Abstract
Chloride attack to reinforced concrete structures located in seaside can cause a serious problem of durability and maintenance during the service life. Corrosion of reinforced steel bars in concrete decreases the bond strength and finally causes the detachment of concrete cover. Polymer cement mortar is usually adopted to repair the deteriorated RC structures because of its strong bonding property. The recovered load-carrying capacity after the repair was simulated by non-linear FEM analysis. The properties of concrete, repairing materials, bonding materials and reinforced bar were used as input data. Four types of redispersible polymer powders were used as components of polymer cement mortar. Pull-off tests were carried out to examine the bond properties such as rigidity and strength. Effects of a corrosion inhibitor and the loss of reinforced bars due to the corrosion were also considered in this study. FEM modeling and analysis were conducted to propose the universal model. Physical bonding in the relationship between repair materials and steel reinforced bar is more dominant than chemical bonding.
단면수복 보수를 실시한 RC조 부재의 내하성능 회복을 예측 평가하기 위하여 FEM해석이 빈도 높게 사용되고 있으나 부착에 대한 정보가 부족하여 정확도 있는 예측이 힘든 실정이다. 수치해석의 입력데이터가 되는 철근과 폴리머 시멘트 모르타르의 부착특성을 평가하기 위하여 폴리머 시멘트 모르타르를 이용한 일련의 인발실험을 실시하였다. 동시에 범용성있는 해석결과 활용을 위하여 부착특성을 부착강성과 부착강도로 정의하고 비선형 FEM 감도 역해석을 실시하였다. 결과를 요약하면 보수재료의 화학적 부착보다 물리적 부착이 지배적이며 폴리머 분말수지의 함유에 의해 다소 부착계면의 성능이 저하하는 것을 알 수 있었다. 부착계면의 물성은 강성과 강도로 구분하여 모델화하는 것이 합리적인 것으로 사료된다.