선체 구조용 강재에 대한 Al과 Zn 아크용사코팅 층의 캐비테이션 손상 특성

Cavitation Damage Characteristics of Al and Zn Arc Thermal Spray Coating Layers for Hull Structural Steel

  • 박일초 (목포해양대학교 기관시스템공학부) ;
  • 김성종 (목포해양대학교 기관시스템공학부)
  • Park, Il-Cho (Division of Marine Engineering, Mokpo National Maritime University) ;
  • Kim, Seong-Jong (Division of Marine Engineering, Mokpo National Maritime University)
  • 투고 : 2016.02.16
  • 심사 : 2016.02.28
  • 발행 : 2016.02.29

초록

In this study, Al and Zn arc thermal spray coatings were carried out onto the substrate of SS400 steel to improve corrosion resistance and durability of hull structural steel for ship in marine environment. Therefore cavitation-erosion test was conducted to evaluate the durability of painted and thermal spray coated specimens. And then the damaged surface morphology and weight loss were obtained to compare with each other, respectively. As a result, the painted specimen was the poorest cavitation resistance characteristics because surface damage behavior appeared to be exfoliated in bulk shape during the cavitation experiment. And Zn thermal spray coating layer presented the significant surface damage depth due to relatively low surface hardness and local cavitation damage tendency. On the other hand, as a result of the weight loss analysis, the painting layer presented the poorest cavitation resistance and the Al thermal spray coating layer relatively showed the best results after cavitation experiment.

키워드

참고문헌

  1. G. S. Kim, C. H. Hyun, H. S. Jin, A Study on Cavitation Erosion of Al and Zn Coating by Thermal Spray Method, J. Res. Inst. Adv. Tech., 14 (2003) 45-51.
  2. H. I. Lee, M. S. Han, K. K. Baek, C. H. Shin, M. K. Chung, Study on New Candidate Coating Materials to Challenge Rudder Cavitation Damage, Corros. Sci. Technol., 7 (2008) 274-282.
  3. S. M. Hong, M. K. Lee, G. H. Kim, K. H. Kim, W. W. Kim, S. I. Hong, Improvement of the Resistance to Cavitation Erosion by the Formation of ${\beta}^{\prime}$ Martensite in Flame-Quenched Cu-9AI-4.5Ni-4.5Fe Alloys, J. Kor. Inst. Surf. Eng., 37 (2004) 234-241.
  4. U. J. Im, J. Y. Lee, A Study on the Behaviour of Erosion-Corrosion at the Bearing Metals by Cavitation (2) - for Influence of Sea Water at Marine Lubricating Oil -, J. Corros. Sci. Soc. of Korea, 22 (1993) 176-182.
  5. J. H. Shin, K. M. Moon, An Electrochemical Evaluation on the Corrosion Property of Metallizing Film, Corros. Sci. Technol., 9 (2010) 325-330.
  6. G. Jandin, H. Liao, Z. Q. Feng, C. Coddet, Correlations Between Operating Conditions, Microstructure and Mechanical Properties of Twin Wire Arc Sprayed Steel Coatings, Mater. Sci. Eng. A, 349 (2003) 298-305. https://doi.org/10.1016/S0921-5093(02)00767-0
  7. W. M. Zhao, Y. Wang, C. Liu, L. X. Dong, H. H. Yu, H. Ai, Erosion-Corrosion of Thermally Sprayed Coatings in Simulated Splash Zone, Surf. Coat. Tech., 205 (2010) 2267-2272. https://doi.org/10.1016/j.surfcoat.2010.09.011
  8. F. Ahnia, B. Demri, Evaluation of Aluminum Coatings in Simulated Marine Environment, Surf. Coat. Tech., 220 (2013) 232-236. https://doi.org/10.1016/j.surfcoat.2012.12.011
  9. G. Hou, X. Zhao, H. Zhou, J. Lu, Y. An, J. Chen, J. Yang, Cavitation Erosion of Several Oxy-fuel Sprayed Coatings Tested in Deionized Water and Artificial Seawater, Wear, 311 (2014) 81-92. https://doi.org/10.1016/j.wear.2013.12.026
  10. A. Amirudin, D. Thierry, Application of Electrochemical Impedance Spectroscopy to Study the Degradation of Polymer-Coated Metals, J. Prog. Org. Coat., 26 (1995) 1-28. https://doi.org/10.1016/0300-9440(95)00581-1
  11. G. R. Kim, S. H. Lee, H. Y. Song, J. M. Han, Electrochemical Characterization of Epoxy Coated Steel under Cathodic Protection, J. Corros. Prot., 5 (2006) 52-58.
  12. S. J. Kim, S. J. Lee, Effects of F−Si Sealer on Electrochemical Characteristics of 15%Al−85%Zn Alloy Thermal Spray Coating, J. Trans. Nonferrous Met. Soc. China., 21 (2011) 2798-2804. https://doi.org/10.1016/S1003-6326(11)61126-6
  13. Y. Q. Zhang, Z. X. Ding, Y. Fan, Performance Study of Nano Structured WC-Co Coatings Sprayed by HVOF, J. China Surf. Eng., 18 (2005) 25-29.
  14. K. M. Moon, J. H. Shin, M. H. Lee, S. Y. Lee, Y. H. Kim, An Electrochemical Evaluation on the Corrosion Property of Metallizing Film, J. Korean Soc. Mar. Eng., 34 (2010) 670-677. https://doi.org/10.5916/jkosme.2010.34.5.670
  15. C. T. Kwok, F. T. Cheng, H. C. Man, Laser Surface Modification of UNS S31603 Stainless Steel. Part II: Cavitation Erosion Characteristics, J. Mater. Sci. & Eng. Struct. Mater., 290 (2000) 74-88. https://doi.org/10.1016/S0921-5093(00)00930-8
  16. D. S. Won, K. S. Jeon, Y. T. Hho, J. H. Lee, Cavitation Behavior of A 5083 Alloy by Vibratory Cavitation Tester, J. Corros. Sci. Soc. of Korea, 23 (1994) 215-225.
  17. J. F. Santa, J. C. Baena, A. Toro, Slurry Erosion of Thermal Spray Coatings and Stainless Steels for Hydraulic Machinery, Wear, 263 (2007) 258-264. https://doi.org/10.1016/j.wear.2006.12.061
  18. C. E. Correaa, G. L. Garcia, A. N. Garcia, W. Bejarano, A. A. Guzman, A. Toro, Wear Mechanisms of Epoxy-Based Composite Coatings Submitted to Cavitation, Wear, 271 (2011) 2274-2279. https://doi.org/10.1016/j.wear.2011.01.088
  19. K. J. Kim, D. S. Kim, A Study on the Cavitation Erosion of Polymeric Materials, Korean Chem. Eng. Res., 32 (1984) 72-78.
  20. L. A. Espitia, A. Toro, Cavitation Resistance, Microstructure and Surface Topography of Materials Used for Hydraulic Components, J. Tribol. Int., 43 (2010) 2037-2045. https://doi.org/10.1016/j.triboint.2010.05.009
  21. P. V. Rao, Evaluation of Epoxy Resins in Flow Cavitation Erosion, Wear, 122 (1988) 77-96. https://doi.org/10.1016/0043-1648(88)90008-7
  22. S. J. Lee, S. J. Kim, Evaluation of Cavitation Characteristics for ALBC3 Alloy Coated with Ni-Cr Series Self Fluxing Alloy in Marine Environment, J. Korean Soc. Mar. Environ. Saf., 19 (2013) 538-544. https://doi.org/10.7837/kosomes.2013.19.5.538