Shrinkage and crack characteristics of filling materials for precast member joint under various restraint conditions

  • Lim, Dong-Kyu (Department of Civil and Environmental Engineering, Dankook University) ;
  • Choi, Myoung-Sung (Department of Civil and Environmental Engineering, Dankook University)
  • Received : 2022.06.01
  • Accepted : 2022.08.13
  • Published : 2022.08.25

Abstract

Filling materials poured into precast member joint are subjected to restraint stress by the precast member and joint reinforcement. The induced stress will likely cause cracks at early ages and performance degradation of the entire structure. To prevent these issues and design reasonable joints, it is very important to analyze and evaluate the restrained shrinkage cracks of filling materials at various restraint conditions. In this study, a new time zero-that defines the shrinkage development time of a filling material-is proposed to calculate the accurate amount of shrinkage. The tensile stresses and strengths at different ages were compared through the ring test (AASHTO PP34) to evaluate the crack potential of the restrained filling materials at various restraint conditions. The mixture which contained an expansive additive and a shrinkage reducing agent exhibited high resistance to shrinkage cracking owing to the high-drying shrinkage compensation effect. The high-performance, fiber-reinforced cement composite, and ultra-high-performance, fiber-reinforced cement composite yielded very high resistance to shrinkage and cracking owing to the pull-out property of steel fibers. To this end, multiple nonlinear regression analyses were conducted based on the test results. Accordingly, a modified tensile stress equation that considered both the geometric shape of the specimen and the intrinsic properties of the material is proposed.

Keywords

Acknowledgement

This work was supported by the Korea Agency for Infrastructure Technology Advancement (KAIA) grant funded by the Ministry of Land, Infrastructure and Transport (Grant 22CFRP-C163381-02).

References

  1. AASHTO (2012), Estimating the Cracking Tendency of Concrete, 99, 3-7.
  2. Ajaev, V.S. and Homsy, G.M. (2001), "Steady vapor bubbles in rectangular microchannels", J. Colloid. Interf. Sci., 240, 259-271. https://doi.org/10.1006/jcis.2001.7562
  3. Altoubat, S.A. and Lange, D.A. (2001), "Creep, shrinkage, and cracking of restrained concrete at early age", ACI Mater. J., 98, 323-331.
  4. ASTM C39/C 39M-01 (2001), Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens, American Society for Testing and Materials. 04.02.
  5. ASTM C403 (2016), ASTM C403- Standard Test Method for Time of Setting of Concrete Mixtures by Penetration Resistance, Annual Book of ASTM Standards.
  6. ASTM C1611M (2014), Standard Test Method for Slump Flow of Self-Consolidating Concrete, ASTM International.
  7. Banthia, N. (1990), "A study of some factors affecting the fiber-matrix bond in steel fiber reinforced concrete", Can. J. Civil Eng., 17, 610-620. https://doi.org/10.1139/l90-069
  8. Boulekbache, B., Hamrat, M., Chemrouk, M. and Amziane, S. (2010), "Flowability of fibre-reinforced concrete and its effect on the mechanical properties of the material", Constr. Build. Mater., 24, 1664-1671. https://doi.org/10.1016/j.conbuildmat.2010.02.025
  9. C.-F.M. Code (2013), fib Model Code for Concrete Structures 2010; Ernst & Sohn, Wiley, Berlin, Germany.
  10. Chan, Y.-W. and Chu, S.-H. (2004), "Effect of silica fume on steel fiber bond characteristics in reactive powder concrete", Cement Concr. Res., 34(7), 1167-1172. https://doi.org/10.1016/j.cemconres.2003.12.023
  11. Chu, I., Kwon, S.H., Amin, M.N. and Kim, J.-K. (2012), "Estimation of temperature effects on autogenous shrinkage of concrete by a new prediction model", Constr. Build. Mater., 35, 171-182. https://doi.org/10.1016/j.conbuildmat.2012.03.005
  12. Dadmand, B., Pourbaba, M., Sadaghian, H. and Mirmiran, A. (2020), "Effectiveness of steel fibers in ultra-high-performance fiber-reinforced concrete construction", Adv. Concrete Constr., Int. J., 10(3), 195-209. https://doi.org/10.12989/acc.2020.10.3.195
  13. Davis, H.E. (1940), "Autogenous volume change of concrete", Proc. ASTM, 40, 1103-1110.
  14. Dela, B.F. (2000), Eigenstresses in hardening concrete, DTU Department of Structural Engineering and Materials, V. Series R.
  15. Esfahani, M.R. and Rangan, B.V. (1998), "Local bond strength of reinforcing bars in normal strength and high-strength concrete (HSC)", Struct. J., 95, 96-106.
  16. Fujiwara, H., Tomita, R. and Shimoyamata, Y. (1994), "Study of frost resistance of concrete using an organic shrinkage-reducing agent", Special Publication, 145, 643-656.
  17. Hadi, M.N.S. (2008), "Bond of high strength concrete with high strength reinforcing steel", Open Civil Eng. J., 2, 143-147. https://doi.org/10.2174/1874149500802010143
  18. Han, C.G., Kim, S.W., Koh, K.T. and Pei, Z.L. (2003), "Properties on the shrinkage of high performance concrete using expansive additive and shrinkage reducing agent", J. Korea Concrete Inst., 15(6), 785-793. https://doi.org/10.4334/JKCI.2003.15.6.785
  19. Han, H.S., Kim, J.K. and Jung, Y.W. (2016), "Development and performance assessment of the high-performance shrinkage reducing agent for concrete", Adv. Mater. Sci. Eng., 2016. https://doi.org/10.1155/2016/9318086
  20. Hossain, A.B. and Weiss, J. (2004), "Assessing residual stress development and stress relaxation in restrained concrete ring specimens", Cement Concr. Compos., 26, 531-540. https://doi.org/10.1016/S0958-9465(03)00069-6
  21. Hossain, A.B. and Weiss, J. (2006), "The role of specimen geometry and boundary conditions on stress development and cracking in the restrained ring test", Cement Concr. Res., 36(1), 189-199. https://doi.org/10.1016/j.cemconres.2004.06.043
  22. Igarashi, S.I., Bentur, A. and Kovler, K. (2000), "Autogenous shrinkage and induced restraining stresses in high-strength concretes", Cement Concr. Res., 30(11), 1701-1707. https://doi.org/10.1016/S0008-8846(00)00399-9
  23. Japan Society of Civil Engineers (JSCE) (2007), Standard specification for concrete structures; Structural Performance Verification.
  24. Kim, S.-W., Kang, S.-T. and Han, S.-M. (2006), "Characteristics and application of ultra high performance cementitious composite", Mag. Korea Concrete Inst., 18, 16-21.
  25. Koh, K., Ryu, G., Kang, S., Park, J. and Kim, S. (2011), "Shrinkage properties of ultra-high performance concrete (UHPC)", Adv. Sci. Lett., 4, 948-952. https://doi.org/10.1166/asl.2011.1505
  26. Lachemi, M., Hossain, K.M.A., Lambros, V., Nkinamubanzi, P.-C. and Bouzoubaa, N. (2004), "Self-consolidating concrete incorporating new viscosity modifying admixtures", Cement Concr. Res., 34, 917-926. https://doi.org/10.1016/j.cemconres.2003.10.024
  27. Li, L., Dabarera, A.G.P. and Dao, V. (2020), "Time-zero and deformational characteristics of high performance concrete with and without superabsorbent polymers at early ages", Constr. Build. Mater., 264, 120262. https://doi.org/10.1016/j.conbuildmat.2020.120262
  28. Li, L., Dao, V. and Lura, P. (2021), "Autogenous deformation and coefficient of thermal expansion of early-age concrete: Initial outcomes of a study using a newly-developed temperature stress testing machine", Cement Concr. Compos., 119, 103997. https://doi.org/10.1016/j.cemconcomp.2021.103997
  29. Lim, D.K. and Choi, M.S. (2021), "Shrinkage and crack characteristics of filling materials under restrain stress in prefabricated structure connection", Constr. Build. Mater., 309, 125188. https://doi.org/10.1016/j.conbuildmat.2021.125188
  30. Lim, W.-Y. and Hong, S.-G. (2016), "Fracture behavior of UHPC reinforced with hybrid steel fibers", J. Korea Concr. Inst., 28, 223-234. https://doi.org/10.4334/JKCI.2016.28.2.223
  31. Mehta, P.K. (1986), Concrete. Structure, properties and materials.
  32. Neville, A.M. (1995), Properties of Concrete, Longman London, UK.
  33. Paillere, A., Buil, M. and Serrano, J.J. (1989), "Effect of fiber addition on the autogenous shrinkage of silica fume", Mater. J., 86, 139-144.
  34. Park, J.-J., Yoo, D.-Y., Kim, S.-W. and Yoon, Y.-S. (2013), "Drying shrinkage cracking characteristics of ultra-highperformance fibre reinforced concrete with expansive and shrinkage reducing agents", Mag. Concr. Res., 65, 248-256. https://doi.org/10.1680/macr.12.00069
  35. Raphael, J.M. (1984), "Tensile strength of concrete", J. Proc., 81, 158-165.
  36. Shafieifar, M., Farzad, M. and Azizinamini, A. (2017), "Experimental and numerical study on mechanical properties of ultra high performance concrete (UHPC)", Constr. Build. Mater., 156, 402-411. https://doi.org/10.1016/j.conbuildmat.2017.08.170
  37. Sun, G., Xue, S., Qu, X. and Zhao, Y. (2019), "Experimental investigation of creep and shrinkage of reinforced concrete with influence of reinforcement ratio", Adv. Concrete Constr., Int. J., 7(4), 211-218. https://doi.org/10.12989/acc.2019.7.4.211
  38. Tazawa, E. (1999), Autogenous shrinkage of concrete, CRC Press, London: E&FN Spon.
  39. Timoshenko, S. and Goodier, J.N. (1970), Theory of Elasticity, (3rd ed.), McGraw-Hill, New York, USA.
  40. Van Chanh, N. (2004), Steel fiber reinforced concrete, Faculty of Civil Engineering Ho Chi Minh City University of Technology; Seminar Material, Citeseer, pp. 108-116.
  41. Weiss, W.J., Yang, W. and Shah, S.P. (1998), "Shrinkage cracking of restrained concrete slabs", J. Eng. Mech., 124, 765-774. https://doi.org/10.1061/(ASCE)0733-9399(1998)124:7(765)
  42. Weiss, W.J., Yang, W. and Shah, S.P. (2000), "Influence of specimen size/geometry on shrinkage cracking of rings", J. Eng. Mech., 126, 93-101. https://doi.org/10.1061/(ASCE)0733-9399(2000)126:1(93)
  43. Yoo, D.-Y., Park, J.-J., Kim, S.-W. and Yoon, Y.-S. (2012), "Properties and prediction model for ultra high performance fiber reinforced concrete (UHPFRC):(I) Evaluation of setting and shrinkage characteristics and tensile behavior", J. Korean Soc. Civil Eng., 32, 307-315. https://doi.org/10.12652/Ksce.2012.32.5A.307
  44. Yoo, D.-Y., Park, J.-J., Kim, S.-W. and Yoon, Y.-S. (2014), "Influence of ring size on the restrained shrinkage behavior of ultra high performance fiber reinforced concrete", Mater. Struct., 47, 1161-1174. https://doi.org/10.1617/s11527-013-0119-0
  45. Yoo, D.Y., Park, J.J. and Kim, S.W. (2017), "Fiber pullout behavior of HPFRCC: Effects of matrix strength and fiber type", Compos. Struct., 174, 263-276. https://doi.org/10.1016/j.compstruct.2017.04.064