A study on effects of water-cement ratio and crack width on chloride ion transmission rate in concrete

  • Li, Yue (The Key Laboratory of Urban Security and Disaster Engineering, MOE, Beijing University of Technology) ;
  • Chen, Xiaohan (The Key Laboratory of Urban Security and Disaster Engineering, MOE, Beijing University of Technology) ;
  • Zhang, Guosheng (The Key Laboratory of Urban Security and Disaster Engineering, MOE, Beijing University of Technology)
  • 투고 : 2016.06.28
  • 심사 : 2017.01.06
  • 발행 : 2017.04.25

초록

To study the effects of water-cement ratio changes and cracks on chloride ion transmission rate in cracked concrete, RCM method was adopted to accelerate the diffusion of chloride ion in cracked concrete, and the changes in chloride ion concentration and around the cracks are inferred by finite-element method. The test results show that as far as prefabricated cracks on concrete components are concerned, the width thresholds of two cracks on the concrete specimens with a water-cement ratio of 0.5 and 0.6 are 0.05 mm and 0.1 mm respectively, the width threshold of two cracks on the concrete specimens with a water-cement ratio of 0.4 is 0.05 mm and 0.2 mm respectively; and the results of numerical simulation show that the smaller the water-cement ratio is, the more significant effects of cracks on chloride ion transmission rate are. As a result, more attention shall be paid to the crack prevention, repairing and strengthening for high-strength concrete.

키워드

과제정보

연구 과제 주관 기관 : National Natural Science Foundation of China, Beijing Natural Science Foundation, Beijing Municipal Institutions

참고문헌

  1. ASTM C 1218M-99 (1999), Standard Test Method for Water-Soluble Chloride in Mortar and Concrete, West Conshohocken, U.S.A.
  2. Baradaran, S.M., Yang, T.Y. and Elwood, K.J. (2013), "Seismic loss estimation of non-ductile reinforced concrete buildings", Earthq. Eng. Struct. Dyn., 42(2), 297-310. https://doi.org/10.1002/eqe.2213
  3. BS1881-124 (1988), Testing Concrete-Part 124: Method for Analysis of Hardened Concrete, London, U.K.
  4. Djerbi, A., Bonnet, S., Khelidj, A. and Baroghel-Bouny, V. (2008), "Influence of traversing crack on chloride diffusion into concrete", Cement Concrete Res., 38(6), 877-883. https://doi.org/10.1016/j.cemconres.2007.10.007
  5. Du, X.L., Jin, L., Zhang, R.B. and Li, Y. (2015), "Effect of cracks on concrete diffusivity: A meso-scale numerical study", Ocean Eng., 108, 539-551. https://doi.org/10.1016/j.oceaneng.2015.08.054
  6. GB/T 50082 (2009), Standard for Test Methods of Long-Term Performance and Durability of Ordinary Concrete, Beijing, China.
  7. GB/T 50476 (2008), Code for Durability Design of Concrete Structures, Beijing, China.
  8. Jang, S.Y., Kim, B.S. and Oh, B.H. (2011), "Effect of crack width on chloride diffusion coefficients of concrete by steady-state migration tests", Cement Concrete Res., 41(1), 9-19. https://doi.org/10.1016/j.cemconres.2010.08.018
  9. Jiang, F.X., Fu-Ru, L.I., Zhao, T.J. and Wittmann, F.H. (2011), "Study on chloride penetration into the cracked zone of reinforce concrete and effect of water repellent treatment", Concrete, 31(2), 21-24.
  10. Jin, L., Du, X.L. and Li, Y. (2016), "Study on chloride diffusivity coefficient in cracks within saturated concrete", Eng. Mech., 33(5), 50-73.
  11. Kwon, S.J., Na, U.J. Park, S.S. and Jung, S.H. (2009), "Service life prediction of concrete wharves with early-aged crack: Probabilistic approach for chloride diffusion", Struct. Safety, 31(1), 75-83. https://doi.org/10.1016/j.strusafe.2008.03.004
  12. Li, Y. and Li, J.Q. (2014), "Capillary tension theory for prediction of early autogenous shrinkage of self-consolidating concrete", Constr. Build. Mater., 53(3), 511-516. https://doi.org/10.1016/j.conbuildmat.2013.12.010
  13. Marsavina, L., Audenaert, K., De Schutter, G., Faur, N. and Marsavina, D. (2009), "Experimental and numerical determination of the chloride penetration in cracked concrete", Constr. Build. Mater., 23(1), 264-274. https://doi.org/10.1016/j.conbuildmat.2007.12.015
  14. McGrath, P.F. and Hooton, R.D. (1996), "Influence of voltage on chloride diffusion coefficients from chloride migration tests", Cement Concrete Res., 26(8), 1239-1244. https://doi.org/10.1016/0008-8846(96)00094-4
  15. Nilenius, F., Larsson, F., Lundgren, K. and Runesson, K. (2015), "Mesoscale modelling of crack-induced diffusivity in concrete", Comput. Mech., 55(2), 359-370. https://doi.org/10.1007/s00466-014-1105-2
  16. Oh, B.H. and Jang, S.Y. (2004), "Prediction of diffusivity of concrete based on simple analytic equations", Cement Concrete Res., 34(3), 463-480. https://doi.org/10.1016/j.cemconres.2003.08.026
  17. Park, S.S., Kwon, S.J. and Jung, S.H. (2012), "Analysis technique for chloride penetration in cracked concrete using equivalent diffusion and permeation", Constr. Build. Mater., 29(4), 183-192. https://doi.org/10.1016/j.conbuildmat.2011.09.019
  18. Picandet, V., Khelidj, A. and Bellegou, H. (2009), "Crack effects on gas and water permeability of concretes", Cement Concrete Res., 39(6), 537-547. https://doi.org/10.1016/j.cemconres.2009.03.009
  19. Pijaudier-Cabot, G., Dufour, F. and Choinska, M. (2009), "Permeability due to the increase of damage in concrete: From diffuse to localized damage distributions", J. Eng. Mech., 135(9), 1022-1028. https://doi.org/10.1061/(ASCE)EM.1943-7889.0000016
  20. Poursaee, A. and Hansson, C.M. (2008), "The influence of longitudinal cracks on the corrosion protection afforded reinforcing steel in high performance concrete", Cement Concrete Res., 38(8), 1098-1105. https://doi.org/10.1016/j.cemconres.2008.03.018
  21. Sahmaran, M. (2007), "Effect of flexure induced transverse crack and self-healing on chloride diffusivity of reinforced mortar", J. Mater. Sci., 42(22), 9131-9136. https://doi.org/10.1007/s10853-007-1932-z
  22. Sangoju, B., Gettu, R., Bharatkumar, B.H. and Neelamegam, M. (2011), "Chloride-induced corrosion of steel in cracked OPC and PPC concretes: Experimental study", J. Mater. Civil Eng., 23(7), 1057-1066. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000260
  23. Song, Z., Jiang, L. and Zhang, Z. (2016), "Chloride diffusion in concrete associated with single, dual and multi cation types", Comput. Concrete, 17(1), 53-66. https://doi.org/10.12989/cac.2016.17.1.053
  24. Sun, G.W., Zhang, Y.S., Sun, W., Liu, Z.Y. and Wang, C.H. (2011), "Multi-scale prediction of the effective chloride diffusion coefficient of concrete", Constr. Build. Mater., 25(10), 3820-3831. https://doi.org/10.1016/j.conbuildmat.2011.03.041
  25. Tsao, W.H., Huang, N.M. and Liang, M.T. (2015), "Modelling of chloride diffusion in saturated concrete", Comput. Concrete, 15(1), 127-140. https://doi.org/10.12989/cac.2015.15.1.127
  26. Win, P.P., Watanabe, M. and Machida, A. (2004), "Penetration profile of chloride ion in cracked reinforced concrete", Cement Concrete Res., 34(7), 1073-1079. https://doi.org/10.1016/j.cemconres.2003.11.020
  27. Xie, Y.J., Liu, B.J. and Liu, W. (2004), "Influence of mineral admixture on resistance to penetration of chloride ions into concrete", J. Rail. Sci. Eng., 1(2), 46-51.
  28. Ye, H.L. (2013), "The research of concrete crack on the chloride ingress and moisture influencing depth", M.S. Dissertation, Zhejiang University, China.
  29. Zhang, S.F., Lu, C.H. and Liu, R.G. (2011), "Experimental determination of chloride penetration in cracked concrete beams", Proc. Eng., 24(8), 380-384. https://doi.org/10.1016/j.proeng.2011.11.2661
  30. Zhao, Y.X., Wang, C.K., Jin, W.L. and Xu, C. (2010), "Experimental analysis on time-dependent law of surface chloride ion concentration of concrete", J. Civil Architect. Environ. Eng., 32(3), 8-13.
  31. Zhou, Y., Hou, D.S., Jiang, J.Y. and Wang, P.G. (2016), "Chloride ions transport and adsorption in the nano-pores of silicate calcium hydrate: Experimental and molecular dynamics studies", Constr. Build. Mater., 126, 991-1001. https://doi.org/10.1016/j.conbuildmat.2016.09.110
  32. Zhuang, Q.C. (2010), "Influences of cracks on durability of marine concrete", M.S. Dissertation, Qingdao University of Technology, China.

피인용 문헌

  1. The Chloride Ion Penetration Mechanism in Basalt Fiber Reinforced Concrete under Compression after Elevated Temperatures vol.11, pp.21, 2021, https://doi.org/10.3390/app112110137