Study on the Effects of Oxidant on Chemical Passivation Treatment of Low Nickel Stainless Steel

저니켈 스테인리스강의 화학적 부동태막 형성에 산화제가 미치는 영향

  • Choi, Jong-Beom (Department of Marine Engineering, Korea Maritime and Ocean University) ;
  • Lee, Kyung-Hwang (Research Institute of Industrial Science & Technology) ;
  • Yun, Yong-Sup (Department of Marine Engineering, Korea Maritime and Ocean University)
  • 최종범 (한국해양대학교 기관시스템공학과) ;
  • 이경황 (포항산업과학연구원 소재이용연구그룹) ;
  • 윤용섭 (한국해양대학교 기관시스템공학과)
  • Received : 2018.05.18
  • Accepted : 2018.06.25
  • Published : 2018.06.30
Download PDF
⟨ Previous Next ⟩

Abstract

In this paper, effects of potassium permanganate, pottasium dichromate, sodium molybdate on lean duplex stainless steel were studied by GDOES, OCP, potentiodynamic curves. The stainless steels were chemically passivated in each nitric acid solutions containing 4wt.% oxidants for 1 hour. As a result, when potassium dichromate or sodium molybdate was added, content of Fe was decreased and content of Cr was increased. Consequently, corrosion resistance of passive film was increased. But in case of potassium permanganate was added, contrastively, content of Fe was increased and content of Cr was decreased. So corrosion resistance was decreased. Adding sodium molybdate in nitric acid for chemical surface treatment process was the most effective among oxidants and also it showed the most stable anti-corrosion in SST.

Keywords

References

  1. Seitovirta, M., Handbook of Stainless Steel. Outokumpu Oyj,.(2013).
  2. Gunn, R. N. (Ed.), Duplex stainless steels: microstructure, properties and applications. Woodhead Publishing, (1997).
  3. Winston, R. E. V. I. E, Uhlig's corrosion handbook, (2000).
  4. 장휘운, 이정훈, 김용환, & 정원섭, 화학적 부동태 처리에 따른 듀플렉스 스테인리스 강의 피막 특성에 관한 연구, 한국표면공학회지, 45(6) (2012) 219-225. https://doi.org/10.5695/JKISE.2012.45.6.219
  5. Standard, A. S. T. M, A967-01. Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts. West Conshohocken, PA: ASTM International, (2001)
  6. Marikkannu, C., Sathiyanarayanan, S., & Venkatachari, G, Studies on newer chemical passivation treatment for stainless steel. Transactions of the IMF, 83(3) (2005) 158-160. https://doi.org/10.1179/002029605X48879
  7. Shimizu, K., Habazaki, H., Skeldon, P., Thompson, G. E., & Wood, G. C, GDOES depth profiling analysis of the air?formed oxide film on a sputterdeposited Type 304 stainless steel. Surface and interface analysis, 29(11) (2000) 743-746. https://doi.org/10.1002/1096-9918(200011)29:11<743::AID-SIA921>3.0.CO;2-Q
  8. Betz, G. G. K. L. A., Wehner, G. K., Toth, L., & Joshi, A, Composition?vs?depth profiles obtained with Auger electron spectroscopy of air?oxidized stainless?steel surfaces. Journal of Applied Physics, 45(12) (1974) 5312-5316. https://doi.org/10.1063/1.1663236
  9. Uemura, M., Yamamoto, T., Fushimi, K., Aoki, Y., Shimizu, K., & Habazaki, H, Depth profile analysis of thin passive films on stainless steel by glow discharge optical emission spectroscopy. Corrosion Science, 51(7) (2009) 1554-1559. https://doi.org/10.1016/j.corsci.2008.11.017
  10. Osozawa, K., & Engell, H. J, The anodic polarization curves of iron-nickel-chromium alloys. Corrosion Science, 6(8) (1966) 389-393. https://doi.org/10.1016/S0010-938X(66)80022-7
  11. Schmuki, P., Hildebrand, H., Friedrich, A., & Virtanen, S, The composition of the boundary region of MnS inclusions in stainless steel and its relevance in triggering pitting corrosion. Corrosion Science, 47(5) (2005) 1239-1250. https://doi.org/10.1016/j.corsci.2004.05.023
  12. Ke, R., & Alkire, R, Surface analysis of corrosion pits initiated at MnS inclusions in 304 stainless steel. Journal of the Electrochemical Society, 139(6) (1992) 1573-1580. https://doi.org/10.1149/1.2069458
  13. Webb, E. G., Suter, T., & Alkire, R. C, Microelectrochemical measurements of the dissolution of single MnS inclusions, and the prediction of the critical conditions for pit initiation on stainless steel. Journal of the Electrochemical Society, 148(5) (2001) B186-B195. https://doi.org/10.1149/1.1360205