Abstract
This study examined the bending performance of high strength and seismic purpose reinforcing bars experimentally with various parameters. For the experimental approach on the bending performance, the specimens were prepared with parameters, such as steel grades, diameters of reinforcing bars, and bending angles of reinforcing bars. Tensile strength tests on the reinforcing bars, the bending tests and re-bending tests, and the second tensile strength tests on the re-bended reinforcing bars were conducted. According to the test results on high strength and seismic purpose reinforcing bars, defects did not appear when the yield strength of the reinforcing bar was 500 MPa or less and the diameter was D13 or less, even when the first bending process was performed with a $135^{\circ}$ bending angle and a $2d_b$ inner radius. The bending performance decreased asthe strength and diameter of the reinforcing bars was increased. In addition, there was no significant difference between the general reinforcing bars and seismic purpose-reinforcing bars.
본 연구는 다양한 구조적 변수에 따른 고강도 및 내진용 이형철근의 굽힘가공 성능을 실험적으로 평가하는데 그 목적이 있다. 굽힘성능에 대한 실험적 연구수행을 위해 이형철근의 강종 및 강도, 직경, 굽힘가공 각도 및 내면 반지름 등을 변수로 하여 시험체를 제작하였다. 시험은 각 변수별 원 소재 철근에 대한 1차 인장강도시험, 원 소재 철근에 대한 1차 굽힘시험과 1차 굽힘시험 철근을 대상으로 한 2차 굽힘시험 그리고 2차 굽힘시험 이후 가력이 가능한 시험체를 대상으로 한 2차 인장강도시험을 수행하였다. 금번 고강도 및 내진용 철근에 대한 실험적 연구결과 항복강도 500 MPa 및 직경 D13 이하 이형철근은 굽힘각도 $135^{\circ}$, 내면 반지름 2db의 경우에도 1차 굽힘가공 후 인장측 표면결함은 나타나지 않았으며, 이형철근의 강도와 직경이 증가할수록 굽힘가공 성능이 저하 하는 것으로 나타났다. 그리고 본 연구에서 수행된 시험에서는 일반용 철근과 특수 내진용 철근의 시험결과 비교에서 두 이형철근 간에 유의미한 구조적 성능 차이는 확인하지 못하였다.