Development of brazing technologies for bonding of graphite and CuCrZr joints applying for the first wall of the EAST device

  • Xianke Yang (University of Science & Technology of China) ;
  • Lei Yin (Institute of Plasma Physics, Hefei Institutes of Physical Science, Chinese Academy of Sciences) ;
  • Yanwei Liu (University of Science & Technology of China) ;
  • Qianqian Lin (University of Science & Technology of China) ;
  • Chongfeng Zhong (University of Science & Technology of China) ;
  • Si Zhang (University of Science & Technology of China) ;
  • Damao Yao (University of Science & Technology of China)
  • Received : 2024.03.21
  • Accepted : 2024.06.08
  • Published : 2024.11.25
Download PDF
⟨ Previous Next ⟩

Abstract

Bonding between plasma-facing materials (PFMs) and heat sinks is an important factor for the performance of plasma-facing components (PFCs) in the tokamak device; in some specific applications, graphite is adopted as the plasma-facing material and CuCrZr as the heatsink. Bonding of graphite and CuCrZr is a critical and difficult process due to the poor wettability of graphite and wide gap of material properties between graphite and CuCrZr, to which should be paid more attention. Herein, brazing processes were developed to achieve the bonding of CuCrZr and graphite, and a layer of oxygen-free copper (OFC) was placed between graphite tiles and CuCrZr heat sinks as a stress-buffer layer. Three types of brazing fillers including Ti powder with AgCu foil, AgCuTi paste and AgCuTi foil were used to achieve the bonding of CuCrZr and graphite. Samples were tested by scanning electron microscopy (SEM), energy dispersive spectrometry (EDS) and shear strength experiment; the results showed that these three types of fillers can achieve the bonding of CuCrZr and graphite. In addition, one-step brazing and multi-step brazing were both developed to achieve the bonding of graphite/OFC/CuCrZr, and the mock-ups were manufactured and endured cyclic high heat loads in the high heat flux (HHF) tests. In conclusion, the simplified one step brazing process including types of fillers, brazing temperature and brazing sequence was determined, which provides a promising premise method for the heat transfer structure design of PFCs.

Keywords

Acknowledgement

This work was supported by MCF Energy R&D Program (2018YFE0312300), Comprehensive Research Facility for Fusion Technology Program of China under Contract No.2018-000052-73-01-001228 and the Science Foundation of the Institute of Plasma Physics, Chinese Academy of Sciences (Grant No. DSJJ-18-03).

References

  1. T. Tanabe, Revisiting carbon materials as plasma-facing materials of a fusion reactor, Plasma Phys. Rep. 45 (2019) 300-314.  https://doi.org/10.1134/S1063780X1904007X
  2. M. Li, S.J. Zinkle, Physical and Mechanical Properties of Copper and Copper Alloys: Volume, Elsevier Ltd., 2012, pp. 667-690. 
  3. D. Yao, L. Bao, J. Li, et al., Design, analysis and R&D of the EAST in-vessel components, Plasma Sci. Technol. 10 (3) (2008) 367. 
  4. Y. Lu, L. Cai, L. Zhang, et al., Engineering design and analysis of first wall on the high-magnetic-field-side for HL-2M tokamak, Fusion Eng. Des. 195 (2023) 113963. 
  5. Y. Lian, J. Wang, F. Feng, et al., Progress in the development of CFC/CuCrZr components for HL-2M divertor, IEEE Trans. Plasma Sci. 46 (5) (2018) 1556-1560.  https://doi.org/10.1109/TPS.2018.2789429
  6. M. Lipa, J. Schlosser, F. Escourbiac, Development of actively cooled plasma-facing components for Tore Supra, Fusion Sci. Technol. 56 (3) (2009) 1124-1149.  https://doi.org/10.13182/FST09-A9171
  7. S.S. Khirwadkar, K.P. Singh, Y. Patil, et al., Fabrication and characterization of tungsten and graphite based PFC for divertor target elements of ITER like tokamak application, Fusion Eng. Des. 86 (9-11) (2011) 1736-1740.  https://doi.org/10.1016/j.fusengdes.2011.01.111
  8. Z. Tao, Q. Guo, X. Gao, et al., The wettability and interface thermal resistance of copper/graphite system with an addition of chromium, Mater. Chem. Phys. 128 (1-2) (2011) 228-232.  https://doi.org/10.1016/j.matchemphys.2011.03.003
  9. R.G. Donnelly, G.M. Slaughter, The brazing of graphite, Welding 41 (1962) 461-469. 
  10. Yuntao Song, et al., Realization of thousand-second improved confinement plasma with Super I-mode in Tokamak EAST, Sci. Adv. 9 (1) (2023) eabq5273. 
  11. T.T. Ikeshoji, Brazing of C/C composites and titanium alloys with inserting OFHC copper foil, Proc. Brazing, Hight Temperature Brazing and Diffusion Bonding LOT2010 DVS (2010), 23-2. 
  12. X. Yang, D. Yao, L. Yin, et al., Design of the CFC composite brazed HFS first wall on the NBI shine-through area of the EAST device, Fusion Eng. Des. 200 (2024) 114151. 
  13. J.W. Davis, P.D. Smith, ITER material properties handbook, J. Nucl. Mater. 233 (1996) 1593-1596. 
  14. H. Kishimoto, W. Kondo, N. Nakazato, et al., Microstructural stability of tungsten coated CFC plates aiming to metal wall experiments at JT-60SA, Fusion Eng. Des. 161 (2020) 111887. 
  15. Q. Lu, W. Long, S. Zhong, et al., TZM/graphite interface behavior in high-temperature brazing by Ti-based brazing filler materials, Weld. World 64 (2020) 1877-1885.  https://doi.org/10.1007/s40194-020-00967-3
  16. X. Peng, J. Liu, J. Wang, et al., Surface diversifying and deuterium retention characteristics of doped graphite with SiC coating exposed to plasma discharges in EAST tokamak, Nanosci. Nanotechnol. Lett. 9 (9) (2017) 1306-1311.  https://doi.org/10.1166/nnl.2017.2450
  17. J.-F. Salavy, L. Giancarli, M. Merola, et al., Analysis of high heat flux testing of mock-ups, Fusion Eng. Des. 66 (3) (2003) 277-281. 
  18. S. Suzuki, M. Akiba, M. Araki, et al., Thermal cycling experiments of monoblock divertor modules for fusion experimental reactors, Fusion Technol. 21 (3P2B) (1992) 1858-1862.  https://doi.org/10.13182/FST92-A29989
  19. M. Merola, A. Orsini, E. Visca, et al., Influence of the manufacturing heat cycles on the CuCrZr properties, J. Nucl. Mater. 307 (2002) 677-680. 
  20. U. Holzwarth, M. Pisoni, R. Scholz, et al., On the recovery of the physical and mechanical properties of a CuCrZr alloy subjected to heat treatments simulating the thermal cycle of hot isostatic pressing, J. Nucl. Mater. 279 (1) (2000) 19-30. https://doi.org/10.1016/S0022-3115(99)00278-0