Abstract
This study was conducted to examine the effect of the light source for the media facade of the 10-story Gyeongcheonsa Stone Pagoda on the pagoda's restoration materials. To restore the pagoda, two types of epoxy resin-L-30, Araldite (AW106, and HV953U)-were used, and the photostability of the restoration materials and the acceptable lighting irradiation time were estimated through accelerated aging experiments of the restoration specimens. Six types of specimens were used in this process: a specimen painted with blue and yellow pigments for each resin type, and an unpainted specimen. Among them, the ΔE of the unpainted specimens (BA) of Araldite AW106 and HV953U was the highest of 4.66, and the acceptable light irradiation time was about 130,000 hours if the change rate of ΔE is limited to about 1. It was confirmed that the BA specimens were losing their characteristics due to light, as their reflectance and transmittance increased and the absorbance decreased, making them more transparent than their original color. It was found that the painted specimens had a low change rate of ΔE, with insignificant changes in their reflectance, transmittance and absorbance. Therefore, the use of pigments with high photostability provides more restoration materials options.
본 연구는 경천사지 십층석탑의 미디어파사드 상영 광원이 석탑의 복원 재료에 미치는 영향을 알아보기 위해 실시하였다. 경천사지 십층석탑에 사용된 복원 재료는 Epoxy 수지로 L-30과 Araldite AW106, HV953U이며, 복원시편의 가속노화 실험을 통해 복원 재료의 광안전성과 조명의 조사 가능 시간을 추정하였다. 복원 재료는 각 수지당 채색하지 않은 시편, 청색 안료, 황색 안료를 사용한 시편으로 총 6가지이다. 이중 Araldite AW106, HV953U의 채색하지 않은 시편(BA)의 ΔE가 4.66으로 가장 변화가 크고 광 조사 가능 시간은 ΔE의 변화율을 1정도로 제한할 경우 약 130,000시간의 조사가 가능한 수준이다. BA시편의 경우 반사율과 투과율이 상승하고 흡수율은 저하되어 본연의 색상이 보다 투명해지는 방향으로 광에 의해 시편의 특성을 잃어가고 있음을 확인 하였다. 복원 재료에 안료를 사용한 경우에는 ΔE 변화율이 적으며, 반사율과 투과율, 흡수율의 변화가 미미한 수준이었다. 따라서 광안전성이 높은 안료를 사용할 경우 복원 재료 선택의 폭을 높일 수 있다.