Abstract
The purpose of this study is to understand a compressive strength and propose a dry shrinkage strain equation being able to predict dry shrinkage of alkali-activated materials(AAM) mortar samples manufactured using fly-ash(FA) and ground granulated blast furnace slag(GGBFS). The main parameters investigated were the GGBFS replace ratios(30, 50, 70 and 100%) and sodium silicate modules(Ms[$SiO_2/Na_2O$] 1.0, 1.5 and 2.0). The compressive strength of AAM increased with increases GGBFS replace ratios or Ms contents. The dry shrinkage strain of AAM decreased with increases Ms contents. But, the dry shrinkage strain of AAM increased as the GGBFS replace ratio increases. Therefore, the GGBFS replace ratio seems to have very significant and important consequences for the mix design of the AAM mortar. The results indicated the R-square of single regression analysis based on each mix properties was the highest value; 0.7539~0.9786(average 0.9359). And the presumption equation of dry shrinkage strain with all variables(GGBFS, Ms and material age) has higher accuracy and its R-square was 0.8020 at initial curing temperature 23 degrees Celsius and 0.8018 at initial curuing temperature 70 degrees Celsius.
본 연구는 플라이애시 및 고로슬래그 미분말을 알칼리 활성화 결합재로 활용하여 제조한 모르타르의 압축강도 특성을 파악하고 건조수축 예측 및 평가가 가능한 추정식을 제안하고자 한다. 이를 위하여 고로슬래그 미분말 치환량을 30, 50, 70 및 100%로 조정하고 규산나트륨 모듈 Ms비[$SiO_2/Na_2O$]은 1.0, 1.5 및 2.0으로 조정하여 압축강도 및 길이변화율을 측정하였다. 그 결과 알칼리 활성화 결합재 모르타르는 Ms비가 증가할수록 압축강도는 증가하고 길이변화율은 감소하였다. 그러나 고로슬래그 미분말의 경우에는 치환량을 증가할수록 압축강도는 증가하였으나 길이변화율도 증가하는 경향이 확인되었다. 따라서, 고로슬래그 미분말을 다량 치환할 경우에는 길이변화율을 고려하여 설계할 필요성이 있다고 판단되었다. 알칼리 활성활 결합재 모르타르의 건조수축을 평가하는 식을 유도하기 위하여 배합조건별 단순회귀분석을 수행한 결과 결정계수 0.7539~0.9786(평균 0.9359)수준의 유효한 추정식을 도출하였다. 또한, 고로슬래그 미분말, Ms비 및 재령을 독립변수로 선정하여 다중회귀분석을 수행한 결과 초기양생온도 $23^{\circ}C$ 및 $70^{\circ}C$에서 결정계수 0.8020 및 0.8018 수준의 타당한 추정식을 제안하였다.