Photoluminescence Characteristics of the Light-Emitting Chromophores Obtained from Organic-Inorganic Hybrid Silica Spheres

  • 투고 : 2016.07.21
  • 심사 : 2016.08.28
  • 발행 : 2016.09.30

초록

Light-emitting chromophores have been separated from silica spheres modified the surface with 3-(trimethoxysilyl)propylmethacrylate (TMSPM). The photoluminescence characteristics of the chromophores were investigated with various excitation wavelengths. The TMSPM was attached to the surface of silica spheres at $75^{\circ}C$. Large number of round shaped particles of the TMSPM was on the surface of silica spheres after 3 h reaction. The TMPSM was completely covered on the surface of the spheres after 6 h reaction. The surface modified silica spheres were soaked into acetone and stored for 20 days at ambient condition. The solution color slowly changed from light yellow to deep yellow with the increase of the storing time. The FTIR absorption peaks at 3348, 2869, 2927, 1715, 1453/1377, 1296, and $1120cm^{-1}$ represent C-OH, $R-CH_3$, $R_2-CH_2$, -C=O, C-H, C=C-H, and Si-O-Si absorption, respectively. The FTIR absorption peak at $1715cm^{-1}$ representing the ester -C=O stretching vibration for silica spheres stored for 20 days was increased compared with the spheres without aging. The UV-visible absorption peaks were at 4.51 eV (275 nm) and 3.91 eV (317 nm). There were two luminescence peaks at 2.51 eV (495 nm) and 2.25 eV (550 nm). The emission at 2.51 eV was dominant peak when the excitation energy was higher than 2.58 eV, and emission at 2.25 eV became dominant peak when the excitation energy was lower than 2.58 eV.

키워드

참고문헌

  1. H. Liu, Z. Huang, J. Huang, S. Xu, M. Fang, Y. Liu, X. Wu, and Zhang, S. "Morphology controlling method for amorphous silica nanoparticles and jellyfish-like nanowires and their luminescence properties," Scientific Reports, 6:22459, 2016. https://doi.org/10.1038/srep22459
  2. A. Y. Karlash, Y. E. Zakharko, V. A. Skryshevsky, A. I. Tsiganova and G. V. Kuznetsov, "Photoluminescence properties of silica aerogel/porous silicon nanocomposites," J Phys: D Appl Phys, 43:335405, 2010. https://doi.org/10.1088/0022-3727/43/33/335405
  3. L. Spallino, L. Vaccaro, S. Agnello and M. Cannas, "Effects induced by UV laser radiation on the blue luminescence of silica nanoparticles," J. Luminescence, 138:39-43, 2013. https://doi.org/10.1016/j.jlumin.2013.01.027
  4. A. Anjiki and T. Uchino, "Visible photoluminescence from photoinduced molecular species in nanometer-sized oxides: crystalline $Al_2O_3$ and amorphous $SiO_2$ nanoparticles," J Phys Chem C, 116:15747-55, 2012. https://doi.org/10.1021/jp303359v
  5. A. G. Cullis, L. T. Canham and P. D. J. Calcott., J. App. Phys, 82:909, 1997. https://doi.org/10.1063/1.366536
  6. B. Hamilton, Porous silicon. Semicond Sci Technol, 10:1187, 1995. https://doi.org/10.1088/0268-1242/10/9/001
  7. J. Lin and K. Baerner, "Tunable photoluminescence in sol-gel derived silica xerogels," Mater Lett, 46:86-92, 2000. https://doi.org/10.1016/S0167-577X(00)00147-6
  8. B. Gao, J. Xu, K. He, L. Shen, H. Chen, H. Yang, A. Li and W. Xiao, "Cellular uptake and intra-organ biodistribution of functionalized silica-coated gold nanorods," Molecular Imaging and Biology, 12:1-10, 2016.
  9. L. Vaccaro, A. Morana, V. Radzig and M. Cannas, "Bright visible luminescence in silica nanoparticles," J Phys Chem C, 115:19476-81, 2011. https://doi.org/10.1021/jp204350u
  10. S. Yang, W. Li, B. Cao, H. Zeng and W. Cai, "Origin of blue emission from silicon nanoparticles: direct transition and interface recombination," J. Phys. Chem. C, 115:21056-62, 2011. https://doi.org/10.1021/jp2075836
  11. S. Kar and S. Chaudhuri, "Catalytic and non-catalytic growth of amorphous silica nanowires and their photoluminescence properties," Solid State Commun, 133:151-55, 2005. https://doi.org/10.1016/j.ssc.2004.10.026
  12. L. Dai, X. L. Chen, J. K. Jian, W. J. Wang, T. Zhou and B. Q. Hu, "Strong blue photoluminescence from aligned silica nanofibers," Appl. Phys. A, Mater. Sci. Process, 76:625-27, 2003. https://doi.org/10.1007/s00339-002-2024-1
  13. K. S. Kang, "Separation of photoluminescence fragment from the silica spheres modified the surface with 3-mercaptopropyltrimethoxysilane," J. Luminescence, 146:83-86, 2014. https://doi.org/10.1016/j.jlumin.2013.09.055
  14. H. Nishikawa, T. Shiroyama, R. Nakamura, Y. Ohki, K. Nagasawa and Y. Hama, "Photoluminescence from defect centers in high-purity silica glasses observed under 7.9-eV excitation," Phys. Rev. B, 45:586-91, 1992. https://doi.org/10.1103/PhysRevB.45.586
  15. J. Garcia, M. A. Mondragon, C. Tellez, S. A. Campero and V. M. Castano, "Blue emission in tetraethoxysilane and silica gels," Mater. Chem. Phys, 41:15-17, 1995. https://doi.org/10.1016/0254-0584(95)01498-5
  16. X. C. Wu, W. H. Song, K. Y. Wang, T. Hu, B. Zhao, Y. P. Sun and J. J. Du, "Preparation and photoluminescence properties of amorphous silica nanowires," Chem. Phys. Lett, 336:53-56, 2001. https://doi.org/10.1016/S0009-2614(01)00063-X
  17. A. Anedda, C. M. Carbonaro, F. Clemente, R. Corpino and P. C. Ricci, "Mesoporous silica photoluminescence properties in samples with different pore size," Mater. Sci. Eng. C, 23:1073-76, 2003. https://doi.org/10.1016/j.msec.2003.09.077
  18. S. H. Li, X. F. Zhu and Y. P. Zhao, "Carbon-assisted growth of $SiO_x$ nanowires," J. Phys. Chem. B, 108:17032-41, 2004. https://doi.org/10.1021/jp048418x
  19. J. J. Wu, T. C. Wong and C. C. Yu, "Growth and characterization of well-aligned nc-Si/$SiO_x$ composite nanowires," Adv. Mater, 14:1643-46, 2002. https://doi.org/10.1002/1521-4095(20021118)14:22<1643::AID-ADMA1643>3.0.CO;2-Y
  20. J. C. Wang, C. Z. Zhan and F. G. Li, "The synthesis of silica nanowire arrays," Solid State Commun, 125:629-31, 2003. https://doi.org/10.1016/S0038-1098(03)00034-6
  21. L. Spallino, L. Vaccaro, S. Agnello and Cannas, M., "Effects induced by UV laserradiation on the blue luminescence of silica nanoparticles," 2013 J. Luminescence, 138:39-43, 2013. https://doi.org/10.1016/j.jlumin.2013.01.027
  22. J. Lin and Baerner, K. "Tunable photoluminescence in sol-gel derived silica xerogels," Mater. Lett, 46:86-92, 2000. https://doi.org/10.1016/S0167-577X(00)00147-6