Abstract
In this study, Fe-based bulk amorphous alloy powder manufactured using gas atomization fabrication was used for laser welding. the fracture behavior of welding layer were analyzed. Tensile test results show that the destruction occurred immediately after the elastic deformation, After plastic deformation of the substrate, the destruction occurred. The actual maximum tensile strength of the welding layer and the substrate are 959.9MPa and 220.4MPa. welding layer were each $485.5{\pm}21$ and $197.4{\pm}14$ to the substrate and the actual microhardness, The welding layer has very high hardness. The welding layer showed a very weak fine acicular structure. The base material was shown in the micro structure appear a coarse grain. SEM observations of the fracture after the tensile test. Fracture morphology of the base metal and the welding layer showed ductile fracture and brittle fracture, respectively.
본 연구에서는 가스아토마이저로 제조된 Fe계 벌크비정질 합금 분말을 이용하여 제작된 시험편에 레이저 육성용접을 하였고, 인장시험과 경도시험의 실시 및 미세조직을 관찰하여 육성용접 층의 파괴거동을 분석하였다. 인장시험 결과 육성용접층은 탄성변형 후 바로 파괴가 일어났고, 모재는 소성변형 후 파괴가 일어났다. 육성용접층과 모재의 실제 최대인장강도는 각 각 955.9Mpa과 220.4Mpa이다. 육성용접층과 모재의 미소경도는 각 각 $485.5{\pm}21$과 $197.4{\pm}14$ 이었고, 육성용접층은 매우 높은 경도를 갖는다. 모재는 조대한 결정립을 갖는 미세 구조를 나타내었다. 인장시험 후 파단면을 고분해능주사전자현미경으로 관찰한 결과 육성용접층과 모재의 파괴형태는 각각 취성파괴와 연성파괴를 나타내었다.