For automotive coating agents that require little change in characteristics due to changes in external temperature, changes in noise characteristics due to changes in the external environment are very important. Therefore, soft polyurethane with excellent cold resistance, weather resistance, and abrasion resistance, and polysiloxane whose -OH terminated and side chains are modified with amines, are widely used. In this study, coating agents was prepared by adding water-born polyurethane, polysiloxane, ultra high molecular weight polypropylene (UHMWPP) powder, carbon black, and a matting agent to determine the effect of each resin component on noise. To study the effect of each resin component on noise, a coating agent was prepared by adding water-born polyurethane, polysiloxane, UHMWPP powder, carbon black, and a matting agent. The hard/soft segment ratio of water-born polyurethane, the main component of the coating, was 27.1%/72.9%, and the ratio of amino siloxanes to hydroxy-terminated polysiloxane was 2:7, which produced the least noise. The difference in friction coefficient was large when the friction body moves at high speed. When UHMWPP powder replaced SiO2, noise decreased and gloss also decreased.
외부 온도 변화에 따른 특성변화가 적어야 하는 자동차 부품용 코팅제는 외부 환경 변화에 의한 노이즈 특성 변화가 매우 중요하다. 이에 내한성, 내후성, 내마모성이 우수한 연질의 폴리우레탄과 하이드록시 말단 혹은 곁사슬이 아민으로 변성된 폴리실록산 등이 널리 사용되고 있다. 본 연구에서는 각각의 폴리머 성분들이 노이즈에 미치는 영향을 확인하기 위하여 수분산 폴리우레탄을 합성하였고, 폴리실록산, ultra high molecular polypropylene (UHMWPP) 분말, 카본블랙, 소광제를 첨가하여 코팅제를 제조하였다. 수분산 폴리우레탄의 hard/soft 세그먼트의 함량을 27.1%/72.9%, 아민으로 변성된 폴리실록산과 하이드록시 말단 폴리실록산이 2:7의 비율에서 노이즈의 발생이 가장 적었으며, 마찰자가 고속에서 움직일 때 마찰계수의 차이가 컸다. 또한 SiO2를 UHMWPP 분말로 대체함으로써, 노이즈가 감소하였으며 광택도 또한 감소하였다.