Abstract
A micro-conductive pattern was fabricated on an insulating substrate ($SiO_2$) surface using a laser direct writing method. In the LIFT process, when the laser beam irradiates a thin metal film, the photon energy is absorbed by the film and converted to thermal energy, and the thermal decomposition reaction produced by the resulting heat conduction forms a deposit on the substrate. The resistivity of the micro-electrodes deposited through LIFT process with and without polymer coating was measured. The results showed that the electric conductivity of the micro-pattern and micro-structure can be increased approximatly two times when the deposited micropattern is fabricated through a LIFT process with a polymer coating, compared to the case without a polymer coating.
레이저 직접묘화방법을 이용하여 절연기판($SiO_2$)위에 미세전도성패턴을 제조하였다. 레이저 유도증착공정은 레이저빔이 금속박막에 조사되면 레이저 빔의 빛 에너지가 금속박막에 흡수되어 열에너지로 바뀌면서 열전도에 의한 열분해반응으로 기판위에 증착이 일어난다. 본 논문에서는 금속박막위에 폴리머 코팅을 하여 레이저 직접묘화공정을 적용하여 미세패턴과 3차원 마이크로 구조물 제조에 관한 연구를 수행하였다. 평균 증착율은 전반적으로 레이저출력이 높을 수록 선형적으로 증가하고, 빔 스캔 속도가 감소할수록 증착율은 증가한다는 것을 확인하였다. Polymer 코팅층을 이용하여 미세전극을 증착하여 비저항값을 측정하여, 코팅층을 사용한 경우의 전기전도도가 코팅을 하지 않은 경우보다 약 3배정도 향상되는 것을 확인할 수 있었다.