Abstract
Raw sap of essential oil in Korean Dendropanax lacquer was extracted with ethanol, and which was cured by using ROMP (ring opening metathesis polymerization, one of olefin metathesis). Curing behavior with subsequent film properties were studied and compared with conventional curing (under ambient conditions) and UV photo curing. The compositional changes of major ingredients in the lacquer before and after curing were studied by using GC-MS (gas chromatography mass spectrometry). ROMP-cured coating film showed higher gel contents (40%) as compared to those of conventional (8%) and UV curing (25%). ROMP curing with 2 wt% Grubbs' catalyst at $100^{\circ}C$ completed curing reaction within 2 h, which was much faster than that of conventional curing. The quality of coating film prepared with ROMP was more homogeneous and wrinkle-free as compared with that with UV curing. It was found that major ingredients of sesquiterpenes, such as ${\alpha}$-selinene, ${\beta}$-selinene, and ${\delta}$-cadinene were reacted in ROMP, as well as polyacetylenes.
황칠원액을 에탄올로 추출한 황칠의 essential oil을 올레핀 메타테시스(olefin metathesis) 반응의 하나인 ROMP(ring opening metathesis polymerization)법을 이용하여 경화 반응을 수행하였으며, 자연 경화 및 UV 광경화법의 경화 특성 및 경화된 필름의 물성에 대해서 비교 연구하였다. 경화 전후의 황칠의 조성 변화에 대해서 가스 크로마토그래피 질량분석법(GC-MS, gas chromatography mass spectrometry)을 통해 연구하였으며, ROMP법에 의해 경화된 필름의 겔 함량(gel contents, 40%)은 자연 경화(8%)나 UV 광경화법(25%)에 비해 높은 값을 보여주었다. $100^{\circ}C$의 온도 및 2 wt%의 Grubbs' catalyst 조건에서 ROMP 경화반응은 2 h 이내의 경화 반응이 완료되어 자연 경화에 비해 비교적 빠른 경화 속도를 보여주었으며, UV 광경화법에 비해 주름이 없으며 외관상 균일한 도막이 형성됨을 확인하였다. 또한 기존에 경화반응에 참여하는 것으로 알려져 있는 폴리아세틸렌계 성분 이외에 sesquiterpene류인 ${\alpha}$-selinene, ${\beta}$-selinene, ${\delta}$-cadinene 등도 ROMP 경화 반응에 참여함을 확인하였다.