Abstract
Research and commercialization of wood chips-urethane resin mixtures as paving materials for park trails and tourist attractions are underway. The aim of this study was to expand the use of such paving materials to the playgrounds, where vigorous physical movements occur frequently. For this purpose, the physical properties and safety of the paving material, in which some or all of the wood chips(passing through a 10mm sieve and remaining in a 3mm sieve) were replaced with sawdust, were studied experimentally. Strength, elastic modulus, slip resistance, shock absorption and heavy metal content tests were carried out by varying the mixing ratio of urethane resin, sawdust and wood chip. As a result, in the case of wood chip-resin mixtures with mass ratios of the resin to total mass of sawdust and wood chips of 1.0 and 1.2 and having a ratio of sawdust mass to total mass of sawdust and wood chips of 0-0.4, it was found that the properties satisfied KS F 3888-2. On the other hand, in case of using sawdust only as a woody material, the shock absorbability was below standard, and the mass ratio of resin to sawdust required 1.2 or more to ensure the specified tensile strength.
공원 산책로 및 관광지의 포장재로서 목재 칩-우레탄 수지 혼합물의 연구 및 상업화가 진행 중에 있다. 본 연구에서는 활발한 몸동작이 일어나는 놀이터에서 이러한 포장재의 이용을 확대하기 위한 방안을 강구하고자 하였다. 이를 위해, 목재 칩 (10mm 체를 통과하고 3mm 체에 남는 것)의 일부 또는 전부를 톱밥으로 대체한 목질 포장재의 물리적 성질 및 안전성을 실험에 의해 검토하였다. 우레탄 수지, 톱밥 및 목재 칩의 혼합비를 변화시켜 인장 강도, 휨강도, 탄성계수, 미끄럼 저항성, 충격 흡수성, 중금속 함량 및 용출 시험을 실시하였다. 그 결과, 톱밥과 목재 칩의 총 질량에 대한 수지의 질량비가 1.0 및 1.2이고, 톱밥과 목재 칩의 총 질량에 대한 톱밥의 질량비가 0~0.4인 시험체의 경우, KS F 3888-2의 표준을 대체로 만족함으로써 놀이터 등에서의 이용 가능성을 확인하였다. 그러나 목질 재료로 톱밥만을 사용한 경우에는 충격 흡수성이 기준치를 밑돌고, 규정된 인장 강도를 확보하기 위해서 톱밥과 수지의 질량비는 1.2 이상을 필요로 하는 것으로 나타났다.