Fluidity and Strength Properties of Non-Sintered Cement Mortar according to the Addition of Superplasticizer

감수제 첨가에 따른 비소성 시멘트 모르타르의 유동성 및 강도 특성

  • Received : 2022.08.24
  • Accepted : 2022.09.27
  • Published : 2022.10.20
Download PDF
⟨ Previous Next ⟩

Abstract

In this study, the fluidity and strength characteristics of NSC mortar according to the type and rate of addition of superplasticizer were analyzed to secure the fluidity of NSC composed of only slag and ash. Through the flow test, it was found that the fluidity of NSC was related to the basicity according to the binder condition, and the lower the reactivity, the higher the fluidity. When polycarboxylate is added, NSC mortar is considered to be more advantageous than plain mortar in terms of securing fluidity. As a result of the strength tests of NSC mortar containing Lignin or Polycarboxylate superplasticizer, it was found that the strength tends to increase as the basicity increases. In addition, when polycarboxylate is added, it is judged that the NSC mortar can secure adequate fluidity and strength at the same time. Through this experiment, an appropriate binder condition that satisfies the flowability while securing the strength was derived.

본 연구에서는 순환자원으로 구성된 비소성 시멘트의 유동성 확보를 위해 감수제의 종류 및 첨가율에 따른 비소성 시멘트 모르타르의 유동성과 강도 특성을 분석하였다. 감수제 첨가에 따른 비소성 시멘트의 유동성은 감수제 첨가비율이 높고 플라이애시 치환 비율이 높을수록 유동성은 향상되는 것으로 나타났다. 특히 폴리카르본산계 감수제 첨가 시 소성 시멘트 모르타르보다 유동성 확보에 유리하며, 비소성 시멘트 모르타르의 적정 유동성 확보와 동시에 강도 확보가 가능한 것으로 판단된다. 또한 감수제 첨가에 따른 비소성 시멘트 모르타르는 고칼슘 애시의 치환 비율이 높고 염기도가 높을수록 반응성이 촉진되는 경향이 있는데 급격한 반응 촉진은 오히려 강도저하를 유발할 수 있으므로 목표한 유동성을 만족하는 범위 내에서 적정 배합조건을 도출하였다.

Keywords

Acknowledgement

This work supported by the National Research Foundation of Korea(NRF) grant funded by the Korea government(No. 2020R1F1A1048414).

References

  1. Song JK, Yang KH, Song KI. Importance and Characteristics of Geopolymer Concrete Technology. Magazine of RCR. 2017 Mar;12(2):8-15. https://doi.org/10.14190/MRCR.2017.12.1.008
  2. Choi SW. Engineering properties of low carbon high strength concrete with ground granulated blast-furnace slag-based blended cement [doctoral thesis]. [Daejeon (Korea)]: Chungnam National University. 2015. p. 10-11.
  3. Roy DM. Alkali-activated cements opportunities and challenges. Cement and Concrete Research. 1999 Feb;29(2):249-54. https://doi.org/10.1016/S0008-8846(98)00093-3
  4. Kong TW. Development of normal strength-high fluidity concrete using all-in-one polycarboxylate-based superplasticizer with viscosity modifying agent [doctoral thesis]. [Seoul (Korea)]: Hanyang University. 2022. p. 1-8.
  5. Hwang HJ, Kim HS, Jeon JY, Ryu DH, Park SJ, Park HC. The experimental study on the fundamental properties of high-calcium fly ash based non-cement inorganic binder. Proceedings of the Korea Concrete Institute; 2011 Nov 9-11; Pyeongchang, Korea. Seoul (Korea): Journal of The Korea Concrete Institute; 2011. p. 329-30.
  6. Lee HY, Moon KJ, Song H, Bae SC, Hyung WG. A study on the chemical resistance of non-sintered cement mortar. Construction and Environment Research Institute. 2011 Dec;6(2):19-26.
  7. Kang SP. A study on the effect of high-calcium fly ash on the compressive strength of the portland blast-furnace slag cement concrete. Journal of the Construction and Environment Research Institute. 2012 Oct;7(1):22-30.
  8. Cho SW, Na HW, Hyung WG. Properties of cement mortar according to mixing of circulating fluidized bedfly ash and pulverized coal fly ash based on blast furnace slag. Journal of the Korea Institute of Building Construction. 2021 Apr; 21(2):141-8. https://doi.org/10.5345/JKIBC.2021.21.2.141
  9. Kim JH. A study on the effects of crystalline change of fa-bfs system geopolymer ceramics to thermal properties [doctoral thesis]. [Chun Cheon (Korea)]: Kangwon National University. 2017. 18 p.
  10. Lee SH. Consideration of cautions regarding the use of admixtures and admixtures in cement and concrete. Korea Cement Association Cement Symposium; 2011 July 7-8; Chungju,Korea. Seoul (Korea): Korea Cement Association; 2011. p. 38-46.
  11. Li Y, Yang C, Zhang Y, Zheng J, Guo H, Lu M. Study on dispersion, adsorption and flow retaining behaviors of cement mortars with TPEG-type polyether kind polycarboxylate superplasticizers. Construction and Building Materials. 2014 Aug;64(14):324-32. https://doi.org/10.1016/j.conbuildmat.2014.04.050
  12. Chang JH. Charaterization of water reducing agents affecting material properties of alkaline activated mortar. [doctoral thesis]. [Cheongju (Korea)]: Cheongju University. 2015. p. 57-97.
  13. Koh KT, Ryu GS, Lee JH, Kang HJ, Jeon YS. Flowability and compressive strength of cementless alkali-activated mortar using blast furnace slag. Journal of the Korean Recycled Construction Resources Institute. 2011 Mar;6(1):63-71.
  14. Smith MA. Slag/fly ash cement. World Cement Technology. 1977 Nov;8(6):223-33.
  15. Choi JJ. Kinds and properties of superplasticizer. Magazine of the Korea Concrete Institute. 2001 May;13(3):32-7. https://doi.org/10.22636/MKCI.2001.13.3.32