Abstract
Recently, the application of a photocatalyst to road structures is being attempted to solve environmental problems caused by fine particulate matter and automobile exhaust. The purpose of this study was to develop a release agent with GST (low-cost, high-performance photocatalyst produced from wastewater sludge). For this, the method of mixing and dispersing GST with the release agent was used first, and the removal performance of nitrogen oxide (NOx) was then checked. The best performance without a precipitation reaction was achieved using a stabilizing agent at 20 % in an outdoor exposure test for four weeks. The NO and NOx removal rate of the specimen demolded by applying the GST release agent developed in this study showed excellent effects of 200 to 400 % compared to the Plain material. To increase the performance of the GST release agent, it is necessary to improve the dispersibility of GST in the release agent and increase the amount of the nano-sized photocatalyst. In addition, the use of GST release agent in road structures and exposed concrete is expected to increase the NOx removal efficiency.
최근 미세먼지 및 배기가스로 인한 환경문제를 해결하고자 도로구조물의 광촉매 적용이 시도되고 있다. 이에 본 연구에서는 폐수슬러지에서 제조 후 재활용된 저비용 고성능 광촉매(GST)의 혼합 및 분산방안을 검토하고, 질소산화물(NOx) 제거 성능을 최종 평가하여 저비용 고성능 광촉매를 활용한 콘크리트 이형박리제를 개발하고자 한다. 광촉매적용을 위한 분산방안을 검토하기 위해 분산된 시료를 4주간 옥외폭로하여 분리유무를 통한 안정성을 평가한 결과, 분산형 증점제 사용량 20 % 적용시 층분리 및 침전현상 없이 안정적인 상태를 보였다. 저비용 고성능 광촉매를 활용한 이형박리제를 거푸집에 도포시켜 탈형한 시편의 NO 및 NOx 제거율은 Plain 대비 200~400 %의 우수한 효과를 나타내었다. 저비용 고성능 광촉매를 활용한 콘크리트 이형박리제의 성능을 증진시키기 위해서는 나노사이즈인 광촉매의 분산성 향상 및 사용량 증가가 필요할 것으로 사료된다. 또한, 저비용 고성능 광촉매를 활용한 이형박리제를 도로구조물 및 노출 콘크리트에 사용하게 되면 NOx 제거효율을 증가시킬 수 있을 것으로 판단된다.