Abstract
This study is to be investigate properties of workability, compacting and compressive strength replaced by the illite powder in high fluidity concrete. For this purpose, illite powder has replaced the binder of high fluidity concrete of 5%, 10%, 15%, 20%. After concrete mixing, slump flow test, reach time slump flow 500mm, O-lot test were conducted on fresh high fluidity concrete. And compressive strength was determined 28 days for the hardened high fluidity concrete specimens. According to the test results, the workability, filling height of high fluidity concrete were increased in 10% replacement of illite powder. Furthermore, the compressive strength of high fluidity concrete was increased in 10% replacement of illite powder.. It was possible to confirm that optimal mixture ratio of illite powder seems to exist, and it is shown to be 10% according to our experimental results.
본 연구에서는 고유동 콘크리트에서 일라이트 미분말을 대체한 콘크리트의 유동성과 충전성 및 압축강도 특성을 조사하기 위한 것이다. 이러한 목적으로 일라이트 미분말을 고유동 콘크리트에 5, 10, 15, 20%를 대체한 후 치환율에 따른 콘크리트의 특성을 알아보았다. 콘크리트 배합 후 굳지않은 콘크리트에서 슬럼프 플로우 시험, 500mm플로우 도달시간 및 O-lot 시험을 실시하였으며, 굳은 콘크리트의 특성으로 재령 28일에 고유동 콘크리트의 압축강도를 측정하였다. 시험결과 고유동 콘크리트의 유동성 및 충전 높이는 일라이트 미분말 10%를 대체하였을 때까지 증가하는 것으로 나타났다. 그리고 고유동 콘크리트의 압축강도 특성을 살펴본 결과에서도 일라이트 미분말 10%를 대체하였을 때까지 강도증진이 발생하였다. 따라서 본 실험결과 일라이트 미분말의 혼입율이 10%일 때 최적 치환율이 되었음을 확인할 수 있었다.