Abstract
In this study, the replacement effects of cementitious materials (fly ash, blast furnace slag, and blended mixtures) were assessed for normal strength concrete with very low shrinkage properties under $350{\mu}{\varepsilon}$ strain using a powder type shrinkage reducing agent. In addition, through mock-up tests of actual size walls restrained with four sides, the shrinkage characteristics using the power type shrinkage reducing agent were measured and the crack reducing ability was assessed. The slump and air contents were measured as the properties of fresh concrete, and the length changes of the prismatic specimens, $100{\times}100{\times}400mm$ in size, were measured for the shrinkage characteristics. To reduce the shrinkage of concrete, the maximum replacing ratio of the fly ash is effective to 20 percent; however, the use of blast furnace slag and ternary mixtures did not reduce the shrinkage.
본 연구는 분말형 수축저감제를 이용하여 일반 강도를 갖는 콘크리트에서 $350{\mu}{\varepsilon}$ 이하의 초수축 특성을 얻게 하는데 필요한 결합재의 치환률을 평가하였다. 또한 이를 바탕으로 4변지지 구속된 조건에서 실대형 벽체를 통해 분말형 수축 저감제의 첨가 유무에 따른 수축 특성을 측정하고 균열저감 특성을 평가하였다. 콘크리트의 기초 물성은 슬럼프와 공기량을 측정하였으며, 수축 특성은 길이 변화를 측정하여 평가하였다. 수축 저감을 위해 최대 플라이애시는 20%까지 유효하였으며, 고로슬래그를 사용하거나 3성분계로 치환하는 경우 수축 특성에 불리한 것으로 평가되었다. 플라이애시와 고로슬래그 및 3성분계 바인더 비율에 따른 일반 강도 콘크리트의 건조수축 길이 변화 특성에 영향을 주는 인자의 특성을 분석하고, 도출된 배합에 대해 분말형 수축저감제를 적용하여 그 균열 계측 결과를 통해 그 유효성을 검증 연구를 수행하였다. 또한 도출된 배합에 적용된 수축저감 콘크리트의 특성은 넣지 않은 경우에 비하여 약 60% 수준으로서 $350{\mu}{\varepsilon}$ 이하의 수축저감 특성을 보였다. 4변지지 구속 조건을 고려한 수축균열 유도실험을 통해 기존의 배합대비 균열발생 저감 효과를 검증하였다.