모사 슬러리 용액에서 정전류 분극을 활용한 고크롬 주철 부식 시험

Corrosion Tests for High Chromium Cast Iron Using Galvanostatic Polarization Technique in a Simulating Slurry Solution

  • 바산자프 오취개럴 (국립창원대학교 소재융합시스템공학과) ;
  • 이준섭 (국립창원대학교 소재융합시스템공학과) ;
  • 이예진 (국립창원대학교 소재융합시스템공학과) ;
  • 오준석 ((주)아이-캐스팅테크) ;
  • 이재현 (국립창원대학교 소재융합시스템공학과)
  • Ochgerel Baasanjav (Materials Convergence and System Engineering, Changwon National University) ;
  • Jun-Seob Lee (Materials Convergence and System Engineering, Changwon National University) ;
  • Ye-Jin Lee (Materials Convergence and System Engineering, Changwon National University) ;
  • Jun-Seok Oh (i-Casting Tech Ltd.) ;
  • Je-hyun Lee (Materials Convergence and System Engineering, Changwon National University)
  • 투고 : 2023.07.24
  • 심사 : 2023.08.08
  • 발행 : 2023.08.30
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

The galvanostatic polarization technique was used to accelerate corrosion in high chromium cast iron (HCCI) immersed in a simulated slurry solution of 0.1 mol dm-3 H2SO4, 0.05 mol dm-3 HCl, and 10 wt% SiC. The HCCI contained 27 wt% of Cr and 2.8 wt% of C, and its microstructure mainly comprised austenitic and carbide phases. A two-electrode system using a dense carbon rod and the HCCI sample was employed for the galvanostatic polarization by applying an anodic current for 24 hours. The corrosion rate increased upon applying the anodic current, but the increase was not significant, particularly for current densities higher than 10 µA cm-2. Following polarization, the corrosion morphology revealed that the anodic current accelerated surface corrosion in the HCCI; however while the depth of the corroded area increased, the increase was not substantial. The propagation behavior of the anodic current and its impact on corrosion were further discussed.

키워드

과제정보

본 과제(결과물)는 교육부와 한국연구재단의 재원으로 지원을 받아 수행된 3단계 산학연협력 선도대학 육성사업(LINC 3.0)의 연구결과입니다.

참고문헌

  1. C. K. Kim, S. Lee, and J. Y. Lee, Wear Resistance and Fracture Toughness of Heat-treated Duo-cast Materials Composed of High-Chromium White Cast Iron and Low-Chromium Steel, Journal of the Korean Institute of Metals and Materials, 42, 877 (2004). Doi: http://kjmm.or.kr/past/view_kiss.asp?a_key=2382457
  2. R. Lee, and Y. S. Kim, Effect of Heat treatment on Hardness and Corrosion Resistance of Super Cast Iron, Korean Journal o Metals and Materials, 52, 511 (2013). Doi: https://doi.org/10.3365/KJMM.2014.52.7.511
  3. I. Chakrabarty, and A. Basak, Structural study of Cr-MnCu white cast irons, Journal of Materials Science Letters, 6, 1399 (1987). https://link.springer.com/content/pdf/10.1007/BF01689301.pdf
  4. J.-S. Lee, J. H. Lee, J. S. Oh, and J. H. Lee, General Corrosion Behavior of High Chromium Cast Iron in an Acid Solution, Corrosion Science and Technology, 20, 367 (2021). Doi: https://doi.org/10.14773/cst.2021.20.6.367
  5. J.-S. Lee, J. H. Lee, Y.-J. Lee, J. S. Oh, J.-G. Kim and J. H. Lee, Stir-Accelerated Corrosion Test of High Chromium Cast Iron for Application in Slurry Pumps, Corrosion Science and Technology, 21, 418 (2022). Doi: https://doi.org/10.14773/cst.2022.21.5.418
  6. J.-S. Lee, J. H. Lee, S.-Y. Rho, Y.-H. Lee, Y.-J. Lee, J. S. Oh, and J. H. Lee, 23. Preferential dissolution behaviour of the austenite phase in Fe-27Cr-xC high chromium cast iron, RSC Advances, 13, 19220 (2023). Doi: https://doi.org/10.1039/d3ra01015e
  7. J.-S. Oh, Y.-G. Song, B.-G. Choi, C. Bhamornsut, R. Nakkuntod, C.-Y. Jo and J.-H. Lee, Effect of Dendrite Fraction on the M23C6 Precipitation Behavior and the Mechanical Properties of High Cr White Irons, Metals, 11, 1576 (2021). Doi: https://doi.org/10.3390/met11101576
  8. D.-W. Jang, J.-H. Shin, I.-S. Kim, I.-Y. Jung, C.-Y. Jo and J.-H. Lee, Effect of Solidification Variables on the Tensile Property of 2.8 wt% C-26 wt% Cr White Iron, Metals, 11, 1579 (2022). Doi: https://doi.org/10.3390/met12091416
  9. Y. Zheng, W. Liu, Z. Yao, and W. Ke., Damage mechanisms and metallic materials development in multiphase flow, Corrosion Science and Technology, 1, 41 (2002). https://www.j-cst.org/opensource/pdfjs/web/pdf_viewer.htm?code=C00010100041 10100041
  10. K. M. Moon, J. G. Kim, M. H. Lee, and K. J. Kim, An Electrochemical Evaluation on the Corrosion of Weld Zone in Cold Arc Welding of the Cast Iron, Corrosion Science and Technology, 7, 134 (2008). https://www.jcst.org/main/download.htm?code=C00070200134
  11. J.-.S. Lee, K. Fushimi, T. Nakanishi, Y. Hasegawa, and Y. S. Park, Corrosion behaviour of ferrite and austenite phases on super duplex stainless steel in a modified green-death solution, Corrosion Sceience, 89, 111 (2014). Doi: http://dx.doi.org/10.1016/j.corsci.2014.08.014