Effect of Zephyr Producing Method on Properties of Bamboo Zephyr Boards

In order to develop structural 'bamboo zephyr board', properties of boards produced by various methods making zephyr were estimated. All of boards were tested with KS(Korean Standards) F 3014 Particle board, and results were summarized as follow. The zephyr boards produced by final 1.5 mm roller space had the best properties(MOR, MOE and IB strength) among boards produced by different final roller space. Also, they had the best properties(MOR and MOE) in bending test after 1 hour soaking treatment after 2 hour-boiling in water, which were similar to properties of boards in dry-condition. Thickness swelling(TS) of all boards was less than 12% required to the Korean Standards A 3014. Zephyr boards produced by final 1.5 mm roller space also had the lowest values among all of boards. Boards produced by non-treatment (in green condition) had the better strength than those of boards produced by different pre-treatment methods(boiling in water and in 0.3% NaOH) in bending test.

대나무 Zephyr의 제조 조건에 따른 보드의 물성비교

본 연구에서는 합판 대체용도로서 고성능을 보유하는 대나무 Zephyr 보드의 제조기술을 확립하기 위한 기초조사로서 Zephyr의 제조방법을 달리하여 Zephyr를 제조한 후 각각의 Zephyr로 제조된 보드의 물성을 검토하였다. 제조된 보드는 KS F 3014와 KS F 3113에 준하여 성능평가를 하였으며 그 결과는 다음과 같다. 최종 롤러간극을 각각 1 mm, 1.5 mm, 2 mm로 달리하여 제조된 Zephyr 보드 중에서는 1.5 mm에서 제조된 Zephyr 보드가 휨성능(MOR, MOE)과 박리강도(IB)에서 가장 높은 강도를 보유하고 있었다. 또한, 2시간 자비한 후 1시간 상온수에 침지한 다음에 측정된 보드의 습윤시 휨성능(MOR, MOE) 역시 최종 롤러간극 1.5 mm에서 제조된 Zephyr 보드에서 가장 높은 잔존강도를 보유하고 있어 상태시와 거의 유사한 경향을 나타내고 있었다. 24시간 상온수에 침지한 후의 두께팽창율 시험에서 모든 보드가 KS A 3014의 기준인 12%보다 낮게 나타났으며 그중 롤러간극 1.5 mm Zephyr로 제조된 보드가 가장 낮은 값을 나타내어 치수안정성이 뛰어난 것으로 나타났다. 전처리에 따른 대나무 Zephyr 보드의 강도 성능은 무처리 생재상태로 제조된 보드가 다른 전처리(증해, 0.3%NaOH자비)를 한 Zephyr 보드보다 높은 강도를 보유하고 있었다. 따라서, 무처리 생재상태에서 최종롤러 간극 1.5 mm로 제조된 Zephyr sheet가 최적의 보드 제조조건임을 알 수 있었다.