Correction of Single Thoracic Adolescent Idiopathic Scoliosis Using Pedicle Screw Instrumentation: Comparison of Stainless Steel to Titanium Alloy Instruments

척추경 나사못 고정술을 이용한 단일 흉추 청소년기 특발성 척추 측만증의 치료: 스테인리스강과 티타늄 합금 기기의 비교

Purpose: To compare the results of two different instruments made of stainless steel and titanium alloy for correction of single thoracic adolescent idiopathic scoliosis (AIS) using pedicle screw instrumentation. Materials and Methods: A total of 141 patients with single thoracic AIS treated with pedicle screw instrumentation and selective thoracic fusion were retrospectively reviewed after a follow-up of 2 years. The patients had a main thoracic curve of 40° to 75° and were divided into two groups based on instrument materials; S group (stainless steel, n=90) and T group (titanium alloy, n=51). The diameter of the stainless steel rod used was 7.0 mm while that of the titanium alloy rod was 6.35 mm or 6.0 mm. Standing long-cassette radiographic measurements including various coronal and sagittal parameters for the preoperative, early postoperative and 2-year postoperative followup were analyzed. There were no significant differences in the preoperative curve characteristics between the two groups. Results: In the S group, the preoperative main thoracic curve of 51.3°±8.4° was improved to 19.0°±7.6° (63.1% correction) and the lumbar curve of 32.3°±8.4° spontaneously decreased to 12.7°±8.2° (62.9% correction) at 2 years postoperatively. In the T group, the preoperative main thoracic curve of 49.5°±8.4° and the lumbar curve of 30.3°±8.9° was improved to 18.8°±7.4° (62.2% correction) and 11.3°±5.4° (63.3% correction), respectively. The corrections of coronal curves were not statistically different between the two groups (p>0.05). The thoracic kyphosis was changed from 16.8°±8.5° to 24.3°±6.1° in the S group and from 19.6°±11.2° to 26.6°±8.5° in the T group. There were no significant differences in the changes of sagittal curves, coronal and sagittal balances at the 2-year follow-up and the number of fused segments and used screws between the two groups (p>0.05). Conclusion: When conducting surgery for single thoracic AIS using pedicles screw instrumentation, two different instruments made of stainless steel and titanium alloy showed similar corrections for coronal and sagittal curves.

목적: 단일 흉추 청소년기 특발성 척추 측만증의 수술적 치료로 척추경 나사못 고정술이 시행된 경우에 서로 다른 재질인 스테인레스강과 티타늄 합금 기기의 결과를 비교해 보고자 하였다. 대상 및 방법: 척추경 나사못 고정술과 선택적 흉추 유합술을 이용하여 수술을 시행하고 최소 2년 이상 추시가 가능하였던 단일 흉추 청소년기 특발성 척추 측만증 환자 141명을 후향적으로 조사하였다. 주 흉추 만곡이 40°-75°인 환자를 대상으로 하였으며, 기기의 재질에 따라 스테인레스강 기기가 사용된 경우는 S군(90명)으로, 티타늄 합금 기기가 사용된 경우는 T군(51명)으로 나누었다. S군의 강봉 직경은 7.0 mm였고 T군의 강봉 직경은 6.35 mm나 6.0 mm였다. 수술 전, 수술 직후와 술 후 2년에 촬영한 기립성 전 척추 방사선 사진을 이용하여 방사선적 측정을 시행하였다. 술 전 관상면과 시상면상 만곡의 측정값에서 두 군 간에 유의한 차이는 없었다. 결과: S군에서 술 전 51.3°±8.4°의 주 흉추 만곡은 술 후 2년에 19.0°±7.6° (63.1% 교정)로 감소되었고, 술 전 32.3°±8.4°의 요추 만곡은 술 후 2년에 12.7°±8.2° (62.9% 교정)로 감소되었다. T군에서는 술 전 49.5°±8.4°의 주 흉추 만곡과 30.3°±8.9°의 요추 만곡은 술 후 2년에 각각 18.8°±7.4° (62.2% 교정)와 11.3°±5.4° (63.3% 교정)로 감소되었다. 관상면상 만곡의 교정은 두 군 간에 통계적으로 유의한 차이는 없었다(p>0.05). 흉추 후만은 S군에서 술 전 16.8°±8.5°에서 술 후 2년에 24.3°±6.1°로, T군에서는 19.6°±11.2°에서 26.6°±8.5°로 증가되었다. 유합 분절수, 사용된 척추경 나사못의 개수 및 술 후 2년의 흉추 후만, 요추 전만, 관상면과 시상면 균형에도 두 군 간에 유의한 차이는 없었다(p>0.05). 결론: 척추경 나사못 고정술을 이용한 단일 흉추 청소년기 특발성 척추 측만증 수술에서 스테인레스강과 티타늄 합금 기기와 강봉은 관상면과 시상면에서 의미 있는 차이 없이 비슷한 교정을 보였다.