Abstract
The purpose of this document is to provide basic data helpful in selecting seating device material by examining the affects of polyurethane foam material on seating pressure. In order to achieve this study objective, four seats, 6cm in height, were produced in hardness of: 13, 28, 25, and $45kg/cm^2$. To measure the sitting pressure distribution (depending on the characteristics of the produced seats), 10 healthy subjects participated in the experiment. XSENSOR was used a measuring device, and each seat was mounted on a wheelchair simulation. By analyzing the obtained data with Average Pressure(AP), Peak Pressure(PP,), and Contact Area(CA), the sitting pressure was measured for five minutes on each seat. This experiment showed the following results: There were significant differences between the AP, PP, and CA in the seat material (p<0.5). While the hardness of $18kg/cm^2$ showed low pressure, the hardness of $45kg/cm^2$ showed high pressure. This study also showed that seat material made of polyurethane should be considered when selecting seats. If polyurethane foam is used in seat recommendations, it will be recommended to use $18kg/cm^2$ for the proper hardness of the seat material.
본 연구는 휠체어 좌석의 재질 중 하나로 국내에서 주로 사용되는 폴리우레탄 폼의 경도에 따른 압력 분석을 통하여 압력 분산이 적절하게 이루어지는 재질을 제시하는 것에 목적이 있다. 이러한 연구의 목적을 달성하기 위해 폴리우레탄 폼의 경도 $13kg/cm^2$, $18kg/cm^2$, $25kg/cm^2$, $45kg/cm^2$로 구성된 전방웨지 6cm 시트를 총 4개를 설계 및 제작하였다. 실험에는 비장애인 10명이 참여하였으며, 측정도구로는 XSENSOR를 사용하였고 휠체어 시뮬레이션에 시트를 올려 실험하였다. 각 시트마다 착석압력 측정은 5분간 실시하였으며 획득한 데이터 중 평균압력, 최대압력, 접촉면적 분석을 통해 경도에 따른 영향을 살펴보았다. 이에 본 실험을 통해 얻은 결과는 다음과 같다. 폴리우레탄 재질의 경도에 따라 평균압력, 최대압력 및 접촉면적은 경도 $45kg/cm^2$에서 높게 나타났고, 13, $18kg/cm^2$에서 낮게 나타났다(p< .05). 이러한 결과를 통해 폴리우레탄 재질의 경도는 착석 시 압력변화에 영향이 있음을 알 수 있었으며, 향후 자세유지기구의 시트 재질로 폴리우레탄 폼을 사용한다면 경도 $18kg/cm^2$가 체압을 분산하기에 적절한 재질로 파악되었다.