacity of Poly(trimethylene terephthalate)", J Polym Sci B: Polym Phys, 1998, 36(14), 2499-2511.   DOI   ScienceOn
9 J. C. Kim, T. H. Oh, and J. H. Hyun, "PTT-New Fibers in 21C", Fiber Technol Ind, 2002, 6(12), 29-40.