Abstract
In the automobile industry, there is growing demand for lightweight vehicles due to environmental problems and rising oil prices. Therefore, aluminum alloys and special materials are being used to reduce the weight of vehicles, but there are still many difficulties to overcome in terms of cost and strength. Therefore, the application of advanced high strength steel (AHSS)is increasing. AHSS has good strength and formability.Safety regulations are becoming stricter, and 1.2-GPa super-high-strength steels are gradually being applied for the center pillar and roof rails. Thus, the application of different kinds of steels in automobile bodiesis also increasing gradually. This study evaluates the resistance point weldability and the characteristics of a welded part of SGAFC1180 1.2t steel. A simulation was used to observe the nugget formation and its growth behavior. The prediction performance showed a similar tendency within an error rate of 10%. Also, the effect of this behavior on the process resistance and dynamic resistance was investigated,along with the correlation between the shear tensile strength and nugget diameter.
자동차 산업에서는 환경 문제와 국제 유가 상승 등으로 인한 차량 경량화에 대한 요구가 증대되고 있다. 이에 따라 알루미늄 합금과 특수 소재 등이 차량 중량을 줄이는데 활용되고 있지만 비용과 강도 측면에서 철강소재를 극복하기 에는 여전히 많은 어려움이 있다. 따라서 강도와 성형성이 좋은 AHSS(Advanced High Strength Steel) 소재의 적용이 증가하고 있다. 특히 운전자 보호를 위한 안전 규제가 강화되면서 센터필러 (Center Pillar), 루프레일 (Roof Rail) 부분에 1.2GPa급 초고강도 강재의 적용이 점차 늘어나고 있으며 이종강재에 대한 자동차 차체 적용 또한 점차 증가하고 있다. 본 연구에서는 SGAFC1180 1.2t 강재의 저항 점용접성 및 용접부의 특성을 파악하였다. 시뮬레이션을 이용하여 너깃의 생성 및 성장 거동을 관찰하였으며 예측 성능은 오차율 10% 이내에서 유사한 경향을 나타내었다. 또한 이러한 거동이 공정변수인 동저항에 미치는 영향을 파악하였고 전단인장강도 및 너깃 직경과의 상관관계를 고찰하였다. 본 연구를 통하여 동저항의 패턴을 인식하여 패턴의 형태에 따라 용접 상태를 분류하고 용접 품질을 판단하는 시스템도 제안할 수 있을 것으로 사료된다.