A Study on the Evaluation of Basic Properties of Composite Emulsion Finishes

복합 에멀젼계 마감재의 기초물성 평가에 관한 연구

  • Received : 2019.11.04
  • Accepted : 2020.01.28
  • Published : 2020.02.20
Download PDF
⟨ Previous Next ⟩

Abstract

The thin coating material used in the outer insulation finishing method is a finishing material mainly based on acrylic emulsion. In this study, the properties of silane modified acrylic emulsion and silica dispersed acrylic emulsion were evaluated. Experimental results showed that the silane modified acrylic emulsion had no significant effect on improving tensile strength, but was effective in improving the performance of adhesion strength, water absorption coefficient, and hot and cold repeat resistance. Silica-dispersed acrylic emulsions were effective in improving tensile strength, and at 10% substitution rate, they were effective in improving the performance of adhesion strength, water absorption coefficient and hot / cold resistance. Through this, it was judged that a composite emulsion capable of improving the performance of the acrylic emulsion could be prepared.

외단열 마감 공법에서 사용되는 얇은 바름재는 아크릴 에멀젼을 주 소재로 한 마감재이다. 본 연구에서는 실란 개질 아크릴 에멀젼과 실리카 분산아크릴 에멀젼을 치환하였을때 특성을 평가하였다. 실험결과, 실란 개질 아크릴 에멀젼은 인장강도 개선에는 큰 효과는 없었으나 부착강도, 물흡수계수, 온냉반복저항성의 성능 개선에 효과적인 것으로 나타났다. 실리카 분산 아크릴 에멀젼은 인장강도 개선에 효과적이며, 10%의 치환율에서는 부착강도, 물흡수계수, 온냉반복저항성의 성능 개선에 효과적인 것으로 나타났다. 이를 통해 아크릴 에멀젼의 성능을 향상할 수 있는 복합 에멀젼을 제조할 수 있는 것으로 판단되었다.

Keywords

References

  1. Nakabayashi N. Hybridization of dental hard tissues pashley. Seoul (korea): Jisung publisher; 2007. Chapter 1; p. 132-3.
  2. Lee JH. Surface modification techniques for subsurface applications of nanoparticles. Polymer science and Technology. 2018 Oct;29(5):421-7.
  3. Nasretdinova GR, Fazleeva RR, Mukhitova RK, Nizameev IR, Kadirov MK, Ziganshina AY, Yanilkin VV. Electrochemical synthesis of silver nanoparticles in solution. Electrochemistry Communications. 2015 Jan;50:69-72. http://doi.org/10.1016/j.elecom.2014.11.016
  4. Ribeiro T, Baleiza C, Farinha JPS. Functional films from silica/polymer nanoparticles. Materials (Basel). 2014 May;7(5):3881-900. https://doi.org/10.3390/ma7053881
  5. Ee SL, Duan X, Liew J, Nguyen QD. Droplet size and stability of nano-emulsions produced by the temperature phase inversion method. Chemical Engineering Journal. 2008 Jul;140(1-3):626-31. http://doi.org/10.1016/j.cej.2007.12.016
  6. Chrusciel JJ, Lesniak E. Modification of epoxy resins with functional silanes, polysiloxanes, silsesquioxanes, silica and silicates. Progress in Polymer Science. 2015 Feb;41:67-121. http://doi.org/10.1016/j.progpolymsci.2014.08.001
  7. Kim WK, Kim DM. Properties of acrylic emulsion mortar using pyroligneous liquid of wood by-product. Journal of Korea Society of Waste Management. 2014 Jan;31(1):70-8. http://doi.org/10.9786/kswm.2014.31.1.70
  8. Ryu HS, Shin SH, Kim DM, Song SY. Evaluation on the properties of fire retardant surface preparation mortars. Journal of the Korea Institute of Building Construction. 2018 Dec;18(6):559-67. https://doi.org/10.5345/JKIBC.2018.18.6.559