Change of Lacquer Surface by Radiation

방사선에 의한 옻칠표면의 변화

  • Yoon, Guk-joung (Devision of Fine Science and Engineering, Paichai University)
  • 윤국중 (배재대학교 정밀응용과학부)
  • Received : 2018.10.06
  • Accepted : 2018.12.05
  • Published : 2018.12.31

Abstract

Natural lacquer was cured at room temperature at a relative humidity of 60% at $27^{\circ}C$ to obtain a lacquer film. Photolysis of lacquer was investigated by irradiating 1~75 kGy of gamma ray to this lacquer film. No significant changes were observed in the range of 1~10 kGy radiation. As the radiation doses were increased, the white spots were increased in the scanning electron microscope photographs. The increase of the white dots of the lacquer surface shows that the lacquer is degradation by radiation. As a result of IR spectral analysis of the lacquer surface with increasing irradiation dose, there was no significant change in $3,445cm^{-1}$ hydroxide group, $2,900cm^{-1}$ hydrocarbon group, and $993cm^{-1}$ triene group. However, the $1,745cm^{-1}$ carbonyl group was found to increase, and the $1,715cm^{-1}$ unsaturated hydrocarbon group and the $1,463cm^{-1}$ methylene group showed a tendency to decrease.

Keywords

References

  1. 김창완, 신진용. 2013. 단파장 자외선 (254 nm)에 노출된 고밀도 폴리에틸렌 수지의 카르 보닐 지수 (CI)와 기계적 물석변화의 관계에 관한 연구. 공업화학. 24(2):138-143.
  2. 박종석, 안성준, 권희정, 정성린, 노영창, 임윤묵. 2017. 방사선에 의한 폐폴리우레탄의 분해거동. 방사선산업학회지. 11(2):101-105.
  3. 이 청 , 김기엽, 류부형, 임기조. 2003. TGA를 이용한 가교폴리에틸렌의 방사선 열화 평가. 산업안전학회지. 18(2):50-55.
  4. Allen NS and Edge M. 1992. Fundamentals of Polymer Degradation and Stabilization. Elsevier Applied Science, London and New York.
  5. Andrady AL, Torikai A and Kobatake T. 1996. Spectral sensitivity of Chitosan phtodegradation. J. Appl. Poly. Scie. 62:1465-1471. https://doi.org/10.1002/(SICI)1097-4628(19961128)62:9<1465::AID-APP16>3.0.CO;2-Y
  6. Bamji SS. 1992. Threshold voltage for electrical tree inception in underground HV transmission cables. IEEE Trans. on EI. 27(2):402-404.
  7. Hong JW, Park MY, Kim HK and Choi JO. 2000. UV-degradation chemistry of oriental lacquer coating containing hindered amine light stabilizer. Bull. Korean Chem. Soc. 21(1):61-64.
  8. Kumanotani J. 1978. Laccase-catalyzed polymerization of urushiol in precisely confined japanese lacquer system. J. Macromol. Chem. 179(1):47-61. https://doi.org/10.1002/macp.1978.021790105
  9. Kumanotani J. 1997. Durable oriental Lacquer (Urushi) A selfsurface renewable coating through effloresence in degradation of the core shell type microgel densely packed lacquer. Shikizai Kyokaishi. 70(12):818-819.
  10. Nakamura T. 1960. On the process of enzymatic oxidation of hydroquinone. Biochem. Biophysics Res. Commun. 2:111-113. https://doi.org/10.1016/0006-291X(60)90198-4
  11. Sasamori M, Egashira T and Kuwada K. 1991. Research on improving the urushi project. Ishikawaken Kogyoushi Kenjyou Kenkyuhoukoku 38:38.
  12. Snyder DM. 1989. An overview of oriental lacquer; art and chemistry of the original hightech coating. J. Chem. Educ. 66(12):977-979. https://doi.org/10.1021/ed066p977
  13. Uchida H, Fukuda T, Miyamoto H, Kawabata T, Suzuki M and Uwajima T. 2001. Polymerization of Bisphenol A by purified laccase from Trametes villosa. J. Biochem. Biophysics Res. Commun. 287:355-358. https://doi.org/10.1006/bbrc.2001.5593
  14. Umey N. 1987. Oriental lacquer. Conservation News. 32:23-25.
  15. Yoshimi K, Rong L, Teruka K, Takayuki H and Tetsuo M. 2006. Deterioration of surface of lacquer film due to ultraviolet irradiation. Surf. & Interf. Anal. 38:1311-1315. https://doi.org/10.1002/sia.2451