Deformation Property of TiC-Mo Solid Solution Single Crystal at High Temperature by Compression Test

TiC-Mo 고용체 단결정의 고온 압축변형 특성

  • Shin, Soon-Gi (Department of Advanced Materials Engineering, College of Samcheok, Kangwon National University)
  • 신순기 (강원대학교 신소재공학과)
  • Received : 2014.08.27
  • Accepted : 2014.10.13
  • Published : 2014.11.27

Abstract

To investigate the deformation properties of TiC-(5-20) mol% Mo solid solution single crystals at high temperature by compression testing, single crystals of various compositions were grown by the radio frequency floating zone technique and were deformed by compression at temperature from 1250K to 2270K at strain rates from $5.1{\times}10^{-5}$ to $5.9{\times}10^{-3}/s$. The plastic flow property of solid solution single crystals was found to be clearly different among a three-temperature range (low, intermediate and high temperature ranges) whose boundaries were dependent on the strain rate. From the observed property, we conclude that the deformation in the low temperature range is controlled by the Peierls mechanism, in the intermediate temperature range by the dynamic strain aging and in the high temperature range by the solute atmosphere dragging mechanism. The work softening tends to become less evident with an increasing experimental temperature and with a decreasing strain rate. The temperature and strain rate dependence of the critical resolved shear stress is the strongest in the high temperature range. The curves are divided into three parts with different slopes by a transition temperature. The critical resolved shear stress (${\tau}_{0.2}$) at the high temperature range showed that Mo content dependence of ${\tau}_{0.2}$ with temperature and the dependence is very marked at lower temperature. In the higher temperature range, ${\tau}_{0.2}$ increases monotonously with an increasing Mo content.

Keywords

References

  1. H. Suzuki and K. Hayashi, Cemented Carbide and Sintered Hard Materials (Basic and Application) (ed. H. Suzuki), p.75, Maruzen Co, Tokyo, (1986).
  2. K. Hara, H. Yoshinaga and S. Morozumi, J. Japan Inst. Metals, 42, 1039 (1978).
  3. H. Kurishita, K. Nakajima and H, Yoshinaga, Master. Sci. Eng., 54, 177 (1982). https://doi.org/10.1016/0025-5416(82)90112-4
  4. G. Das, K. S. Mazdiyasni and H. A. Lipsitt, J. Am. Ceram. Soc., 65, 104 (1982). https://doi.org/10.1111/j.1151-2916.1982.tb10366.x
  5. D. B. Miracle and H. A. Lipsitt, J. Am. Ceram. Soc., 66, 592 (1983). https://doi.org/10.1111/j.1151-2916.1983.tb10098.x
  6. H. Kurishita and H. Yoshinaga, Creep and Fracture of Engineering Materials and Structures (ed. B. Wilshire and D. R .Owen), p.503, Pineridge Press, (1984).
  7. W. S. Williams and R. D. Schaal, J. Appl. Phys., 33, 955 (1962). https://doi.org/10.1063/1.1777197
  8. J. B. Venables, Phil. Mag., 16, 873 (1967). https://doi.org/10.1080/14786436708229681
  9. G. E. Hollox, Master. Sci. Eng., 3, 121 (1969).
  10. S. G. Shin, Korean J. Met. Mater. Int., 48, 825 (2010).
  11. S. G. Shin, Kor. J. Mater. Res., 23(10), 568 (2013). https://doi.org/10.3740/MRSK.2013.23.10.568
  12. C. H. Pai, Korean J. Met. Mater., 50, 839 (2012).
  13. R. Horiuchi and H. Yoshinaga, Trans. JIM, 6, 131 (1965).
  14. H. Oikawa, N. Matsuno and S. Karashima, Metal Sci., 9, 209 (1975). https://doi.org/10.1179/030634575790445251
  15. A. H. Cottrell and M. A. Jaswon, Proc. Roy. Soc., A199, 104 (1949).
  16. J. D. Eshelby, J. Appl. Phys., 25, 255 (1954). https://doi.org/10.1063/1.1721615
  17. T. Ohji, Frontiers of Next-Generation Structural Materials-Impact on Society and Industry- (ed. N. Shinya), p. 161-168, cmcbooks, Tokyo, (2008).
  18. R. Horiuchi and M. Ohtsuka, Trans. JIM, 13, 284 (1972).
  19. M. L. Baskin, V. I. Tret'yakov and I. N. Chaporova, Fiz. Metal Metalloved., 14, 159 (1967).
  20. S. G. Shin, Kor. J. Mater. Res., 23(7), 373 (2013). https://doi.org/10.3740/MRSK.2013.23.7.373
  21. S. G. Shin, Kor. J. Mater. Res., 24(1), 13 (2014). https://doi.org/10.3740/MRSK.2014.24.1.13