Abstract
This study is to develop high quality floor mortar which can be applied in construction sites using EXFG(Expansive admixdure Flue Gas desulfurization gypsum). First, as the substitution rate of ALS(Aluminum Slag) increased, the flow is increased proportionally. EXFG showed a tendency to decrease with increasing substitution rate. Also, in the case of the setting time of 5% of ALS replacement rate, the setting time of Plain compared to EXFG was decreased by 5~20%. The compressive strength increased with the ALS replacement ratio at 0%, 5% and the EXFG replacement ratio at 1%. The strength was increased when the ALS replacement ratio was more than 10%. In the case of ALS replacement rate of 0% and 5%, drying shrinkage compared to plain was decreased by about 10~25% regardless of EXFG replacement rate.
본 연구에서는 EXFG를 활용하여 실제 현장 적용이 가능한 고품질의 바닥모르타르를 개발하고자 하였는데, 그 결과를 요약하면 다음과 같다. 먼저, ALS의 치환율이 증가할수록 플로치도 비례하게 증가하는 것으로 나타났으며, 이를 이용한 EXFG의 경우 반대로 치환율이 증가할수록 유동성은 감소하는 경향을 나타냈다. 또한, 응결시간의 경우 ALS 치환율이 5%인 배합에서는 EXFG의 치환율에 관계없이 Plain 대비 응결시간이 약 5~20% 이상 단축되는 것으로 나타났다. 압축강도의 경우 ALS 치환율 0%, 5%에서 EXFG 치환율이 1% 이내일 때 전반적으로 강도는 증가하였으며, ALS 치환율이 10% 이상일 경우에는 오히려 강도가 저하 되는 것으로 나타났다. 건초수축길이변화율의 경우 ALS 치환율 0%, 5%에서는 EXFG 치환율에 관계없이 Plain 대비 건조수축길이변화율이 약 10~25% 이상 감소하는 것으로 나타났다.