Effect of polymerization temperature on the mechanical properties of provisional prosthesis resins

중합 온도가 임시 보철용 수지의 기계적 성질에 미치는 영향

The purpose of this study was to examine the effects of the curing sequence and polymerization temperature on the flexural strength and microhardness of two provisional resins (Bis-acryl resin composite and polymethyl methacrylate (PMMA)). Polymerization was carried out under various conditions, in air at $25^{\circ}C$ (control) and in hot water (40, 50, 60, 70, and $80^{\circ}C$). The flexural strength test was conducted according to ISO-4049. The Knoop hardness was measured. For the Bis-acryl resin, the temperature up to $50^{\circ}C$ did not increase the flexural strength nor the hardness of the bis-acryl resin composite (p>0.05) but higher temperatures increased the strengths. For the PMMA resin, flexural strength increased with temperatures up to $70^{\circ}C$ and then decreased slightly. Bis-acryl resin composite had higher mechanical properties than the PMMA resin. The effect of heat was more pronounced in the bis-acryl resin composite than in the PMMA resin (p<0.05).

본 연구의 목적은 2가지 임시 수지 (Bis-acryl resin composite 및 polymethyl methacrylate (PMMA))의 굴곡 강도 및 미세 경도에 대한 경화 순서 및 중합 온도의 영향을 조사하는 것에 있다. 중합은 대기 중 $25^{\circ}C$ (대조) 및 온수 (40, 50, 60, 70 그리고 $80^{\circ}C$)에서 다양한 조건하에 수행되었다. 굴곡 강도 시험은 ISO-4049에 따라 수행되었다. 또한, 누프 경도를 측정 하였다. Bis-acryl resin의 경우, $50^{\circ}C$까지의 온도는 굴곡 강도와 bis-acryl resin composite의 경도를 증가시키지 않았지만 (p> 0.05), 온도가 높을수록 강도가 증가 하였다. PMMA 수지의 경우 굴곡 강도는 최대 $70^{\circ}C$의 온도에서 증가하고 약간 감소합니다. Bis-acryl resin은 PMMA 수지보다 기계적 특성이 더 컸다. 열의 영향은 Bis-acryl resin에서 PMMA 수지보다 더 두드러졌다(p <0.05).