초록
We investigated the interfacial properties of fluorocarbon self-assembled monolayers (FC-SAMs) with different alkyl chain lengths. It was found that the substrate characteristics were changed rapidly with the fabrication time and temperature of the SAM. FC-3SAM, which has the shortest alkyl chain in this study, showed a contact angle of $54.1^{\circ}$ when it was fabricated in an electric oven at $60^{\circ}C$ for the first minute. The FC-3SAM showed a contact angle of up to $76.9^{\circ}$ when it was fabricated in an electric oven at the same temperature condition for 180 minutes. FC-10SAM, which has the longest alkyl chain in this study, showed a contact angle of $64.7^{\circ}$ when it was fabricated at a temperature condition of $60^{\circ}C$ for 1 minute, and a contact angle of $98.7^{\circ}C$ at a temperature condition of $60^{\circ}C$ for 180 minutes. It was found that the FC-10SAM shows an increased contact angle and hydrophobic properties due to a well-aligned molecular structure resulting from a strong van der Waals force. In contrast, the FC-3SAM shows a small contact angle due to the intermolecular disorder resulting from a weak van der Waals force. The average roughness of FC-SAMs was investigated using AFM. The surface roughness of FC-SAMs, which verifies the results of contact angle, was confirmed. At a fabrication time of 120 minutes, the FC-10SAM showed an improvement in average roughness by 62% compared to that of FC-3SAM due to its good alignment.