초록
In this study, an experiment was conducted to confirm the applicability of the external shape control of the ultrasonic knife to the CFRTP material, which is the base material of thermoplastic. TC910 based on polyamide6 (PA6) was used as the material. The slope 와 and tool transfer speed of the material and tool were selected as process factors for processing, and the following results were obtained. Under all cutting conditions using an ultrasonic knife, friction heat caused by high-frequency vibration was issued at 150℃ at the contact part between the material and the knife during cutting. As a result of the cutting force analysis, the faster the transfer speed, the higher the cutting force as the angle of entry of the blade increased, and the size of the cutting force changed during cutting. As for the size of the burr in accordance with the transfer speed condition, the smallest burr occurred at 150mm/min in the side part, and the smallest burr occurred at 150mm/min and 200mm/min in the case of the outlet burr. The size of the burr according to the entry angle tended to decrease as the tool entry angle increased, and the side part tended to increase as the tool entry angle increased. As a result of the cutting surface analysis, it was confirmed that the base material was eluted under all conditions, and the faster the transfer speed, the lower the elution phenomenon of the base material. Based on the above results, cutting the CFRTP material with an ultrasonic knife is possible, but the effect on heat generation caused by friction needs to be minimized, and further research needs to be conducted on this.